Resin of zinc acrylate or copper acrylate containing indole function group, its preparation and use

An acrylic resin, indole functional technology, applied in the application field of preparing marine antifouling coatings, can solve problems such as environmental pollution, toxicity, impact on human health, etc., and achieve good antifouling performance.

Inactive Publication Date: 2005-12-21
OCEAN UNIV OF CHINA
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It was not until 1987 that people realized that this organotin compound was highly toxic, would pollute the environment, and even affect human health through the food chain

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin of zinc acrylate or copper acrylate containing indole function group, its preparation and use
  • Resin of zinc acrylate or copper acrylate containing indole function group, its preparation and use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] 1. Preparation of 1-acryloyl indole monomer

[0011] Put 50mL of freshly steamed tetrahydrofuran, 3.5g of 1-hydroindole, and 3.9g of sodium cyanide into a three-neck flask successively, and react at room temperature for 30 minutes to obtain indole sodium salt. Dissolve 3.3 g of acryloyl chloride in 10 mL of tetrahydrofuran, drop it into the indole sodium salt prepared above, control the reaction temperature at 0° C., and react for 2.5 hours to obtain 1-acryloyl indole monomer.

[0012] Replace the above-mentioned 1-hydroindole with haloindole, 1-hydrohydrophylline or halocarpine, and follow the above-mentioned preparation method to obtain 1-acryloyl haloindole, 1-acryloyl Alkaline or 1-acryloylhalocarpine monomer.

[0013] 2. Preparation of acrylic resin containing indole functional groups and carboxyl groups

[0014] Add toluene and n-butanol in a three-necked flask equipped with a stirring device, a condenser, and a thermometer. Their weight ratio is 262g of a mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This is a kind of acrylic zinc or cuprum resin containing indole functional group and its preparation method. Its characteristics are: firstly prepare monomer containing indole functional group, then synthesize acrylic resin containing functional group and carboxyl, finally make the acrylic resin and zinc hydroxide or cuprum hydroxide react to obtain acrylic zinc or cuprum resin containing indole functional group; the reaction temperature of the said synthesizing monomer containing indole functional group is -10 - 10 Deg. C, the reaction time is 1.5 - 5 hours. The resin of the invention can be used for preparing sea antifouling dope. In the seawater, the organic zinc or cuprum acrylic ester on the polymer linear main chain of the coat surface hydrolyzes, and send out organic zinc or cuprum; the hydrolyzed polymer main chain contains indole functional group with highly efficient antifouling activeness, which makes the hydrolyzed polymer main chain still has sterilization activeness. So the dope can effectively prevent halobios from clinging on the surface of fishing tools, ships and seacoast establishments, and has good antifouling performance.

Description

technical field [0001] The invention relates to a zinc or copper acrylate resin, in particular to a zinc or copper acrylate resin containing an indole functional group, a preparation method thereof and an application in preparation of marine antifouling paint. technical background: [0002] There are thousands of fouling organisms in the ocean, and more than half of these fouling organisms float on the coast and harbors. They attach and grow on the bottom of ships, buoys, water pipelines, cooling pipelines, rafts and nets. The attachment of these fouling organisms will cause the surface fouling of these facilities, increase the surface friction resistance, and also accelerate the corrosion rate. The most common solution to marine biofouling is to apply paints containing antifouling agents. At present, a large number of antifouling coatings used at home and abroad contain organotin and cuprous oxide, such as the copolymer of tributyltin methacrylate and methyl methacrylate a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F20/04
Inventor 于良民张志明李昌诚姜晓辉徐焕志董磊
Owner OCEAN UNIV OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com