Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Weatherability self-cleaning external wall coating material and its preparation method

An exterior wall coating, self-cleaning technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc. Effects of chemical and thermal stability, low cohesive energy density, and large specific surface area

Inactive Publication Date: 2006-03-15
GUANGZHOU SUPER CHEM COATING CO LTDGUANGZHOU SUPER CHEM COATING CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing acrylic coatings have the defects of easy back-sticking at high temperature and brittle cracking at low temperature, so it is difficult to meet the requirements
At present, this kind of building veneer brick or curtain wall glass decoration, veneer brick or curtain wall glass, due to the high-altitude fall and injury hazards caused by the aging of the adhesive, and urban light pollution and other hazards, are expressly prohibited by the relevant departments from being used in certain areas.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment one: formula is: (total amount is 100 kilograms meter) 22 kilograms of tap water, polyacrylate ammonium wetting and dispersing agent GA-40 0.6 kilograms, rutile type titanium dioxide (CR-828) 16 kilograms, anatase type nanometer TiO 28 kg of powder, 5 kg of kaolin (3000 mesh), 3 kg of sericite (1250 mesh), 0.4 kg of silicone oil defoamer CF-2460.4 kg of BLACKBURN company, 0.3 kg of hydroxyethyl cellulose thickener NATROSOL PLUS330, silicic acid 0.1 kg of aluminum-magnesium thickener ATTAGEL50, 0.4 kg of hydrophobic modified polyurethane thickener RM2020, 0.2 kg of PH regulator 2-amino-2-methyl-1-propanol, and the fungicide is an isothiazole derivative produced by Bayer +Hydroxymethylurea+1, 0.2 kg of bactericide mixed with 6 dihydroxyl-2-5 dioxane, antifungal agent is 2-n-octyl-4-isothiazoline-3 of Progiven company -Ketobenzimidazole, 0.3 kg, 2 kg of antifreeze agent propylene glycol, 1.5 kg of caking agent 2,2,4-trimethyl-1,3-pentanediol methyl ethyl butyrat...

Embodiment 2

[0034] A new commercial building, because it is a large-scale and high-rise building, uses this product for exterior wall coating. The formula is (total weight based on 100 kg): 23 kg of tap water, 0.5 kg of ammonium polyacrylate wetting and dispersing agent H-100, 20 kg of rutile titanium dioxide (CR-828), anatase nano-TiO 2 5 kg of powder, 5 kg of kaolin (3000 mesh), 3 kg of sericite, 2 kg of wollastonite powder (900 mesh), 0.4 kg of silicone oil mixture defoamer CF-246 from BLACKBURN company, thickened with hydroxyethyl cellulose Agent CellosizeER-150000.25 kg, thickener aluminum magnesium silicate Attgel500.1 kg, hydrophobic modified polyurethane thickener RM2020 0.45 kg PH regulator 2-amino-2-methyl-1-propanol 0.2 kg, fungicide is 0.2 kg of fungicide made by mixing isothiazole derivatives+hydroxymethylurea+1,6 dihydroxy-2-5 dioxane by Progiven company or bayer company, antifungal agent is 2- produced by Progiven company n-octyl-4-isothiazolin-3-one benzimidazole fungicid...

Embodiment 3

[0036] The 10th to 22nd floors of a high-rise office building have adopted the product of the present invention for exterior wall coating. The formula is (100 kg in total) 25 kg of tap water, 0.5 kg of ammonium polyacrylate wetting and dispersing agent H100, rutile titanium dioxide (CR -828) 16 kg, anatase nano TiO 2 8 kg of powder, 5 kg of kaolin (3000 mesh), 3 kg of sericite (1250 mesh), 0.5 kg of silicone oil defoamer CF-2460.5 kg of BLACKBURN company, 0.3 kg of hydroxyethyl cellulose thickener NATROSOL PLUS 330, silicon Acid aluminum magnesium thickener ATTAGEL50 0.1 kg, hydrophobic modified polyurethane thickener RM2020 0.4 kg, PH regulator 2-amino-2-methyl-1-propanol 0.2 kg, bactericide is derived from isothiazole produced by Bayer 0.2 kilograms of fungicides made from compound + hydroxymethylurea + 1,6 dihydroxy-2-5 dioxane, and the fungicide is 2-n-octyl-4-isothiazoline- 3-ketobenzimidazole antifungal agent, 0.3 kg, antifreeze agent propylene glycol 2 kg, caking agent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to an ultraweatherability self-cleaning paint for outer wall, and its composition contains pigment filling material, moistening dispersing agent, defoaming agent, thickening agent A, B and C, polymer emulsion, anti-mildew bactericide, film-forming adjuvant and water, etc. Said emulsion paint has the water-proofing property, good dirt resistance and anti-ageing property. In particular, the anatase titanium dioxide powder body is added, it make said paint has self-cleaning function. The invention also provides preparation method.

Description

Technical field: [0001] The invention relates to a super-weather-resistant self-cleaning exterior wall coating and a preparation method thereof, in particular to a method for decomposing pollutants attached to the surface of the coating and anatase nano-TiO by photocatalytic reaction. 2 The micronization characteristics of the powder, the anatase nano-TiO 2 The powder is added into the coating to prepare a novel water-based silicone acrylic ultra-weather-resistant self-cleaning latex coating suitable for the exterior walls of large-scale and high-rise buildings. The invention belongs to the field of architectural coatings. Background technique: [0002] After years of hard work, the production technology of acrylic latex coatings has matured and has been widely used in low and medium buildings, and the trial period can basically meet the requirements of 5 to 10 years. With the development of the economy, the buildings in many large and medium-sized cities are developing tow...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D143/04C09D5/16
Inventor 石玉英丁春台周子鹄李赉周
Owner GUANGZHOU SUPER CHEM COATING CO LTDGUANGZHOU SUPER CHEM COATING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com