Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Preparation method of composite filtering net of stainless steel net and metal fiber felt

A technology of metal fiber felt and stainless steel mesh, applied in chemical instruments and methods, lamination devices, lamination and other directions, can solve the problems of easy wrinkling, low pressure resistance, shortened service life of fiber felt, etc., and achieve strong bonding force. , high filtration performance, high strength effect

Active Publication Date: 2006-06-14
WESTERN METAL MATERIAL
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that there is no joint point between the net and the felt, the pressure resistance is low, and it is easy to wrinkle.
The net does not protect the sintered felt very well, thus reducing the service life of the fiber felt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] First wash and dry the 40-mesh stainless steel square hole mesh, cut it according to the required size of the filter mesh to be made, and then arrange the pre-laid stainless steel fiber felt according to the filtration accuracy level, and then place the mesh flat on the fiber felt, Double-sided re-netting: one upper and lower net, and the middle re-netting, add fiber mat to the top and bottom of the net, press the above-mentioned felt net in a two-roll rolling mill, the thickness of the felt net after pressing is: 2.5mm~3mm. Put the pressed felt net into a vacuum furnace and carry out vacuum pressure sintering. The method of pressure is: evenly lay a perforated molybdenum plate with a specification of 250×420×5mm on the uppermost layer of the material. The hole diameter of the molybdenum plate is 5mm, hole spacing is 15mm.

[0015] When sintering the multi-net felt in a vacuum furnace, the required vacuum degree is: 1.0×10 -2 pa, the sintering temperature is between 12...

Embodiment 2

[0017] First wash and dry the 40-mesh stainless steel square hole mesh, cut it according to the required size, and then arrange the pre-laid stainless steel fiber felt according to the filtration accuracy level, and then place the mesh on top of the fiber felt (special structure felt mesh) Composite body: one piece of felt at the top and bottom, adding mesh in the middle, that is, adding fiber felt on the top and bottom of the mesh), put the above felt mesh on a two-roll rolling mill to press, and the thickness of the felt mesh after pressing is: 2.5mm~3mm . Put the pressed felt net into the vacuum furnace, and charge 200 sheets per furnace (specification: 1200×1800mm). , The isolation material is a 40-mesh non-metal mesh with surface treatment. Vacuum pressure sintering is carried out in the following way: On the uppermost layer of the material, a perforated molybdenum plate with a specification of 250×420×5mm is evenly laid, the hole diameter of the molybdenum plate is 5mm,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

A composite filter net is prepared from the stainless steel mesh with square holes and the stainless steel fiber felt through overlaying, two-roller rolling, and vacuum sintering. Its advantages are high filter power, high strength and high adhesion.

Description

technical field [0001] The invention discloses a method for preparing a composite filter screen of stainless steel mesh and metal fiber felt, and relates to a method for preparing a composite material of stainless steel metal mesh and stainless steel fiber felt used for filtering in processes such as chemical industry, metallurgy, and environmental protection. Background technique [0002] As a new type of filter material, stainless steel fiber felt has the advantages of high temperature resistance, corrosion resistance, high filtration accuracy, high dirt holding capacity, and high filtration efficiency, but it also has the disadvantage of not being able to withstand pressure (≤10Mpa). Although the metal square hole mesh is used as the filter material, although the pressure resistance is high, the mesh is easily deformed, and the filtration accuracy is not easy to control. The traditional method of using the combination of the two is to sinter the fiber mat and then cover t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F7/04B32B37/00
Inventor 巨建辉杨延安苏明辉白文峰左彩霞石丹郝龙陈清勤高小军
Owner WESTERN METAL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com