Nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant ground coat and preparation method thereof

An environmentally friendly, nitrate-based technology applied in the field of enamel

Pending Publication Date: 2022-04-19
SINOPIGMENT & ENAMEL CHEM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] One of the purposes of the present invention is to provide a nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant underglaze for the above-mentioned environmental protection problems existing in the current traditional nitrate-containing enamel enamel without reducing the performance indicators of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant ground coat and preparation method thereof
  • Nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant ground coat and preparation method thereof
  • Nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant ground coat and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Weigh the raw materials according to the mass parts of the following components:

[0041] Quartz 52kg, zero-water borax 27.0kg, soda ash 5.7kg, manganese oxide 1.6kg, cobalt oxide 0.8kg, calcium carbonate 5.0kg, sodium fluorosilicate 4.3kg, titanium dioxide 3.7kg, potassium feldspar 2.6kg, lithium carbonate 3.6kg .

[0042] SiO in quartz 2 The mass proportion of ≥99.5%, SiO in potassium feldspar 2 The mass proportion of titanium dioxide is ≥71%, the mass proportion of titanium dioxide in titanium dioxide is ≥99.0%, the mass proportion of Co in cobalt oxide is ≥71%, and other raw materials are industrial-grade purity.

[0043] (2) Stir and mix the above raw materials evenly.

[0044] (3) Put the uniformly mixed material into the melting furnace, and melt it under the condition of pure oxygen, and control the melting temperature at 1290±10°C.

[0045] (4) After the above materials are completely melted, the borosilicate glass body is obtained, and the molten boros...

Embodiment 2

[0048] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:

[0049] The mass parts of each component in step (1) are: quartz 52kg, zero-water borax 25.5kg, soda ash 6.2kg, manganese oxide 1.6kg, cobalt oxide 0.8kg, calcium carbonate 5.0kg, sodium fluorosilicate 4.6kg, titanium dioxide 3.7kg, potassium feldspar 2.9kg, lithium carbonate 3.7kg.

[0050] In step (5), the process of rapidly cooling the melted borosilicate glass body is by tableting.

Embodiment 3

[0052] The preparation process of this embodiment and embodiment 1 is basically the same, the difference is:

[0053] The mass parts of each component in step (1) are: quartz 52kg, zero-water borax 24.9kg, soda ash 6.3kg, manganese oxide 1.6kg, cobalt oxide 0.8kg, calcium carbonate 5.0kg, sodium fluorosilicate 4.9kg, titanium dioxide 3.7kg, potassium feldspar 3.6kg, lithium carbonate 3.8kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant ground coat and a preparation method thereof, and belongs to the technical field of enamel, the formula comprises the following components by mass: 50-54 parts of quartz, 24-27 parts of anhydrous borax, 5-7 parts of sodium carbonate, 1.5-1.7 parts of manganese oxide, 0.7-0.9 part of cobalt oxide, 4.5-5.5 parts of calcium carbonate, 4-5 parts of sodium fluosilicate, 3.0-4.0 parts of titanium dioxide, and 2.0-3.8 parts of potassium feldspar. And 3.5 to 4.5 parts of lithium carbonate. The raw materials are uniformly mixed according to the proportion and are molten under the condition of pure oxygen at 1290 + / -10 DEG C, and the firing temperature of the finished product is 800-820 DEG C. The formula does not contain nitrate, and the major technical problem that in the production process of existing cast iron enamel high-temperature acid-resistant ground coat, nitrogen oxide (NOx) gas is generated and discharged to pollute the environment is fundamentally solved.

Description

technical field [0001] The invention belongs to the technical field of enamel, and in particular relates to a nitrate-free environment-friendly cast iron enamel high-temperature acid-resistant bottom glaze and a preparation method thereof. Background technique [0002] Enamel enamel is mainly composed of feldspar, quartz and other refractory raw materials, borax, sodium nitrate, potassium nitrate, soda ash and other fusible chemical raw materials, as well as characteristic raw materials such as non-ferrous metal oxides. They are mixed in a certain proportion, melted at high temperature, and rapidly cooled into granules or flakes. Shaped borosilicate glass bodies were prepared. [0003] The introduction of nitrates (sodium nitrate, potassium nitrate, etc.) into enamel glazes as oxidants and fluxes has become a consensus in the industry, and it is an indispensable raw material for enamel glazes in traditional enamel theory. So far, there is no safe, colorless, reasonably pric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C23D5/00
CPCC03C8/00C23D5/00
Inventor 汤上殷乐颜顺时
Owner SINOPIGMENT & ENAMEL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com