Method for improving crude fiber and fine fiber blended strength

A fine fiber and thick fiber technology, applied in the field of spinning, can solve problems such as difficult cohesion, poor strength, and low cohesion of blended yarns

Active Publication Date: 2009-06-17
SUZHOU MOWEI NATURAL FIBER MATERIAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention solves the problems of the prior art that thick and thin fibers are difficult to cohere and entangle when they are blended, and the blended yarn obtained has low cohesion and poor strength, and invents a method for improving the strength of thick and fine fiber blended yarns

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving crude fiber and fine fiber blended strength
  • Method for improving crude fiber and fine fiber blended strength
  • Method for improving crude fiber and fine fiber blended strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Increase length at 27~33 millimeters, the flax fiber that fineness is about 1200 (Nm) carries out fiber mixing together as intermediate fiber with jute fiber and cotton fiber. The fineness metric count (Nm) of the flax fiber is 2.4~3 times of the fineness metric count (Nm) of the jute fiber, and the fineness metric count (Nm) of the cotton fiber is 2.4~3 times of the flax fiber fineness metric count (Nm). About 5 times that of fiber, according to figure 2 and image 3 As shown, at this time, because the fineness difference between flax fiber, jute fiber and cotton fiber is not large, it can be entangled with jute fiber and cotton fiber in blending. The breaking strength of jute / cotton / flax blended 12 counts (s) yarns of different blending ratios is shown in the table below:

[0028] Table 2 Breaking strength of jute / cotton / flax blended yarn with 12 counts (s)

[0029] Proportion (wt%) Breaking strength (cN) 20 / 65 / 15 580.93 25 / 50 / 25 629.05 3...

Embodiment 2

[0033] In order to enhance the breaking strength of jute and cotton fiber blended yarn, it is also possible to add polyester fibers with a length of 27 to 33 mm and a fineness of 2000 to 4500 (Nm) into the jute and cotton fibers for fiber mixing. The breaking strength of 12 yarns of blended jute / cotton / polyester fiber blended in percentage by weight is shown in the table below.

[0034] Table 3 Breaking strength of jute / cotton / polyester blended yarn with 12 counts (s)

[0035] Proportion (wt%) Breaking strength (cN) 20 / 65 / 15 592.87 25 / 50 / 25 647.56 30 / 50 / 20 618.93 30 / 40 / 30 655.79 40 / 45 / 15 587.65

[0036] 45 / 50 / 5 545.98 50 / 28 / 22 590.45 60 / 30 / 10 535.58 70 / 20 / 10 520.67 80 / 15 / 5 496.05

[0037] As can be seen from Table 3, except that the breaking strength of the yarn of a kind of jute / cotton / polyester blend ratio of 80 / 15 / 5 (wt%) does not reach 520 (cN), all the other have exceeded 520 (cN). The breaking s...

Embodiment 3

[0039] Also can add length about 31-35 millimeter in jute and cotton fiber in order to strengthen the breaking strength of jute and cotton fiber blended yarn, and the ramie fiber that fineness is about 1200 (Nm) carries out fiber mixing. The breaking strength of the 12-count yarns of the three fiber blends mixed according to different weight percentages are shown in the table below.

[0040] Table 4 Breaking strength of jute / cotton / ramie blended yarn with 12 counts (s)

[0041] Proportion (wt%) Breaking strength (cN) 20 / 65 / 15 589.76 25 / 50 / 25 638.03 30 / 50 / 20 604.58 30 / 40 / 30 623.45 40 / 45 / 15 588.56 45 / 50 / 5 534.79 50 / 28 / 22 579.08

[0042] 60 / 30 / 10 536.98 70 / 20 / 10 530.28 80 / 15 / 5 500.69

[0043] As can be seen from Table 4, except that the breaking strength of the yarn of a kind of jute / cotton / ramie blend ratio of 80 / 15 / 5 (wt%) does not reach 520 (cN), all the others have exceeded 520 (cN). The breaking str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for improving the strength of a rough fiber / fine fiber blended yarn, and at least another one type of intermediate fiber with the fineness which is between the fineness of rough fiber and fine fiber is added during the blending of the rough fiber and the fine fiber. The spinning method improves the breaking strength of the blended yarn by adding at least another one type of the intermediate fiber with the fineness which is between the fineness of the rough fiber and the fine fiber in the fiber mixture. As the intermediate fiber has small differences with the rough fiber and the fine fiber in fineness and hardness, the intermediate fiber can be well cohered during the spinning process, thereby being capable of improving the breaking strength of the blended yarn. If the intermediate fiber with one fineness is added, the intermediate fiber can be cohered with the rough fiber and can also be cohered with the fine fiber; if various types of the intermediate fibers with different finenesses are added, the various types of the intermediate fibers can also be well cohered together, so that the various types of the fiber can be cohered and wound together in blending and the breaking strength of the blended yarn can be further well enhanced.

Description

technical field [0001] The invention relates to a spinning method, in particular to a method for improving the strength of thick and thin fiber blended yarns. Background technique [0002] Blending has become one of the development trends of fabrics. There are many ways and methods of blending, such as natural fiber blending, intervening functional fiber blending, chemical fiber and natural fiber blending, etc. It is difficult to directly distinguish whether a fabric is cotton or wool. , hemp, silk or chemical fiber, the diversification of textile raw materials makes them have me in you, and you in me. Common blended yarns in the market include cotton / polyester blended yarn, cotton / linen blended yarn, cotton / ramie blended yarn, wool / viscose blended yarn, etc. The fineness is close, the difference between the fineness and metric counts of the two fibers is not more than 5 times, the difference is not large, the two fibers after twisting can be well entangled together, the tw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D02G3/22
Inventor 刘国忠张振华
Owner SUZHOU MOWEI NATURAL FIBER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com