Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Liquefied dicyandiamide and its preparing process

A technology of dicyandiamide and chemical formula, which is applied in the field of liquefied dicyandiamide and its preparation, can solve the problems of complex process and poor miscibility of epoxy resin, and achieve the effect of good compatibility and long-term storage stability

Inactive Publication Date: 2004-03-31
北京科化新材料科技有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Soluble in water and ethanol, but poor miscibility with epoxy resin, so dicyandiamide, as an effective curing agent for epoxy resin, must be crushed into very fine powder and suspended in epoxy resin, and because it is very easy to Absorb moisture in the air, so the process is more complicated in the preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquefied dicyandiamide and its preparing process
  • Liquefied dicyandiamide and its preparing process
  • Liquefied dicyandiamide and its preparing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In a 250ml there-necked flask equipped with an electric stirrer, a spherical condenser and a thermometer, add 34 grams of dicyandiamide, 0.34 grams of 2-ethyl-4-methylimidazole, 60 grams of ethylene glycol monomethyl ether and 91 gram of glycidyl neodecanoate, start the stirrer, start to heat up, keep the temperature at 140°C to 150°C, react for 12 hours, vacuumize and remove the solvent for about 10 minutes. A milky white viscous liquid was obtained. See Tables 1 and 2 for properties.

Embodiment 2

[0034] In a 50ml there-necked flask equipped with an electric stirrer, a spherical condenser and a thermometer, add 34 grams of dicyandiamide, 0.34 grams of 2-ethyl-4-methylimidazole, 80 grams of ethylene glycol monomethyl ether and 137 gram of glycidyl neodecanoate, start the stirrer, start to heat up, keep the temperature at 140°C to 150°C, react for 12 hours, vacuumize and remove the solvent for about 10 minutes. A viscous, pale milky white product was obtained. See Tables 1 and 2 for properties.

Embodiment 3

[0036] In a 250ml there-necked flask equipped with an electric stirrer, a spherical condenser and a thermometer, add 34 grams of dicyandiamide, 0.34 grams of 2-ethyl-4-methylimidazole, 100 grams of ethylene glycol monomethyl ether and 182 grams of glycidyl neodecanoate, start the stirrer, start to heat up, keep the temperature at 140°C to 150°C, react for 14 hours, vacuumize and remove the solvent for about 10 minutes. A viscous, light orange-red product was obtained. See Tables 1 and 2 for properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Liquefacient dicyandiamide and its preparation method. The method comprises: adding 100 parts of dicyandiamide, 300-600 parts of dehydrated neodecanoic acid glyceride, 50-200 parts of solvent, 0.5-1 par of 2-ethyl-4-methylimidazol or 2-methylimidazol into a reactor; mixing and heating, reacting for 12-14hours at 140degree Cí½150degree C ; vacuumizing and removing the solvent, obtaining viscous liquid. When the liquefacient dicyandiamide is used with ethoxyline resin, the weight ratio of liquefacient dicyandiamide to ethoxyline resin is 30-50í†100. Liquefacient dicyandiamide of the invention could be dissolved in ethoxyline resin, has an ability of solidifying ethoxyline resin with high mechanical strength.

Description

technical field [0001] The invention belongs to the field of coatings, composite materials or adhesives, and in particular relates to liquefied dicyandiamide and a preparation method thereof. Background technique [0002] Dicyandiamide is also known as cyanoguanidine. First, due to the effect of conjugated double bonds and cyano groups in the molecule, the alkalinity is greatly reduced, so its mixture with epoxy resin is very stable at room temperature and can be used as a latent curing agent; second, it is compatible with epoxy resin The cured product has excellent mechanical properties; third, it is non-toxic and non-irritating. Therefore, as a curing agent for epoxy resins, dicyandiamide is widely used in the fields of coatings, composite materials, and adhesives. [0003] Dicyandiamide is a white crystalline powder with a melting point of 207-209°C. Soluble in water and ethanol, but poor miscibility with epoxy resin, so dicyandiamide, as an effec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/50
Inventor 聂绪宗杨川王丽娟李世媛
Owner 北京科化新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com