Aluminum material chemical polishing solution and polishing method thereof

A technology for chemical polishing and polishing liquid, applied in the field of polishing liquid, can solve the problem of pollution that cannot be recycled and used, and achieve the effects of remarkable polishing effect, low emission, and easy recycling operation.

Active Publication Date: 2022-05-31
SICHUAN UNIV
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the above problems, the purpose of the present invention is to propose a kind of aluminum material chemical polishing liquid and polishing method thereof, solve the problem that the existing aluminum material chemical polishing liquid cannot be recycled and used big pollution problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum material chemical polishing solution and polishing method thereof
  • Aluminum material chemical polishing solution and polishing method thereof
  • Aluminum material chemical polishing solution and polishing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides a chemical polishing liquid for aluminum materials, which is prepared by mass percentage of the following raw materials: 20% of quaternary phosphonium hydrogen sulfate ionic liquid, 1% of citric acid, 3% of polyethylene glycol and the balance of water.

[0028] see figure 1 , this embodiment also provides a polishing method for aluminum chemical polishing liquid, comprising the following steps:

[0029] Step 1: First, prepare the chemical polishing liquid for aluminum materials by ionic liquid, additives and water according to the actual required ratio, and introduce it into the polishing tank and heat it to 60 °C for use;

[0030] Step 2: First clean the surface of the aluminum to be polished, then put the cleaned aluminum directly into the aluminum chemical polishing solution in the polishing tank to soak for 2 minutes, then take out the aluminum and put it into the washing tank to wash with water Clean and finish chemical polishing of alumi...

Embodiment 2

[0035] This embodiment provides a chemical polishing liquid for aluminum materials, which is prepared from the following raw materials by mass percentage: 5% tributyloctylcarboxylate quaternary phosphonium dihydrogen phosphate ionic liquid, 1% phosphotungstic acid, 2% % polyethylene glycol, 0.5% coco acid diethanolamide, balance water.

[0036] see figure 1 , this embodiment also provides a polishing method for aluminum chemical polishing liquid, comprising the following steps:

[0037]Step 1: First, prepare the chemical polishing liquid for aluminum materials by ionic liquid, additives and water according to the actual required ratio, and introduce it into the polishing tank and heat it to 35 °C for use;

[0038] Step 2: First clean the surface of the aluminum to be polished, then put the cleaned aluminum directly into the aluminum chemical polishing solution in the polishing tank to soak for 6 minutes, then take out the aluminum and put it into the washing tank to wash with...

Embodiment 3

[0043] This embodiment provides a chemical polishing liquid for aluminum materials, which is prepared by the following raw materials by mass percentage: 15% trimethylbutylcarboxylate quaternary phosphonium hydrogen oxalate ionic liquid, 2% citric acid, 1% Polyethylene glycol, 0.5% coco acid diethanolamide, balance water.

[0044] see figure 1 , this embodiment also provides a polishing method for aluminum chemical polishing liquid, comprising the following steps:

[0045] Step 1: First prepare the chemical polishing liquid for aluminum material by ionic liquid, additives and water according to the actual required ratio, and introduce it into the polishing tank and heat it to 80 °C for use;

[0046] Step 2: First clean the surface of the aluminum to be polished, and then put the cleaned aluminum directly into the aluminum chemical polishing solution in the polishing tank to soak for 0.5 minutes, then take out the aluminum and put it into the washing tank to wash with water Cl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
mean roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum material chemical polishing solution and a polishing method thereof.The aluminum material chemical polishing solution is prepared by mixing an ionic liquid, an additive and water, and the using method of the aluminum material chemical polishing solution comprises the steps that the aluminum material chemical polishing solution is prepared firstly, then chemical polishing treatment is conducted on a to-be-polished aluminum material, and finally the used aluminum material chemical polishing solution is recycled. The polishing solution is treated and recycled and is used for the aluminum material polishing procedure again, repeated recycling is achieved, toxic substances such as yellow smoke and irritant gas are not generated in the using process, harm to the human body and the environment is small, meanwhile, due to the fact that the polishing solution can be recycled, low emission and low pollution are achieved, and the polishing solution is environmentally friendly. The polishing solution is composed of ionic liquid with low concentration, most of the ionic liquid is composed of water, the problem that the polishing solution is lost due to the fact that the aluminum material is attached to and taken out of the polishing solution is obviously solved in the using process, a solution in a rinsing bath can be recycled into the polishing bath after polishing and is used for chemical polishing of the aluminum material, cost is saved, and pollution to the environment is avoided.

Description

technical field [0001] The invention relates to the technical field of polishing liquids, in particular to a chemical polishing liquid for aluminum materials and a polishing method thereof. Background technique [0002] Aluminum has the advantages of light weight, good ductility, corrosion resistance and easy plastic processing. It has been widely used in aerospace, aviation, electronics, automobiles, ships and many other fields. However, during the use of aluminum products, aluminum products will be Corrosion occurs in different degrees, and at the same time, because of its low wear resistance, the decorative and functional properties of aluminum products are not good. In order to improve this shortcoming of aluminum products, it is usually necessary to Surface treatment is carried out to improve its application value, and surface polishing is an important processing technology in the surface treatment of aluminum products, mainly including mechanical polishing, chemical po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/03B01D36/00B01D15/10B01D15/22
CPCC23F3/03B01D36/00B01D15/10B01D15/22Y02P10/20
Inventor 陶国宏朱秋红张国浩何玲
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com