Formaldehyde-free durable crease-proof finishing agent used for cellulosic fiber fabric

A technology of cellulose fiber and non-ironing finishing, which is applied in fiber treatment, plant fiber, textiles and papermaking, etc. It can solve the problems of cotton fabrics such as decreased air permeability, inability to be used alone, and no significant impact

Inactive Publication Date: 2010-02-03
东莞市德能化工有限公司
View PDF3 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Utilizing the solubility and film-forming properties of chitosan and the interconvertible chemical structure of chitosan and chitin, using chitosan as a raw material and acetic anhydride as a transformation curing agent, a carapace-type non-formaldehyde permanent iron can be obtained Finishing agent, the non-ironing performance of the finished cotton fabric is obviously improved, and the washability is better, the breaking strength is almost unchanged, the non-ironing effect is comparable to that of the synthetic 2D resin, and it does not have a significant impact on the whiteness of the fabric, but it cannot be used alone Use, and will reduce the breathability of cotton fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A formaldehyde-free durable non-ironing finishing agent, which consists of the following components by weight percentage:

[0034] Acetal crosslinking agent (molecular weight is 500) 30.0%;

[0035] Polypolycarboxylic acid (molecular weight is 1400) 40.0%;

[0036] Amino silicone oil emulsion 8.0%;

[0037] Magnesium Chloride 10.0%;

[0038] Deionized water 12.0%,

[0039]First add magnesium chloride to deionized water, use a stirrer to stir at a speed of 80-100r / min for 10-15 minutes, add the acetal crosslinking agent in the stated proportion and continue stirring; then add polypolycarboxylic acid and amino silicone oil emulsion, Stir for 30 minutes to obtain a light-colored transparent liquid, namely the described formaldehyde-free durable no-ironing finishing agent.

[0040] Use the obtained finishing agent to do durable non-ironing finishing on pure cotton fabrics by padding process. The concentration of the working solution is 200g / L, and the fabric liquid rete...

Embodiment 2

[0042] A formaldehyde-free durable non-ironing textile finishing agent, which consists of the following components by weight percentage:

[0043] Acetal crosslinking agent (molecular weight is 600) 25.0%;

[0044] Polypolycarboxylic acid (molecular weight is 1500) 42.0%;

[0045] Cationic silicone hydroxyl emulsion 9.0%;

[0046] Tartaric acid 3.0%;

[0047] Aluminum sulfate 8.0%;

[0048] Deionized water 13.0%,

[0049] First add tartaric acid and aluminum sulfate to deionized water, stir with a stirrer at a speed of 80-100r / min for 10-15 minutes, add the acetal crosslinking agent in the stated proportion and continue stirring; then add polypolycarboxylic acid and cationic The silicone hydroxyl emulsion was stirred for 30 minutes to obtain a light white transparent liquid, which is the long-lasting formaldehyde-free and easy-care finishing agent.

[0050] Use the obtained finishing agent to 65 / 35 polyester-cotton fabrics for durable non-ironing finishing by dipping proce...

Embodiment 3

[0052] A formaldehyde-free durable non-ironing textile finishing agent, which consists of the following components by weight percentage:

[0053] Acetal crosslinking agent (molecular weight is 700) 39.0%;

[0054] Polypolycarboxylic acid (molecular weight is 1600) 33.0%;

[0055] Epoxy polyether modified silicone oil 6.0%;

[0056] Tartaric acid 5.0%;

[0057] Aluminum sulfate 8.0%;

[0058] Deionized water 9.0%,

[0059] First add tartaric acid and aluminum sulfate to deionized water, use a stirrer to stir at a speed of 80-100r / min for 10-15 minutes, add the acetal crosslinking agent in the stated proportion and continue stirring; then add polypolycarboxylic acid and cyclic Oxygen polyether modified silicone oil was stirred for 30 minutes to obtain a light-colored transparent liquid, namely the described formaldehyde-free durable no-ironing finishing agent.

[0060] Use the obtained finishing agent to do durable non-ironing finishing on linen fabrics by padding process. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
angleaaaaaaaaaa
angleaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of textile finishing agents, in particular to a formaldehyde-free durable crease-proof finishing agent which is prepared by adopting the following raw material proportions: 20.0%-40.0% of acetal crosslinking agent, 28.0%-50.0% of polymeric carboxylic acid, 5.0%-10.0% of polysiloxane, 8.0%-15.0% of catalyst and 8.0%-16.0% of deionized water; the finishing agent is characterized in that an crease recovery angle of the cellulosic fiber fabric treated by the finishing agent can reach above 299 degrees, and maintain above 287 degrees after the cellulosicfiber fabric is washed for 5 times; the whiteness of the fabric after being finished is above 78.2%, and the tear strength retention rate is 68%-75%; and the composition is applicable to cotton fiber, bast fiber, bamboo pulp fiber (Lyocell), viscose fiber, Modal fiber and tencel fiber.

Description

Technical field: [0001] The invention relates to the technical field of textile finishing agents, in particular to a formaldehyde-free durable non-ironing finishing agent and its preparation method and application. Background technique: [0002] Cellulose fiber fabrics have the advantages of soft touch, soft luster, good warmth retention, wear resistance, strong sweat absorption, and comfortable wearing. Ironing and other shortcomings, in order to improve its performance and commercial value, usually by adding non-ironing finishing agent for finishing processing. The non-ironing finishing agents used mainly include urea-formaldehyde, melamine-formaldehyde, dimethylol dihydroxyethylene urea, dimethylol carbamate, N-methylol amide resin initial shrinkage and etherification etc. The finished fabric has high dry and wet wrinkle resistance, and the seams and stitches formed during the pressing of the garment remain unchanged after washing, achieving an effect equivalent to that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/263D06M15/39D06M15/643D06M15/647D06M15/65D06M11/82D06M13/192D06M101/06
Inventor 曾松威
Owner 东莞市德能化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com