Highly wearable vacuum coating ultraviolet curing coatings

A technology for vacuum coating and curing coatings, applied in the field of coatings, can solve the problems of restricting UV-curing vacuum coating coatings, poor wear resistance and fouling resistance, and poor anti-yellowing properties of the coating film, and achieves excellent ring test performance, Excellent resistance to high temperature and humidity, improving surface effect

Active Publication Date: 2009-12-09
HUNAN SOKAN NEW MATERIAL
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Wherein the Chinese patent CN1281011A applies for "ultraviolet light curing vacuum coating bottom and topcoat", the topcoat adopts polyester acrylate and phenolic epoxy acrylate as the main resin, which solves the adhesion problem of the ultraviolet light curing vacuum coating topcoat, but due to Low hardness, poor wear resistance and stain resistance, Chinese patent CN1803942A application "UV curable coating for metal coating surface protection" uses epoxy acrylic resin and polyurethane resin with 2 functional groups as the main resin, with thermoplastic acrylic resin and fiber The composite resin composed of plain resin improves the hardness of the coating by increasing the rigid structure in the coating system. However, due to the poor wear resistance of epoxy acrylic resin and the poor anti-yellowing performance of the coating film, it is far from meeting the requirements of today's electronic products for coatings. Higher requirements, especially the need for high wear resistance
Thus limiting the application of UV-curable vacuum coating coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Changxing 6071 10.0wt%

[0039] Nippon Synthetic 7605B 20.0wt%

[0040] DPHA 15.0wt%

[0041] Isobornyl Acrylate 4.0wt%

[0042] CD 9051 8.0wt%

[0043] 1-Hydroxy-cyclohexyl phenyl ketone 4.0wt%

[0044] NANOBYK-3601 2.0wt%

[0045] BYK 333 0.1wt%

[0046] BYK 066 0.1wt%

[0047] Ethyl acetate 21.8wt%

[0048] Butanone 10.0wt%

[0049] Ethylene glycol ether acetate 5.0wt%

Embodiment 2

[0051] Changxing 6075 20.0wt%

[0052] Cytec 5704 10.0wt%

[0053] Nippon Synthetic 7640B 10.0wt%

[0054] DPHA 10.0wt%

[0055] Cytec EB 168 1.0wt%

[0056] 1-Hydroxy-cyclohexyl phenyl ketone 4.0wt%

[0057] NANOBYK-3610 4.0wt%

[0058] BYK 307 0.5wt%

[0059] BYK 066 0.2wt%

[0060] BYK 164 0.3wt%

[0061] Ethyl acetate 15.0wt%

[0062] Butanone 20.0wt%

[0063] Propylene Glycol Ether 5.0wt%

Embodiment 3

[0065] Changxing 6071 20.0wt%

[0066] Cytec EB1290 25.0wt%

[0067] Pentaerythritol tetraacrylate 10.0wt%

[0068] CD 9051 2.0wt%

[0069] 2-Hydroxy-2-methyl-1-phenylacetone 3.0wt%

[0070] NANOBYK-3610 5.0wt%

[0071] TEGO 432 0.2wt%

[0072] TEGO 920 0.2wt%

[0073] Ethyl acetate 14.6wt%

[0074] Butyl acetate 15.0wt%

[0075] Methyl isobutyl ketone 5.0wt%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of electronic application coatings, in particular to high wear-resistant vacuum coating ultraviolet light curing coatings. The composition and content of the high wear-resistant vacuum coating UV-curable coating are: 10-30wt% of difunctional urethane acrylate, 10-40wt% of high-functional urethane acrylate, 5-20wt% of high-functional acrylate monomer, single Functional acrylate monomer 0-15wt%, acid adhesion promotion 1-10wt%, photoinitiator 1-6wt%, nano wear-resistant material 0-5wt%, additive 0.1-2wt%, solvent 10-50wt%. The invention is aimed at protecting the surface of vacuum coating workpieces of electronic products such as mobile phones, MP3s, and digital cameras, and has the characteristics of good surface effect, super wear resistance, high temperature and high humidity resistance, cold and heat cycle resistance, and excellent yellowing resistance, among which RCA has the highest wear resistance It can reach more than 1500 times, effectively improving the service life of electronic products. The invention effectively solves the adhesive force and wear resistance of the UV-cured vacuum coating paint, solves the matching problem of the primer and top paint of the UV-cured vacuum coating paint, and has wide versatility.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to an ultraviolet curing coating used after the surface of a workpiece is metallized by vacuum coating. Background technique [0002] After more than 40 years of development, radiation curing technology has been widely used in various fields and industries all over the world. Ultraviolet curable coatings (UV coatings for short) have the advantages of low VOC content, fast curing speed, and good comprehensive properties of the coating film, and have developed rapidly in China. The plastic substrate is treated by vacuum coating, which can make the workpiece get a high degree of metallic luster and mirror effect. UV-curable vacuum coating coatings are generally applied by spraying, with fast curing speed, simple operation and convenient construction, and have been widely used. Generally used in computer peripheral equipment, communication equipment, audio-visual equipment, consumer electronic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/00C09D175/14
Inventor 凌云剑龙凤飞伍松
Owner HUNAN SOKAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products