Water-soluble crylic acid resin and preparation method thereof

A technology of water-soluble acrylic acid and acrylic acid, which is applied in the field of acrylic resin for ink and its preparation, can solve problems such as poor slipperiness, wear resistance and anti-adhesion, low hardness of coating, difficult to meet, and achieve the goal of reducing air pollution Effect

Active Publication Date: 2008-05-14
浙江英科水墨材料有限公司
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It retains the performance of solvent-based resins and is more environmentally friendly than solvent-based resins. However, because it contains a large amount of strong hydrophilic carboxyl groups, the coating hardness is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A water-soluble acrylic resin is provided, comprising the following:

[0025] Acrylic: 1-2 parts

[0026] Methyl methacrylate: 15-29 parts

[0027] Butyl acrylate: 18-22 parts

[0028] Styrene: 3-7 parts

[0029] Hydroxyethyl methacrylate: 3-7 parts

[0030] Mercaptoethanol: 0.25-0.65 parts

[0031] Azobisisobutyronitrile: 0.3-0.7 parts

[0032] Isopropanol: 3-5 parts

[0033] Ethanol: 15-20 parts

[0034] Monoethanolamine: 2.5-8.75 parts

[0035] Water: 25-31.5 parts

[0036] The above are parts by mass.

Embodiment 2

[0038] Acrylic: 1-2 parts

[0039] Methyl methacrylate: 25-29 parts

[0040] Butyl acrylate: 19-21 parts

[0041] Styrene: 5-6 parts

[0042] Hydroxyethyl methacrylate: 4-6 parts

[0043] Mercaptoethanol: 0.25-0.65 parts

[0044] Azobisisobutyronitrile: 0.3-0.7 parts

[0045] Isopropanol: 3-5 parts

[0046] Ethanol: 18-20 parts

[0047] Monoethanolamine: 2.5-8.75 parts

[0048] Water: 25-31.5 parts

[0049] The above are parts by mass.

Embodiment 3

[0051] Acrylic: 1-2 parts

[0052] Methyl methacrylate: 26-28 parts

[0053] Butyl acrylate: 21 parts

[0054] Styrene: 7 parts

[0055] Hydroxyethyl methacrylate: 7 parts

[0056] Mercaptoethanol: 0.25-0.65 parts

[0057] Azobisisobutyronitrile: 0.3-0.7 parts

[0058] Isopropanol: 3-5 parts

[0059] Ethanol: 20 parts

[0060] Monoethanolamine: 2.5-8.75 parts

[0061] Water: 25-31.5 parts

[0062] The above are parts by mass.

[0063] Provide a kind of preparation method for preparing above-mentioned water-soluble acrylic resin, comprise the following steps:

[0064] a. Mix acrylic acid, methyl methacrylate, butyl acrylate, styrene, hydroxyethyl methacrylate, mercaptoethanol, and azobisisobutyronitrile in the head tank, and stir evenly;

[0065] b. Put isopropanol and ethanol into a reaction kettle with a reflux condenser, raise the temperature to 80°C, add the mixed monomer obtained in step a dropwise, keep the temperature at 75-80°C for 10 hours after dropping, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a waterborne acrylic resin and the preparation method, which aims to provide a waterborne acrylic resin and the preparation method which can not only keep the performance of organic solvent type acrylic resins, but also have friendly environmental protection property. The invention comprises the following matters of mass portion: 1 to 2 of acrylic, 15 to 29 of methyl methacrylate, 18 to 22 of butyl acrylate, 3 to 7 of styrene, 3 to 7 of 2-hydroxyethyl methacrylate, 0.25 to 0.65 of mercaptoethanol, 0.3 to 0.7 of azobisisobutyronitrile, 3 to 5 of isopropanol, 15 to 20 of ethanol, 2.5 to 8.75 of monoethanolamine and 25 to 31.5 of water.

Description

technical field [0001] The invention relates to an acrylic resin for ink and a preparation method thereof, in particular to a water-soluble acrylic resin and a preparation method thereof. Background technique [0002] In the prior art, the resin used for the pearlescent linking material is oily nitro resin, but it contains a large amount of organic solvents, which will pollute the environment, cause great harm to the human body, and is not safe, so the development is environmentally friendly The water-soluble acrylic resin is an urgent task to solve the above problems. [0003] Chinese patent CN20051022901 discloses an acrylic resin for coatings with good environmental protection and its preparation method, which is characterized in that 40-80% wt of acrylic acid monomer and 20-60% wt of organic solvent, 0.1-10% wt of initiator free radical solution polymerization After removing the organic solvent, the water-soluble acrylic resin with a solid content of 20-60%wt is obtaine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/18C08F4/04
Inventor 丁伟梁永升
Owner 浙江英科水墨材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka