Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Plate for building industry

A technology for industry and boards, applied in the field of boards used in the construction industry, to achieve the effects of saving raw materials, reducing wood consumption, and reducing costs

Active Publication Date: 2011-01-26
沃尔德建筑装饰集团股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the reality does not allow people to be optimistic at all. With the improvement of the industrial level, the amount of domestic garbage has also increased by leaps and bounds. With the construction of various buildings, the phenomenon of deforestation has become increasingly serious. Increasing tension, how to deal with this mountain of garbage, turn waste into treasure, and effectively reduce the use of wood is in front of people

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The plate used in the construction industry of the present invention is formed by adding raw materials twice, wherein the raw materials of the following weights are required for the first molding:

[0023] PTFE 100 kg Tribasic lead sulfate 6 kg

[0024] Dibasic lead stearate 6 kg water glass 5 kg

[0025] 6kg glutinous rice flour 6kg honey

[0026] Potassium peroxide ethyl ketone 2 kg Cobalt isooctanoate 1 kg

[0027] Divinyl benzene 1 kg emulsified silicone oil 2 kg;

[0028] Secondary molding requires the following raw materials in parts by weight:

[0029] PTFE 100 kg Tribasic lead sulfate 12 kg

[0030] Dibasic Lead Stearate 12kg Gypsum Powder 10kg

[0031] Salt 5 kg 80-20 mesh wood chips or wood shavings 300 kg

[0032] Potassium peroxide ethyl ketone 4 kg Cobalt isooctanoate 3 kg.

[0033] The construction industry plate of the present invention, the preparation method is:

[0034] (1) One-time molding: Brush the template with emulsified silicone oil, dry ...

Embodiment 2

[0037] The plate used in the construction industry of the present invention is formed by adding raw materials twice, wherein the raw materials of the following weights are required for the first molding:

[0038] PTFE 100 kg Tribasic lead sulfate 22 kg

[0039] Dibasic lead stearate 12 kg water glass 10 kg

[0040] 10kg glutinous rice flour 10kg honey

[0041] Potassium peroxide ethyl ketone 6 kg Cobalt isooctanoate 3 kg

[0042] Divinyl benzene 2 kg emulsified silicone oil 3 kg;

[0043] Secondary molding requires the following raw materials in parts by weight:

[0044] PTFE 100 kg Tribasic lead sulfate 44 kg

[0045] Dibasic lead stearate 24 kg gypsum powder 20 kg

[0046] Salt 10 kg 80-20 mesh wood chips or shavings 500 kg

[0047] Potassium peroxide ethyl ketone 10 kg Cobalt isooctanoate 6 kg.

[0048] All the other are identical with embodiment 1.

Embodiment 3

[0050] The plate used in the construction industry of the present invention is formed by adding raw materials twice, wherein the raw materials of the following weights are required for the first molding:

[0051] PTFE 100 kg Tribasic lead sulfate 14 kg

[0052] Dibasic lead stearate 9 kg water glass 7 kg

[0053] Glutinous rice flour 8kg honey 8kg

[0054] Potassium peroxide ethyl ketone 4 kg Cobalt isooctanoate 2 kg

[0055] Divinyl benzene 2 kg emulsified silicone oil 2.5 kg;

[0056] Secondary molding requires the following raw materials in parts by weight:

[0057] PTFE 100 kg Tribasic lead sulfate 28 kg

[0058] Dibasic lead stearate 18 kg gypsum powder 15 kg

[0059] Salt 8 kg 80-20 mesh wood chips or shavings 400 kg

[0060] Potassium peroxide ethyl ketone 7 kg Cobalt isooctanoate 5 kg.

[0061] All the other are identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a sheet material in the building industry, which is formed by addition of raw materials for twice, wherein the following raw materials in weight portion are required for primary forming: polytetrafluoroethylene, lead sulfate tribasic, dibasic lead stearate, water glass, glutinous rice, honey, methyl ethyl ketone peroxide, cobaltous isooctane, divinyl benzene and emulsified silicon oil; and the following raw materials in weight portion are required for secondary forming: polytetrafluoroethylene, lead sulfate tribasic, dibasic lead stearate, gypsum powder, common salt, 80 to 20 meshes of saw dust or wood shavings, methyl ethyl ketone peroxide and cobaltous isooctane. The sheet material has the advantages of environmental protection, resource conservation, full utilization of the waste materials in the woodworking, namely the saw dust and the wood shavings, solution of severe energy crisis in the building industry, high strength, high rigidity, good toughness, nodeformation, fire retardation, oil resistance, water resistance, acid resistance, corrosion resistance, conservation of raw materials, wide use range, capability of being used for indoor and outdoor decoration and high-grade package, and capability of being used for manufacturing furniture instead of wood.

Description

(1) Technical field [0001] The invention belongs to boards used in the construction industry, in particular to a board used in the construction industry. (2) Background technology [0002] With the continuous development of the national economy and the improvement of people's living standards, the awareness of environmental protection and energy saving and consumption reduction is gradually increasing in people's minds, especially the surrounding environment and greening issues are becoming more and more concerned. However, the reality does not allow people to be optimistic at all. With the improvement of the industrial level, the amount of domestic garbage has also increased by leaps and bounds. With the construction of various buildings, the phenomenon of deforestation has become increasingly serious. With increasing tension, how to deal with this mountain of garbage, turn waste into treasure, and effectively reduce the use of wood is in front of people. (3) Contents of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/18C08L3/02C08L97/02C08K13/08C08K13/02B32B27/30B32B27/18C08K3/30C08K5/098C08K3/34C08K5/14
Inventor 林擘袁显兰
Owner 沃尔德建筑装饰集团股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com