Water-soluble low oil fog anti-rust cutting liquid

A cutting fluid, water-soluble technology, applied in the petroleum industry, additives, lubricating compositions, etc., to achieve the effects of no irritating odor, excellent extreme pressure lubricity and rust resistance, and reduce production costs

Inactive Publication Date: 2008-09-17
CHANGZHOU XIALEI CHEM
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to disclose a water-soluble low-oil mist anti-rust cutting fluid and its preparation method for heavy-duty cutting of ferrous and non-ferrous metals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0009] A preparation method of water-soluble low oil mist antirust cutting fluid, comprising the following preparation steps:

[0010] I. Preparation of low oil mist anti-rust cutting oil: Add DB-10 transformer oil to the electric heating glass-lined reactor, heat to 80°C while stirring, b. add 10.0% of the mass of the base oil to the reactor in turn borated glyceride, 7.5% sulfurized fat, 15.0% soybean oil and 0.8% butyl octyl zinc dithiophosphate; stop heating and continue to stir the mixed solution until it is uniform to obtain low oil mist antirust cutting oil;

[0011] II. Add low oil mist anti-rust cutting oil as base oil in the reaction kettle, stir and heat up to 60°C-80°C, then add emulsifier with a mass of 5%-15% of the mass of the base oil, 3%- 10% water-soluble phosphate ester and 0.5%-2% copper / aluminum corrosion inhibitor, stop heating the reactor and continue to stir the mixed solution until it is uniform and transparent.

[0012] The object of the present inve...

Embodiment 1

[0015] First prepare low oil mist anti-rust cutting oil: In a 1000L electric heating glass-lined reactor, add 600kg of DB-10 transformer oil, heat to 80°C while stirring, add 60kg of borated glyceride, 45kg of vulcanized fat, and 90kg of soybean oil in sequence and 5 kg of butyl octyl zinc dithiophosphate, after the addition, stop heating and continue to stir for 1 hour to obtain 800 kg of light yellow transparent oil, which is low oil mist antirust cutting oil.

[0016] Then, in a 1000L electric heating glass-lined reactor, add 600kg of low oil mist anti-rust cutting oil, heat to 70°C while stirring, add 70kg of triethanolamine oleic acid soap, 26kg of phosphoric acid ester and N,N-(dibenzo Triazole methylene) laurylamine 10kg, after feeding, stop heating, continue to stir 1 hour, sampling inspection.

Embodiment 2

[0018] Prepare low oil mist antirust cutting oil, same as Example 1.

[0019] Then, in a 1000L electric heating glass-lined reaction kettle, add 600kg of low oil mist anti-rust cutting oil, heat to 60°C while stirring, add 60kg of castor oil polyoxyethylene condensate, 60kg of phosphate ester and N-acetyl benzo Triazole 12kg, after feeding, stop heating and continue to stir for 1 hour, sampling inspection.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-soluble low oil mist antirust cutting liquid used for the ferrous and nonferrous metal heavy-duty cutting operation, and the preparation method thereof. The preparation method comprises the following steps: firstly, the low oil mist antirust cutting liquid is prepared; secondly, the low oil mist antirust cutting liquid is added in a reaction vessel as the base oil, and is mixed, heated and warmed up to 60 to 80 DEG C; and then 5 to 15 percent of emulsifying agent, 3 to 10 percent of water solubility phosphate ester and 0.5 to 2 percent of copper / aluminum corrosion inhibitor by the base oil wight are added in sequence; after the completion of feeding, the heating to the reaction vessel is stopped, and the mixed liquor is agitated continuously untill in the uniform and transparent state. The prepared cutting liquid is used after being diluted by adding water, is particularly suitable for metal drilling, threading, gear processing and other heavy-duty cutting operations, and has good extreme pressure lubricating property and anti-rust property. The production cost of the cutting liquid is low, the oil mist is extremely low when in use, and no penetrating odor exists.

Description

technical field [0001] The invention relates to a water-soluble low-oil-mist anti-rust cutting fluid for heavy-duty cutting of black and non-ferrous metals and a preparation method thereof. Background technique [0002] Cutting fluid is essential in metal cutting. At present, ordinary cutting fluids are used for light-load cutting and grinding, but in the processing of difficult-to-cut materials (such as titanium alloys, stainless steel, etc.) and difficult machining processes (such as drilling, tapping), ordinary cutting fluids cannot achieve The ideal requirement is replaced by heavy-duty caustic water-soluble cutting fluid or cutting oil, but the biggest disadvantage of cutting oil is that it is extremely expensive to use and the production environment is poor. At present, the general heavy-duty water-soluble cutting fluids are deficient in terms of rust resistance, oil mist, and odor during use. Contents of the invention [0003] The technical problem to be solved by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M177/00C10M137/10C10M125/04C10N30/12C10N40/22
Inventor 陆峰
Owner CHANGZHOU XIALEI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com