High performance metallic composite material and its preparation method and application

A technology of metal composite materials and metal sheets, which is applied in the field of high-performance metal composite materials and its manufacturing, to achieve the effects of strong acid and alkali corrosion resistance, good heat transfer, and small temperature difference

Inactive Publication Date: 2006-09-13
SHANGHAI XINGYUYING COMPOSITION METAL MATERIAL
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The use of these metal composite plates as cooking utensil materials such as pots has great advantages, but there are still improvements and improvements in their bonding strength and service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1, the material selection and preparation process are as follows:

[0039] 1. Aluminum plate AL1050, AG3003, shearing;

[0040] 2. Surface polishing treatment;

[0041] 3. Three-layer clad rolling;

[0042] 4. Annealing: temperature 380℃, time 7 hours;

[0043] 5. Cleaning;

[0044] 6. Steel plates 304SS and 430, shearing;

[0045] 7. Surface polishing treatment;

[0046] 8. Cleaning;

[0047] 9. The three-layer clad plate and the two-layer steel plate are heated and rolled together, the temperature is 220℃, the pressure is 2500KW, and the speed is 4m / min;

[0048] 10. Annealing: temperature is 380℃, time is 3 hours.

[0049] The required five-layer metal composite board is obtained.

[0050] Physical properties: (1) Tensile strength 300MPa; Elongation rate 47%; Yield strength 210MPa.

Embodiment 2

[0051] Example 2: Material selection and preparation process are as follows:

[0052] 1. Aluminum plate: AL1050, AL3003, shearing;

[0053] 2. Surface polishing treatment;

[0054] 3. Three-layer clad rolling;

[0055] 4. Annealing: temperature 390℃, time 6 hours;

[0056] 5. Cleaning;

[0057] 6. Steel plate: sns304, sns304, shearing;

[0058] 7. Surface polishing treatment;

[0059] 8. Cleaning;

[0060] 9. The three-layer clad plate and the two-layer steel plate are heated and rolled together, the temperature is 260℃, the pressure is 2500KW, and the speed is 4.5m / min;

[0061] 10. Annealing: temperature 450℃, time 1 hour.

[0062] Get the required five-layer metal composite board

[0063] Physical properties: (1) tensile strength 305MPa, (2) elongation rate 48%, (3) yield strength 215MPa.

Embodiment 3

[0064] Example 3: The material selection and preparation process are as follows:

[0065] 1. Aluminum plate AL1050, AL3003, cut;

[0066] 2. Surface grinding treatment;

[0067] 3. Three-layer clad rolling;

[0068] 4. Annealing: temperature 400℃, time 5 hours;

[0069] 5. Cleaning;

[0070] 6. Steel plate sus304, sus304, shearing;

[0071] 7. Surface polishing treatment;

[0072] 8. Cleaning;

[0073] 9 The three-layer clad plate and the two-layer steel plate are heated, rolled and compounded, at a temperature of 420°C, a pressure of 2700KW, and a speed of 3.5 m / min;

[0074] 10 Annealing: temperature 260℃, time 1 hour.

[0075] Get the required five-layer metal composite board

[0076] Mechanical and physical properties: (1) tensile strength of 315MPa, (2) elongation of 49%, (3) yield strength of 220MPa.

[0077] The metal composite materials in each of the above examples can be used to make cooking utensils such as woks, cooking pots, and electromagnetic cookers, and have...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A high-performance composite metallic material used for manufacturing cooking pan or cooker is composed of the 1st stainless steel layer, the 2nd aluminum layer, the 3rd Al-alloy layer, the 4th aluminum layer and the 5th stainless steel (or iron) layer. Its preparing process includes such steps as laminating three aluminum layers, rolling, heat treating, attaching two stainless steel layers, hot rolling and heat treating.

Description

Technical field [0001] The invention belongs to the technical field of metal products, and specifically relates to a high-performance metal composite material and a manufacturing method and application thereof. Background technique [0002] Now domestically produced cookware products (such as woks, etc.) usually use a single material. Because a single material is limited by its inherent physical and chemical characteristics, the pot body material's strong hardness, wear resistance, corrosion resistance, heat transfer, electromagnetic induction performance and surface treatment process are greatly limited. , So that the overall performance of the internal and external performance of the cookware made of a single material is not satisfactory. Many improvement measures have also been proposed. For example, in order to make up for the lack of thermal conductivity of stainless steel materials, a piece of aluminum or copper plate with better thermal conductivity is re-welded on the bot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/01B21B1/38B21B37/00A47J27/00
Inventor 唐根兴金林德
Owner SHANGHAI XINGYUYING COMPOSITION METAL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com