Method for producing red brass pipe
A red brass, manufacturing method technology, applied in the direction of pipes, rigid pipes, pipes/pipe joints/pipe fittings, etc., can solve the problems of small aspect ratio, small size, unsuitability, etc., and achieve uniform and good material properties The effect of uniform support and performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
specific Embodiment approach 2
[0040] Make a red brass tube of φ21.33×2.72mm and O61 state.
[0041] Ingot Casting: The ingot is cast using a melting furnace.
[0042] Heating: use a heating furnace to heat, the heating temperature is 800° C., and the heating time is 1.5 hours.
[0043] Extrusion: Use a hydraulic press for extrusion and preheat the supporting extrusion barrel, perforation needle, extrusion pad and extrusion die. The preheating temperature of the extrusion barrel is 350°C and the preheating time is 3 hours; the preheating temperature of the perforating needle, extrusion pad and extrusion die is 300°C and the preheating time is 3 hours, the extrusion die is φ80mm, and the perforating needle It is φ60mm; the extrusion temperature is 800°C, the extrusion speed is 20mm / min, the extrusion ratio is 21, and it is extruded into a tube blank of φ80×60mm.
[0044] Sawing: Use a circular saw to cut off the head and tail.
[0045] Pickling: pickling the pipe in the pickling tank, the concentration of s...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com