Thermal-insulation smelting composite furnace for non-ferrous metal

A thermal insulation composite, non-ferrous metal technology, used in furnaces, furnace types, lighting and heating equipment, etc., to achieve the effect of long service life, convenient and effective use, and cost reduction

Active Publication Date: 2007-05-23
JINTIAN COPPER GROUP CORP NINGBO
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a non-ferrous metal smelting and heat preservation composite furnace in view of the above-mentioned technical status, so that the non-ferrous metal melt does not come into contact with the air during the transfer process, and can effectively avoid the loss of easily evaporated and oxidized metals , which solves the adverse effects on the quality caused by the suction of the metal melt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal-insulation smelting composite furnace for non-ferrous metal
  • Thermal-insulation smelting composite furnace for non-ferrous metal

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments.

[0014] As shown in Figures 1 and 2, the nonferrous metal smelting and heat preservation compound furnace of this embodiment includes a smelting furnace 1 and a heat preservation furnace 3, and a continuous casting crystallizer 4 is provided at the exit 32 of the heat preservation furnace 3. A channel 31 is provided between the smelting furnace 1 and the holding furnace 3, and the channel 31 is a conduit 31a made of a material with good high temperature resistance. A control valve 2 is provided at the channel 31, and the valve 2 is an adjustable valve with adjustable flow rate. It includes a valve body 24 and a valve stem 22. The valve body 24 is placed horizontally on the bottom of the melting furnace 1. The upper side of the middle part of the body 24 is provided with an insertion cavity 25 into which the valve stem 22 can extend. Out of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

It relates to a non-ferrous metal smelting and heat preserving composite furnace comprises smelting and heat preserving furnaces and through ways between them, control valve at the through way, featuring in one end of the said through way connecting with the bottom of the smelting furnace, the other end connecting with the heat preserving furnace bottom, and the outlet of the heat preserving furnace at the bottom of the heat preserving furnace. Compared with existing techniques, it can effectively avoid the consumption of evaporable and oxidizable metals, reducing material cost, improving production environment, and prevents unsatisfactory effect on the quality due to the drawing of air of the smelting metal. It does not interfere with the heat preserving furnace casting, keeping consistent alloy composition control with that of the detachable furnace, realizing feeding through furnaces, with the highest working temperature rising up to 1500 DEG C, with extensive application.

Description

technical field [0001] The invention relates to the technical field of non-ferrous metal casting furnaces, in particular to a smelting and heat preservation composite furnace applied to the regeneration of yellow miscellaneous copper. Background technique [0002] At present, the traditional process of using scrap copper to produce brass rods is to melt the raw materials in the melting furnace first, and then pour the molten copper into the holding furnace for continuous casting after the composition of the copper liquid is qualified. Volatilizes to form white zinc oxide mist, which not only causes metal loss, but also pollutes the production environment. From the analysis of the mechanism of zinc mist generation, it can be known that a layer of zinc oxide film will be formed on the surface of the copper liquid when it is left standing, which hinders the further evaporation of zinc, but the copper liquid is disturbed when the furnace is poured, which destroys the zinc oxide ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F27B19/04F27B3/04
Inventor 王永如方友良张学士洪燮平李红卫张建华丁国安楼春章邵高科朱云福
Owner JINTIAN COPPER GROUP CORP NINGBO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com