Organic field effect transistor and special source/drain electrode and preparation method thereof

An organic field and electrode technology, which is applied in the field of patterned graphene electrodes and preparation, can solve problems such as difficult graphene patterning, and achieve the effects of improved performance, good contact, and easy large-scale preparation

Inactive Publication Date: 2009-05-27
INST OF CHEM CHINESE ACAD OF SCI
View PDF0 Cites 58 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the growth and patterning of graphene is also one of the main problems it faces now, and graphite splitting, epitaxial growth and graphite oxidation are currently effective methods to obtain graphene, ((a) Novoselov, K.S.; Geim, A.K.; Morozov, S.V.; Jiang, D.; Zhang, Y.; Dubonos, S.V.; Grigorieva, I.V.; .2006, 61, 1. (c) McAllister, M.J., Li, J.; Adamson, D.H.; Schniepp, H.C.; Abdala, A.A.; Liu, J.; Herrera-Alonso, M.; .; Prud'homme, R.K.; Aksay, I.A.Chem.Mater.2007, 19, 4396.), but these methods are difficult to achieve graphene patterning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic field effect transistor and special source/drain electrode and preparation method thereof
  • Organic field effect transistor and special source/drain electrode and preparation method thereof
  • Organic field effect transistor and special source/drain electrode and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] 1) Preparation of patterned metal thin film:

[0036] The substrate deposited with the gate electrode and the insulating layer is ultrasonically cleaned with deionized water, ethanol, and acetone, and then dried in an oven, and then at least one layer of metal film is prepared, and its patterning is realized through a mask plate or photolithography technology.

[0037] 2) Preparation of patterned graphene source-drain electrodes:

[0038] The substrate with the patterned metal film is placed in a chemical vapor deposition system, and graphene is chemically vapor deposited on the surface of the patterned metal film to obtain a patterned graphene electrode, which is used as the source and drain electrodes of the organic field effect transistor.

[0039] The third step, the deposition of organic semiconductor materials:

[0040]An organic semiconductor layer with a thickness of 10-150 nanometers is prepared on the substrate with the graphene source-drain electrodes and th...

Embodiment 1

[0046] The following example illustrates the preparation of a pentacene-based organic field-effect transistor whose electrode is a graphene-modified copper electrode, but the present invention is not limited thereto.

[0047] The first step is to sequentially deposit gate electrodes and dielectric layers on the substrate according to conventional methods;

[0048] Highly doped N-type single crystal silicon is selected as the substrate and gate electrode, and a silicon dioxide dielectric layer is grown by thermal oxidation.

[0049] The second step is to prepare patterned graphene source and drain electrodes

[0050] 1. Deposition of patterned copper film:

[0051] Such as figure 2 , the substrate deposited with the gate electrode and insulating layer was ultrasonically cleaned with deionized water, ethanol and acetone, and then dried in an oven, and then a 30-nanometer thick copper layer was prepared by plasma-enhanced vacuum thermal evaporation deposition method; The inte...

Embodiment 2

[0061] According to the preparation of Example 1, photolithography was used to prepare interdigitated thin films to realize the patterning of the silver thin film; then, a graphene thin film was grown on the silver thin film as the source and drain electrodes; the remaining steps were the same as in Example 1.

[0062] The performance test of the transistor shows that the pentacene-based crystal has a field effect mobility of 0.48cm when the channel length is 5 microns 2 V -1 the s -1 , an on-off ratio of 10 7 . As a comparison, the mobility of an organic field effect transistor with a lower electrode structure directly using silver electrodes as source and drain electrodes can reach 0.026cm 2 V -1 the s -1 , an on-off ratio of 10 4 . The results show that the organic field effect transistor with graphene as the source and drain electrodes is superior to the device with silver as the electrode in performance, that is to say: compared with silver, the graphene electrode ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an organic field effect transistor (FET), as well as a special source-drain electrode and a preparation method thereof. The organic FET with an electrode structure comprises a gate electrode, a dielectric layer, an organic semiconductor layer, a source electrode and a drain electrode, wherein the source electrode and the drain electrode are patterned Graphene electrodes. The method for preparing the patterned Graphene electrodes comprises the following steps: 1) a metal film is deposited on a substrate and is patterned; and 2) the substrate on which the patterned metal film is deposited is placed in a chemical vapor deposition system, and chemical vapor Graphene deposition is performed on the surface of a patterned metal electrode material, so as to obtain the patterned Graphene electrodes, wherein a carbon source used in chemical vapor deposition is methanol, ethanol, propanol, pentanol, benzene, toluene, xylene, methane and the like.

Description

technical field [0001] The present invention relates to an organic field effect transistor and a preparation method thereof, in particular to an organic field effect transistor with a patterned graphene electrode as the lower electrode structure of the source and drain electrodes and a preparation method thereof, and the patterned graphite Alkene electrode and its preparation method. Background technique [0002] Organic field effect transistors (OFETs) are active devices that control the current between the source and drain by adjusting the gate voltage. The entire transistor consists of a gate electrode 1, a dielectric layer 2, an organic semiconductor Layer 3, source electrode 4 and drain electrode 5, and its structure can be divided into upper electrode structure and lower electrode structure according to the position of source and drain electrodes. The schematic diagrams of the structures are as follows: figure 1 a and figure 1 As shown in b, in the upper electrode st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L51/40H01L51/05H01L51/30
Inventor 于贵狄重安魏大程刘云圻郭云龙朱道本
Owner INST OF CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com