Special nonwoven fabric and its production process
A production process and technology of non-woven fabrics, applied in the direction of non-woven fabrics, textiles and papermaking, etc., can solve problems such as environmental hazards, environmental pollution, and use range restrictions, and achieve the effect of saving wood resources
Inactive Publication Date: 2006-07-19
周永斌
View PDF0 Cites 22 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] Most of the existing non-woven fabrics are made of single polyester staple fiber through acupuncture or spunlace. Due to the characteristics of polyester staple fiber, the elongation rate of the product is relatively large, so the scope of use of the product is limited to a certain extent.
For products with certain requirements on hardness, elasticity, tensile strength, wear resistance, etc., such as Simmons mattresses, it is difficult to adapt to ordinary non-woven fabrics made of single polyester staple fiber through acupuncture or spunlace. Most of the existing Simmons mattresses use wood boards. Due to the limited wood resources and the use of formaldehyde in the processing of wood boards, excessive formaldehyde content will cause great harm to the human body and the environment; another example is the backup of automotive interior parts. In the past, phenolic resin was added to the non-woven fabric for the base material of the box and the central carpet. Because the material contains a large amount of formaldehyde, it leads to a large amount of free formaldehyde in the car. The formaldehyde content in the air in the car exceeds the standard, which not only pollutes the environment, and endanger human health
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
example 1
[0014] Example 1: Mix 75kg6D×51mm polyester staple fiber and 25kg 4D×51mm LMF4080 low-melting point fiber evenly, after opening, cotton feeding, carding, web laying, pre-punching, lower main spine, upper main spine, two-roll hot rolling Rolling and scalding treatment, the temperature of the upper and lower rolls of the two-high hot rolling mill is 150°C, the line speed of the hot rolling mill is 6m / min, and finally it is packaged in rolls.
example 2
[0015] Example 2: Mix 60kg 6D×51mm polyester staple fiber and 40kg4D×51mm LMF4080 low melting point fiber evenly, after opening, cotton feeding, carding, web laying, pre-punching, lower main thorns, upper main thorns, coiling, and then The semi-finished product is shaped by a tenter-type heat-setting oven, the setting temperature is 210°C, the line speed is 5m / min, and finally sliced and packaged.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| length | aaaaa | aaaaa |
Login to view more
Abstract
The related manufacture technique for a special non-woven fabric with polyester staple fiber and LMF4080 fiber low-melting fiber as main constituent comprises: mixing, opening, feeding cotton, carding, placing net, pre- embroidering, primary embroidering, thermal treating with a cluster hot-rolling mill with surface temperature as 120-195Deg, forming or tenter-type hot-air forming at 130-230Deg or the combination of cylinder-type hot-air forming at 120-195Deg and rolling with a cluster hot-rolling mill, and packing. This product contains no any harmful chemical material (such as formaldehyde) fit to spread.
Description
technical field [0001] The invention relates to a special non-woven fabric and a production process thereof, belonging to the technical field of non-woven fabrics. Background technique [0002] Most of the existing non-woven fabrics are made of single polyester staple fiber through acupuncture or spunlace. Due to the characteristics of polyester staple fiber, the elongation rate of the product is relatively large, so the range of use of the product is limited to a certain extent. For products with certain requirements on hardness, elasticity, tensile strength, wear resistance, etc., such as Simmons mattresses, it is difficult to adapt to ordinary non-woven fabrics made of single polyester staple fiber through acupuncture or spunlace. Most of the existing Simmons mattresses use wood boards. Due to the limited wood resources and the use of formaldehyde in the processing of wood boards, excessive formaldehyde content will cause great harm to the human body and the environment; ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/46D04H1/435D04H1/4382
Inventor 周永斌
Owner 周永斌
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap