Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Thermo-setting acrylic-acid emulsion, its preparing method and paint containing same

An acrylic emulsion and thermosetting technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problem of interlayer adhesion, uncontrollable coating thickness, and salt spray resistance that can only reach 9.5 or even Lower problems

Active Publication Date: 2008-01-23
GUANGZHOU HUMAN CHEM
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, the commercially available organic primers are mainly based on acrylic and epoxy resins, and the main problems are as follows: (1) The corrosion resistance of the coating is not ideal, and the general single-layer coating should reach 1.5um or more , and the salt spray resistance can only reach 9.5 or even lower levels; (2) The coating stability is not good, and some products are prone to deposits during the coating process, which affects the coating quality; The service life is only tens of hours. If it is not used up, the remaining part can no longer be used, which is a huge waste; some coatings change in physical and chemical properties during use, especially the viscosity increases with the extension of the coating process , causing the thickness of the coating film to be uncontrollable and the performance of the coating to decline
Because the primer contains more defoamers and leveling agents, it directly affects the coating stability of the primer coating, and also has a greater impact on the interlayer adhesion between the primer and the top coat; and the patent The stability of the primer, the post-processing of the primer, and the adhesion between the primer and the topcoat have not been tested and evaluated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] Recipe (1):

[0075] Sodium vinyl sulfonate (25% aqueous solution) 8.0g

[0076] Sodium lauryl sulfate (5% aqueous solution) 4.0g

[0077] 150g deionized water

[0078] Recipe (2):

[0079] Methyl methacrylate 35.5g

[0080] Isooctyl acrylate 15.0g

[0081] Butyl acrylate 18.4g

[0082] Acrylic acid 1.5g

[0083] Hydroxyethyl Acrylate 25g

[0084] A-174 (GE company silane department) 1.0g

[0085] Vinyl tertiary carbonate (EXXON company) 1.5g

[0086] Trimethylolpropane diallyl ether 0.1

[0087] Formula (3):

[0088] Potassium persulfate (5% aqueous solution) 16g

[0089] The preparation steps of thermosetting acrylic emulsion are as follows:

[0090] (1) Under the condition of nitrogen protection, in a 1-liter reaction bottle equipped with a stirrer, a thermometer, and a condenser, add the substances in the formula (1) in sequence, stir and mix evenly, and heat to 40°C to make a mixture A;

[0091] (2) Add all the monomers in the formula (2) to the beake...

Embodiment 2

[0096] Recipe (1):

[0097] AMPS (Lubrizol company) 25% ammonia solution*4.0g

[0098] Sodium lauryl sulfate (5% aqueous solution) 16.0g

[0099] 150g deionized water

[0100] Recipe (2):

[0101] Methyl methacrylate 42.95g

[0102] Isooctyl acrylate 20.0g

[0103] Butyl acrylate 14.0g

[0104] Methacrylic acid 4.0g

[0105] Hydroxyethyl methacrylate 15g

[0106] Witco A-172 (GE Company Silane Division) 1.5g

[0107] Glycidyl methacrylate 1.5g

[0108] Trimethylolpropane trimethacrylate 0.05

[0109] Formula (3):

[0110] Potassium persulfate (5% aqueous solution) 30g

[0111] (*Preparation of AMPS 25% ammonia solution: make AMPS solid into 30% aqueous solution with deionized water, then use ammonia water to adjust pH to 5-6, then use deionized water to adjust the effective content, calculated as 25% of AMPS.)

[0112] The preparation steps of thermosetting acrylic emulsion are as follows:

[0113] (1) Under the condition of nitrogen protection, in a 1-liter react...

Embodiment 3

[0119] Recipe (1):

[0120] AMPS (NH3) (Lubrizol company) (25% aqueous solution) 16.0g

[0121] Sodium lauryl sulfate (5% aqueous solution) 2.0g

[0122] 150g deionized water

[0123] Recipe (2):

[0124] Methyl methacrylate 40.3g

[0125] Isooctyl acrylate 16.0g

[0126] Butyl acrylate 21.0g

[0127] Acrylic acid 8.0g

[0128] Hydroxyethyl Acrylate 10g

[0129] A-151 (Silane Department of GE Company) 0.5g

[0130] Trimethylolpropane triacrylate 0.2g

[0131] Formula (3):

[0132] Potassium persulfate (5% aqueous solution) 60g

[0133] The preparation steps of thermosetting acrylic emulsion are as follows:

[0134] (1) Under the condition of nitrogen protection, in a 1-liter reaction bottle equipped with a stirrer, a thermometer, and a condenser, add the substances in the formula (1) in sequence, stir and mix evenly, and heat to 70°C to make a mixture A;

[0135] (2) Add all the monomers in the formula (2) to the beaker one by one, stir and mix evenly to make mixt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

This invention discloses a thermoset crylic acid latex and its preparation method and a corrosion resistant bottom coat containing such latex and used in the Al fins of the heat converter of air conditioners, in which, said latex includes a crylic acid kind monomers, an ionic vinyl monomers, an ethene monomers, a vinyl silane coupler, a crosslink monomers, a surface active agent and an initiator to be got by seed latex and semi-continuous drop technology. Said bottom coat includes said thermoset crylic acid latex, water-base coating resin, water-base cross-linker, booster solvent, neutralization agent, a water-base adhesive force accelerant, a catalyst and water.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a thermosetting acrylic emulsion and a preparation method thereof, and a corrosion-resistant primer containing the emulsion and used for aluminum fins of air-conditioning heat exchangers. Background technique [0002] With global warming, the market demand for various types of air conditioners is increasing; and the situation of energy shortage has prompted the development of air conditioners in the direction of lightweight, miniaturization, and high energy efficiency. One of the effective measures to realize the lightweight, miniaturization and high energy efficiency ratio of the air conditioner is to reduce the thickness of the aluminum fins of the air conditioner heat exchanger, reduce the distance between the aluminum fins, and increase the heat transfer area per unit weight of the heat exchanger . At present, the thickness of aluminum foil used for aluminum fins has been reduced to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L33/14C09D133/14C09D5/08
Inventor 唐靖黄光燕陈兴耀陈勇李晨隽唐泉
Owner GUANGZHOU HUMAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com