Plasma and enzyme combined anti-felting method for tidying wool knitted fabric

A technology of wool knitted fabric and plasma, which is applied in the direction of biochemical fiber treatment, fiber treatment, animal fiber, etc., can solve the problem of excessive damage to wool fiber, and achieve the effect of improving the anti-felting process

Inactive Publication Date: 2009-11-04
DONGHUA UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a wool knitted fabric anti-felting finishing method combined with plasma and biological enzymes to solve the problem of excessive damage to wool fibers in the protease finishing, and to control fiber damage through plasma pretreatment and TG enzyme Repair process to reduce the damage of protease to the interior of wool fibers; develop machine-washable wool knitted fabrics with anti-felting and low-strength damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1 plasma treatment wool knitted fabric

[0023] Process flow: wool scouring→plasma treatment

[0024] in:

[0025] 1) Wool washing: The wool knitted fabric is treated at a constant temperature of 40°C for 30 minutes in 0.5 g / L wool washing liquid at a bath ratio of 1:30. Drain lightly, dry and set aside.

[0026] 2) Plasma treatment:

[0027] Treat at 30Pa, 100W for 3min. Gas: air.

[0028] The wool knitted fabric treated by the above process has an anti-felting rate of 10.47% (untreated 17.20%), and a bursting strength of 0.276Mpa, which is 6.15% stronger than the bursting strength of 0.260Mpa after scouring.

Embodiment 2

[0029] Embodiment 2: Plasma combined with protease to treat wool knitted fabric

[0030] Process flow: wool scouring→plasma treatment→protease treatment→water washing→drying

[0031] 1) Wool washing: The wool knitted fabric is treated at a constant temperature of 40°C for 30 minutes in 0.5 g / L wool washing liquid at a bath ratio of 1:30. Drain lightly, dry and set aside.

[0032] 2) Plasma treatment:

[0033] Treat at 30Pa, 100W for 3min. Gas: Air.

[0034] 3) Protease treatment:

[0035] The mass concentration of protease is 4% (o.w.f) (weight to wool), the temperature is 50° C., the time is 40 minutes, the bath ratio is 1:20, and the pH is 8.5.

[0036] 4) Washing:

[0037] Treat at 90°C for 10 minutes, and inactivate the enzyme at high temperature. Wash twice in cold water, gently absorb the water, dry at 80°C, and set aside.

[0038] The wool knitted fabric treated by the above process has an anti-felting rate of 1.79% (untreated 17.20%) and a bursting strength of ...

Embodiment 3

[0039] Example 3 Plasma combined with protease and transglutaminase (TGase) to treat wool knitted fabrics

[0040] Process flow: wool scouring→plasma treatment→protease treatment→water washing→transglutaminase treatment→water washing→drying

[0041] in:

[0042] 1) Wool washing: The wool knitted fabric is treated at a constant temperature of 40°C for 30 minutes in 0.5 g / L wool washing liquid at a bath ratio of 1:30. Drain lightly, dry and set aside.

[0043] 2) Plasma treatment:

[0044] Treat at 30Pa, 100W for 3min. Gas: air.

[0045] 3) Protease treatment:

[0046] The mass concentration of protease is 4% (o.w.f) (weight to wool), the temperature is 50° C., the time is 40 minutes, the bath ratio is 1:20, and the pH=8.5.

[0047] 4) Washing:

[0048] Treat at 90°C for 10 minutes, and inactivate the enzyme at high temperature. Wash twice in cold water, gently absorb the water, dry at 80°C, and set aside.

[0049] 5) Transglutaminase treatment:

[0050] The mass conce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for anti-felting finishing of wool knitted fabrics combined with plasma and biological enzymes. The steps include: wool scouring→plasma treatment→protease treatment→water washing→transglutaminase treatment→water washing→drying. The anti-felting method for wool of the present invention enables wool knitted fabrics to reach the machine-washable standard (felting shrinkage rate is less than 2%) under the condition of ensuring strength (strength damage is less than 10%), and the finishing process has little damage to fibers, which is safe and environmentally friendly. It is an energy-saving and clean wool finishing process.

Description

technical field [0001] The invention belongs to the field of anti-felting of wool, in particular to an anti-felting finishing method of wool knitted fabrics combined with plasma and biological enzymes. Background technique [0002] When wool products are processed and washed, the oriented scales will be rubbed to cause displacement between fibers, resulting in shrinkage, resulting in shrinkage of the product size, unclear lines, etc., which seriously affect the appearance, feel, easy care and wearing performance. At present, the domestic wool anti-felting process generally adopts a relatively mature chlorination method and a two-step method of chlorinating a resin (IWS / CSIRO Chlorine Hercosett method). These two methods are based on chlorination treatment, which are easy to absorb chlorine and turn yellow, and cause great damage to the fiber strength. Not only the wool fiber is severely eroded by chemicals, but also there are a large amount of absorbable organic halogenated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M16/00D06M10/02D06M101/10
Inventor 张瑞萍蔡再生
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com