Modified polyphenyl composite insulation board and production technique thereof

A composite thermal insulation and production process technology, applied in the direction of thermal insulation, synthetic resin layered products, hydraulic material layered products, etc., can solve problems such as difficult to withstand the test of time, unsatisfactory thermal conductivity, and durability concerns. Achieve the effect of reducing construction technology, fast construction speed and high production efficiency

Inactive Publication Date: 2008-06-18
朱玉华
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally speaking, most of the above materials have the above disadvantages: large capacity, unsatisfactory thermal conductivity, low strength, and thick plates
In addition, if wood chips and plant fibers are used as reinforced skeleton materials, it is difficult to withstand the test of time, and it is worrying in terms of durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The specific production process is as follows:

[0021] Step 1: Lay the first layer of material, spread the stirred polymer mortar according to the pre-adjusted paving thickness;

[0022] Step 2: Scrape the first layer of material layer, and use a vibrating scraper to scrape the first layer of polymer mortar to ensure the required thickness of the material layer;

[0023] The third step: spread the second layer of glass fiber mesh cloth, and the selected glass fiber mesh cloth is laid on the first layer of material by mechanical assistance as required;

[0024] The fourth step: spread the third layer of modified polystyrene board, and spread the modified polystyrene board on the glass fiber mesh according to step 2.3;

[0025] Step 5: Spread the fourth layer of polymer paste emulsion of the present invention on the modified polystyrene board layer;

[0026] Step 6: Lay the fifth layer of calcium silicate board on the polymer paste emulsion after completing the fifth s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of energy-saving, environment-friendly building materials, in particular to a modified polyphenyl composite thermal insulation board and a production technique thereof. The present invention also relates to the fabrication method of the thermal insulation board material, the thermal insulation board material includes six layers: the first layer is polymer mortar, the second layer is fiber glass mesh cloth, the third layer is a modified polyphenyl board, the fourth layer is polymer adhesive emulsion, the fifth layer is a calcium silicate board and the sixth layer is coating, and with a novel production technique, the six layers are compounded together to form the thermal insulation board material. Because the modified polyphenyl board is added with 5 percent to 10 percent of rare earth material, diatomite, and an aluminium plate is embedded in the middle, the properties of the product, such as ageing resistance, crack resistance, etc., are increased, and meanwhile, the service life of the product is prolonged by over one time.

Description

Technical field: [0001] The invention relates to the technical field of energy-saving and environment-friendly building materials, in particular to a modified polystyrene composite thermal insulation board and its production process. Background technique: [0002] At present, my country's construction industry is developing very fast, but all kinds of wall materials and roof insulation boards are very backward. With the increase of high-rise buildings, most of them use frame structures to pour cement wall panels as a whole, which has poor thermal insulation and requires additional insulation layers. Therefore, my country's wall reform is imperative, in view of this, several wall insulation panels came into being. About, foam cement board, gypsum foam board, foam polystyrene board or colloidal materials such as cement, gypsum, magnesite powder, plus fly ash, wood chips or plant fibers. Generally speaking, most of the above materials have the above disadvantages: large capacit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/76B32B37/02B32B37/15B32B37/12B32B27/04B32B27/06B32B17/02B32B13/02E04C2/284C04B28/00C04B18/08C04B14/04C04B14/06C04B18/24
CPCY02B30/94Y02A30/00Y02A30/244Y02B30/90
Inventor 朱玉华
Owner 朱玉华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products