Radiation dispersion polymerization process of phenylethylene micro ball

A technology of styrene microspheres and dispersion polymerization, which is applied in the field of polymer material preparation, can solve the problems of easy pollution and complex process, and achieve the effect of strong operability, simple process and low pollution

Inactive Publication Date: 2007-03-14
TSINGHUA UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The general preparation methods of polymer microspheres mainly include emulsion polymerization, suspension polymerization, dispersion polymerization, seed swelling polymerization, etc., which are affected by temperature and time, and the process is complicated and easy to be polluted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Radiation dispersion polymerization process of phenylethylene micro ball

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Styrene monomer 14wt%, ethanol and water 84wt% (the mass ratio of alcohol to water is 5:1), polyvinylpyrrolidone 2wt%, disperse by ultrasonic for 15min, and then pass nitrogen gas to remove oxygen for 15min. Then it is irradiated with gamma rays with a dose of 100KGy to obtain microspheres with a size of about 1 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses radiating dispersion and polymerization process of styrene micro ball in the field of polymer material preparing technology. In styrene monomer, stabilizer PVP is added to disperse medium ethanol and water, gamma-ray irradiation initiates dispersed polymerization and separation, and styrene micro ball powder is obtained of 1-2 micron size after stoving. The present invention has simple process, no initiator pollution, no temperature limitation in preparing micron level polymer micro ball, and may be used widely in catalyst carrier, medicine, biochemical and electronic information material fields.

Description

technical field [0001] The invention belongs to the technical scope of polymer material preparation, in particular to a radiation dispersion polymerization method of styrene microspheres. technical background [0002] Polymer microspheres have special properties such as good sphericity, small size, large specific surface area, strong adsorption, enrichment of functional groups on the surface, and strong surface reaction ability. As a functional material, the application of polymer microspheres has not only penetrated into all aspects of daily life, but also has entered high-tech fields such as medical and pharmaceutical fields, biochemical fields, and electronic information materials in the past ten years. The study of molecular microspheres has become a new research field of polymer science. Therefore, the preparation and application technology of polymer microspheres has attracted more and more attention. [0003] The general preparation methods of polymer microspheres m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F112/08C08F2/38C08F2/46
Inventor 梁彤祥王娟阎迎辉
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com