An environmentally friendly, nitrate-based technology for enamel applications
Pending Publication Date: 2022-04-12
SINOPIGMENT & ENAMEL CHEM
View PDF8 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0016] One of the objectives of the present invention is to provide a nitrate-free environment-friendly low-temperature titanium white surface glaze for steel plate enamel without reducing the performance indicators of the product in view of the above-mentioned environmental protection problems existing in the current traditional nitrate-containing steel plate enamel enamel
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0043] (1) Take the raw materials by the mass parts of the following components:
[0045] (2) Stir and mix the above raw materials evenly.
[0046] (3) Put the uniformly mixed material into the melting furnace, and melt it under the condition of pure oxygen, and control the melting temperature at 1230±10°C.
[0047] (4) After the above materials are completely melted, the borosilicate glass body is obtained, and the molten borosilicate glass body is brazed, and quickly drawn into a glass filament of 1.2 to 1.5 meters for detection. The detection requirement is: within 1 meter of the glass filament. The knot is the completion of melting.
[0048] (5) Quenching (water quenching) the melted borosilicate glass body to obtain the product.
Embodiment 2
[0050] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:
[0051] The mass parts of each component in the step (1) are: quartz 39KG, zero-water borax 34KG, cobalt oxide 0.012KG, titanium dioxide 15KG, magnesium carbonate 2KG, sodium tripolyphosphate 3.6KG, sodium fluorosilicate 7KG, potassium carbonate 5.5 KG, alumina 1.8KG.
[0052] In step (5), rapid cooling of the melted borosilicate glass body adopts a tableting process.
Embodiment 3
[0054] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:
[0055] The mass parts of each component in the step (1) are: quartz 39KG, zero-water borax 35KG, cobalt oxide 0.012KG, titanium dioxide 15KG, magnesium carbonate 2KG, sodium tripolyphosphate 3.6KG, sodium fluorosilicate 6.5KG, potassium carbonate 5KG, alumina 1.8KG.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a nitrate-free environment-friendly steel plate enamel low-temperature titanium dioxide cover glaze and a preparation method thereof. The invention belongs to the technical field of enamel. The formula comprises the following components in parts by mass: 38-40 parts of quartz, 33-35 parts of borax anhydrous, 0.01-0.02 part of cobalt oxide, 14-16 parts of titanium dioxide, 1.8-2.5 parts of magnesium carbonate, 2-4 parts of sodium tripolyphosphate, 6-8 parts of sodium fluosilicate, 4-6 parts of potassium carbonate and 1.5-2 parts of aluminum oxide. The raw materials are uniformly mixed according to the proportion and are molten under the condition of pure oxygen at 1230 + / -10 DEG C, and the firing temperature of the finished product is 760-790 DEG C. The formula of the low-temperature titanium white cover glaze does not contain nitrate, and the major technical problem that in the production process of existing steel plate enamel low-temperature titanium white cover glaze, nitrogen oxide (NOx) gas is generated and discharged to pollute the environment is fundamentally solved.
Description
technical field [0001] The invention belongs to the technical field of enamel, and in particular relates to a nitrate-free environment-friendly steel plate enamel low-temperature titanium white surface glaze and a preparation method thereof. Background technique [0002] Enamel enamel is mainly composed of feldspar, quartz and other refractory raw materials, borax, sodium nitrate, potassium nitrate, soda ash and other fusible chemical raw materials, as well as characteristic raw materials such as non-ferrous metal oxides. They are mixed in a certain proportion, melted at high temperature, and rapidly cooled into granules or flakes. Shaped borosilicate glass bodies were prepared. [0003] The introduction of nitrates (sodium nitrate, potassium nitrate, etc.) into enamel glazes as oxidants and fluxes has become a consensus in the industry, and it is an indispensable raw material for enamel glazes in traditional enamel theory. So far, there is no safe, colorless, reasonably pr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.