Double layer sandwich foamed concrete composite solid wall plate

A foamed concrete, solid technology, applied in the field of building materials, can solve the problems of long production time, large damage, insufficient strength, etc., and achieve the effects of good thermal insulation effect, simple production process and high production efficiency

Inactive Publication Date: 2007-06-27
贵州华骏集团节能环保材料有限公司
View PDF0 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, hollow blocks need to be sintered, which consumes a lot of energy, pollutes the environment, and takes a long time to make; gypsum hollow slats have poor waterproof performance and low fire resistance; polystyrene foam sandwich panels are heavy and low in fire resistance, and polystyrene will be released when burning. Poisonous ethylene gas; GRC hollow slats have low surface strength and great damage during transportation; magnesium chloride cement plant fiber hollow slats are mainly made of magnesium oxide and magnesium chloride, which have high early strength but insufficient later strength, poor water resistance and large deformation. When the climate is humid, there will be a phenomenon of re-halogenation, which will affect the quality and appearance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) First mix 30 kg of quick-hardening sulfoaluminate cement, 40 kg of fly ash, 30 kg of river sand and 60 kg of water, stir to make a slurry, put it into the mold, and add a layer of glass fiber grid Cloth, made of 5-10mm cement sheet.

[0022] (2) After the initial setting of the cement sheet, mix 30 kg of quick-hardening sulfoaluminate cement, 40 kg of fly ash, 30 kg of river sand, 0.2 kg of PAV fiber and 60 kg of water, stir evenly, and then add peroxide 1 kg of hydrogen, 1 kg of diphenylthiourea, 2 kg of metal soap, 1.5 kg of sodium methyl silicate, stir well, pour on the first layer of cement sheet after 1-2 minutes;

[0023] (3) The cement slurry to be poured is foamed for 25-30 minutes, and then a layer of glass fiber mesh cloth is spread on the foamed concrete surface, and then the slurry prepared in step 1 is poured onto the glass fiber mesh cloth After smoothing and polishing, the second layer of cement sheet is made, with a thickness of about 5-10mm. It is ...

Embodiment 2

[0025] (1) First mix 35 kg of quick-hardening sulfoaluminate cement, 35 kg of fly ash, 30 kg of river sand and 60 kg of water, stir to make a slurry, put it into the mold, and add a layer of glass fiber mesh Cloth, made of 5-10mm cement sheet.

[0026] (2) After the initial setting of the cement sheet, mix 335 kg of fast-hardening sulfoaluminate cement, 35 kg of fly ash, 30 kg of river sand, 0.2 kg of PAV fiber and 60 kg of water, stir evenly, and then add peroxide 1 kg of hydrogen, 1 kg of diphenylthiourea, 2 kg of paraffin, 1 kg of sodium methyl silicate, stir well, and pour it on the first layer of cement sheet after 1-2 minutes.

[0027] (3) The cement slurry to be poured is foamed for 25-30 minutes, and then a layer of glass fiber mesh cloth is spread on the foamed concrete surface, and then the slurry prepared in step 1 is poured onto the glass fiber mesh cloth After smoothing and polishing, the second layer of cement sheet is made, with a thickness of about 5-10mm. It ...

Embodiment 3

[0029] (1) First mix 40 kg of quick-hardening sulfoaluminate cement, 30 kg of fly ash, 30 kg of river sand and 60 kg of water, stir to make a slurry, put it into the mold, and add a layer of glass fiber mesh Cloth, made of 5-10mm cement sheet.

[0030] (2) After the initial setting of the cement sheet, mix 40 kg of fast-hardening sulfoaluminate cement, 30 kg of fly ash, 30 kg of river sand, 0.2 kg of PAV fiber and 60 kg of water, stir well, and then add peroxide 1 kg of hydrogen, 1 kg of polyvinyl alcohol, 1 kg of gelatin, 1 kg of sodium ethyl silicate, stir well, and pour it on the first layer of cement sheet after 1-2 minutes;

[0031] (3) The cement slurry to be poured is foamed for 25-30 minutes, and then a layer of glass fiber mesh cloth is spread on the foamed concrete surface, and then the slurry prepared in step 1 is poured onto the glass fiber mesh cloth After smoothing and polishing, the second layer of cement sheet is made, with a thickness of about 5-10mm. It is n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A dual-layer sandwich-type solid wall slab is composed of two surficial thin cement slabs and a foam concrete core layer. It is proportionally made of fast hardening sulphoaluminate cement, powdered coal ash, river sand, fibers, hydrogen peroxide as foaming agent, and stabilizer. Its advantages are light weight, high surface strength and high insulating effect.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a concrete product. Background technique [0002] With the development of urban buildings and the continuous improvement of building functions, people have put forward new requirements for wall materials such as light weight, environmental protection, energy saving, thermal insulation, sound insulation, and fire prevention. The traditional wall materials made of clay as the main raw material and produced by the sintering process have been gradually eliminated, replaced by a wide variety of lightweight and environmentally friendly wall materials, such as hollow blocks, gypsum hollow slats, and polystyrene foam sandwich panels. , GRC hollow slats, fly ash hollow slats, magnesium chloride cement plant fiber hollow slats, autoclaved aerated concrete slabs, etc. Although the above-mentioned light wall materials have their own strengths, they all have some shortc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04C2/04B28B1/14C04B28/06C04B18/08C04B14/06C04B14/42C04B22/06C04B38/00B32B5/18
CPCC04B41/009C04B41/5076C04B28/06Y02W30/91C04B14/068C04B18/08C04B20/0048C04B22/068C04B24/20C04B38/10C04B24/2623
Inventor 徐君元
Owner 贵州华骏集团节能环保材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com