Thermoplastic powder electrically-conducting paint/printing ink and manufacture method thereof

A conductive coating and thermoplastic technology, applied in conductive coatings, inks, wax coatings, etc., can solve the problems that are difficult to meet the requirements, and achieve the effects of high-speed automatic production, low resistance, and excellent electrical conductivity

Active Publication Date: 2008-08-20
SHANGHAI TRANSCOM ELECTRONICS TECH
View PDF0 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If it is required to form a narrow and thick (such as 100μm film thickness) coating, such as a silver grid electrode on a solar surface, it is difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1: prepare TPU-silver thermoplastic powder conductive coating / ink

[0040] Raw material name ratio

[0041] (1) Silver powder 70%

[0042] (2) TPU 20%

[0043] (3) Rosin 6%

[0044] (4) SiO 2 2%

[0045] (5) Paraffin 0.5%

[0046] (6) Zinc stearate 1%

[0047] (7) Di-tert-butyl p-cresol 0.4%

[0048] (8) Phosphorus 0.1%

[0049] Total 100%

[0050] (9) Ethyl acetate (preparation co-solvent) 50%

[0051] Pour (2)(3)(4)(5)(6)(7)(8) into (9) respectively, stir evenly, then add (1) while stirring and stir vigorously with a high-shear disperser until it is evenly dispersed, then put it in an oven at 50°C for drying, then use a pulverizer to pulverize the dried block mixture, put the pulverized material into a grinder and grind it until it is powdery, which is the finished product.

Embodiment 2

[0052] Embodiment 2: prepare EVA-silver thermoplastic powder conductive coating / ink

[0053] Raw material name ratio

[0054] (1) Silver powder 75%

[0055] (2) EVA 15%

[0056](3) Rosin 5%

[0057] (4) SiO 2 2.5%

[0058] (5) Paraffin 1.3%

[0059] (6) Calcium stearate 0.8%

[0060] (7) Di-tert-butyl p-cresol 0.3%

[0061] (8) Boron 0.1%

[0062] Total 100%

[0063] (9) ethyl acetate (preparation co-solvent) 40%

[0064] Pour (2)(3)(4)(5)(6)(7)(8) into (9) respectively, stir evenly and disperse evenly, then add (1) while stirring, use high shear The disperser stirs vigorously until it is uniformly dispersed, then puts it in an oven at 50°C for drying, and then pulverizes the dried block mixture with a pulverizer, and puts the pulverized material into a grinder for grinding until it becomes powdery, which is the finished product.

Embodiment 3

[0065] Embodiment 3: prepare TPU-silver-aluminum thermoplastic powder conductive coating / ink

[0066] Raw material name ratio

[0067] (1) Aluminum powder 30%

[0068] (2) Silver powder 40%

[0069] (3) TPU 25%

[0070] (4) Rosin 2%

[0071] (5) SiO 2 1%

[0072] (6) Paraffin 0.7%

[0073] (7) Zinc stearate 1.0%

[0074] (8) Di-tert-butyl p-cresol 0.25%

[0075] (9) Gallium 0.05%

[0076] Total 100%

[0077] (10) ethyl acetate (preparation co-solvent) 60%

[0078] Pour (2)(3)(4)(5)(6)(7)(8)(9) into (10) respectively, stir evenly and disperse evenly, then add (1) while stirring, use Stir vigorously with a high-shear disperser until it is evenly dispersed, then place it in an oven at 50°C for drying, and then use a pulverizer to pulverize the dried block mixture, and put the pulverized material into a grinder for grinding until it is powdery. finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a chemical industry electronic material, in particular to a thermoplastic powder conductive coating / ink applied in solar field and electronic communication field. The chemical industry electronic material comprises the following components according to weight percentage: (1) conductive powder: 60 to 80 percent; (2) adhesive: 5 to 30 percent; (3) film-forming strengthening agent: 0.3 to 10 percent; (4) lubricant: 0.1 to 3 percent; (5) solidification regulator: 0.1 to 3 percent; (6) adhesion promoter: 0.5 to 10 percent; (7) antioxidant: 0.1 to 3 percent; (8) doping elements:0 to 5 percent.

Description

Technical field: [0001] The invention relates to a chemical electronic material, especially a powdered conductive material (paint / ink) used in the field of solar energy and electronic communication. Background technique: [0002] In the field of solar energy and electronic communication, a conductor is generally required to transmit current and signals. This conductor is attached to other substrates in the form of a coating, and can be sintered at a certain temperature as required. Forms an adhering and well-conducting electrical conductor. It should have excellent electrical conductivity, surface smoothness, good adhesion, environmental resistance, good operability, and environmental protection. [0003] Existing similar products, such as conductive coatings or electronic pastes, exist in liquid form. The cured forms of these products are all thermosetting and contain more volatile organic compounds (VOC), which is not good for the ecological environment. . When used, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/24C09D11/02C09D7/12C09D175/04C09D123/08C09D193/04C09D191/06H01B1/20C09D11/52
Inventor 杨建平
Owner SHANGHAI TRANSCOM ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com