Nitrate-free environment-friendly steel plate enamel high-temperature transparent glaze and preparation method thereof

An environmentally friendly, nitrate technology, applied in the field of enamel, achieves the effect of increasing the oxidizing atmosphere, reducing the usage, and solving the pollution of the environment

Pending Publication Date: 2022-04-19
SINOPIGMENT & ENAMEL CHEM
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] One of the purposes of the present invention is to provide a nitrate-free environment-friendly high-temperature transparent glaze for steel plate enamel without reducing the performance indicators of the product in view of the above-mentioned environmental protection problems existing in the current traditional nitrate-containing enamel enamel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrate-free environment-friendly steel plate enamel high-temperature transparent glaze and preparation method thereof
  • Nitrate-free environment-friendly steel plate enamel high-temperature transparent glaze and preparation method thereof
  • Nitrate-free environment-friendly steel plate enamel high-temperature transparent glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) Take the raw materials by the mass parts of the following components:

[0043] Zero water borax 21KG, potassium feldspar 37.5KG, quartz 20KG, sodium fluorosilicate 7.6KG, fluorite 5.5KG, titanium dioxide 5KG, alumina 7KG, barium carbonate 3KG;

[0044] (2) Stir and mix the above-mentioned raw materials;

[0045] (3) Put the uniformly mixed material into a melting furnace, and melt it under the condition of pure oxygen, and control the melting temperature at 1290±10°C.

[0046] (4) After the above materials are completely melted, the borosilicate glass body is obtained, and the molten borosilicate glass body is brazed, and quickly drawn into a glass filament of 1.2 to 1.5 meters for detection. The detection requirement is: within 1 meter of the glass filament. The knot is the completion of melting.

[0047] (5) Quenching (pressing) the melted borosilicate glass body to obtain the product.

Embodiment 2

[0049] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:

[0050] The mass parts of each component in the step (1) are: zero-water borax 22KG, potassium feldspar 37KG, quartz 20KG, sodium fluorosilicate 7KG, fluorite 6.2KG, titanium dioxide 5KG, aluminum oxide 7KG, barium carbonate 3KG.

[0051] In step (5), quenching the melted borosilicate glass body is a process of water quenching.

Embodiment 3

[0053] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:

[0054] The mass parts of each component in the step (1) are: zero-water borax 23KG, potassium feldspar 36.7KG, quartz 20KG, sodium fluorosilicate 6.3KG, fluorite 6.8KG, titanium dioxide 5KG, aluminum oxide 7KG, barium carbonate 3KG .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nitrate-free environment-friendly steel plate enamel high-temperature transparent glaze and a preparation method thereof, and belongs to the technical field of enamel, and the formula comprises the following components in parts by mass: 21-23 parts of borax anhydrous, 36-38 parts of potassium feldspar, 19-21 parts of quartz, 6-8 parts of sodium fluosilicate, 5-7 parts of fluorite, 4-6 parts of titanium dioxide, 6-8 parts of aluminum oxide and 2-4 parts of barium carbonate. The raw materials are uniformly mixed according to the proportion and are molten under the condition of pure oxygen at 1290 + / -10 DEG C, and the firing temperature of the finished product is 850-880 DEG C. The formula does not contain nitrate, and the major technical problem that in the production process of existing steel plate enamel high-temperature transparent glaze, nitrogen oxide (NOx) gas is generated and discharged to pollute the environment is fundamentally solved.

Description

technical field [0001] The invention belongs to the technical field of enamel, and in particular relates to a nitrate-free environment-friendly high-temperature transparent glaze for steel plate enamel and a preparation method thereof. Background technique [0002] Enamel enamel is mainly composed of feldspar, quartz and other refractory raw materials, borax, sodium nitrate, potassium nitrate, soda ash and other fusible chemical raw materials, as well as characteristic raw materials such as non-ferrous metal oxides. They are mixed in a certain proportion, melted at high temperature, and rapidly cooled into granules or flakes. Shaped borosilicate glass bodies were prepared. [0003] The introduction of nitrates (sodium nitrate, potassium nitrate, etc.) into enamel glazes as oxidants and fluxes has become a consensus in the industry, and it is an indispensable raw material for enamel glazes in traditional enamel theory. So far, there is no safe, colorless, reasonably priced o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/06
CPCC03C8/06C03C2207/04
Inventor 汤上张全福郭浩
Owner SINOPIGMENT & ENAMEL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com