High-temperature glue for ceramic material as well as preparation method and application of high-temperature glue

A technology of ceramic material and high temperature glue, applied in the field of high temperature glue, can solve problems such as poor high temperature resistance, achieve the effects of stable and orderly structure, simple and uncomplicated preparation process, and stable high temperature resistance

Pending Publication Date: 2022-03-15
SHENZHEN STAIR AUTOMOBILE SALES
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the high temperature resistant adhesives currently on the market have problems such as poor high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] The present invention also proposes a method for preparing high-temperature glue for ceramic materials, comprising the following steps:

[0060] Weighing and mixing the raw materials constituting the high-temperature glue for ceramic materials according to the formula to obtain the mixed raw materials; dispersing the mixed raw materials for a preset time under the condition of a preset rotating speed, and obtaining the high-temperature glue for ceramic materials. Specifically, the preset speed range is 500-5000r / min, and the preset time range is 100-500s. In this embodiment, within the preset speed range and preset time range, the raw materials of the high-temperature glue for ceramic materials can be better mixed, so that the chemical reaction between the raw materials is more sufficient, and the obtained ceramic material The high temperature resistance performance is better with high temperature glue. Preferably, the preset rotation speed is 1200r / min, and the preset...

Embodiment 1

[0068] The high-temperature glue for ceramic materials includes 10 parts by weight of silicon dioxide with a large particle size; 2 parts by weight of silicon dioxide with a small particle size; 26 parts by weight of aluminum oxide with a large particle size; Aluminum; 2.5 parts by weight of aluminum oxide with a small particle size; the balance is sodium silicate; wherein, the particle size range of the silicon dioxide with a large particle size is 40-50 μm, and the particle size range of the silicon dioxide with a small particle size is 2.4~4.4μm; the particle size range of large particle size alumina is 33~43μm, the particle size range of medium particle size alumina is 8~12μm, and the particle size range of small particle size alumina is 5.5~7.5μm .

[0069] A method for preparing high-temperature glue for ceramic materials, comprising the following steps:

[0070] Weighing and mixing the raw materials constituting the high-temperature glue for ceramic materials according...

Embodiment 2

[0081] The high-temperature glue for ceramic materials includes 11 parts by weight of silicon dioxide with a large particle size; 2.2 parts by weight of silicon dioxide with a small particle size; 27 parts by weight of aluminum oxide with a large particle size; Aluminum; 3 parts by weight of aluminum oxide with a small particle size; the balance is sodium silicate; wherein, the particle size range of the silicon dioxide with a large particle size is 40-50 μm, and the particle size range of the silicon dioxide with a small particle size is 2.4~4.4μm; the particle size range of large particle size alumina is 33~43μm, the particle size range of medium particle size alumina is 8~12μm, and the particle size range of small particle size alumina is 5.5~7.5μm .

[0082] A method for preparing high-temperature glue for ceramic materials, comprising the following steps:

[0083] Weighing and mixing the raw materials constituting the high-temperature glue for ceramic materials according...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses high-temperature glue for a ceramic material and a preparation method and application of the high-temperature glue for the ceramic material, and the high-temperature glue for the ceramic material comprises the following components in parts by weight: 10-14 parts of large-particle-size silicon dioxide; 2-4 parts by weight of silicon dioxide with a small particle size; 26-30 parts by weight of aluminum oxide having a large particle size; 5-7 parts by weight of aluminum oxide with a medium particle size; 2.5-4.5 parts by weight of alumina having a small particle size; and the balance of sodium silicate. Wherein the particle size range of the large-particle-size silicon dioxide is 40-50 microns, and the particle size range of the small-particle-size silicon dioxide is 2.4-4.4 microns; the particle size range of the aluminum oxide with the large particle size is 33-43 microns, the particle size range of the aluminum oxide with the medium particle size is 8-12 microns, and the particle size range of the aluminum oxide with the small particle size is 5.5-7.5 microns. According to the technical scheme, the high-temperature glue for the ceramic material is stable in high-temperature resistance.

Description

technical field [0001] The invention relates to the technical field of high-temperature glue, in particular to a high-temperature glue for ceramic materials and its preparation method and application. Background technique [0002] High-temperature glue is a high-temperature-resistant inorganic nanocomposite binder made of inorganic nanomaterials through polycondensation reaction. Through the screening of the composition ratio and preparation process parameters, the binder is a suspension dispersion system with a neutral pH value. , not only has strong adhesion and is non-corrosive to metal substrates, but also can maintain good adhesion performance and corrosion resistance at high temperatures, and has a long service life. High-temperature glue is easy to use and can be used for direct bonding of high-temperature resistant materials. The paint can be directly sprayed on the surface of a high-temperature substrate at 400-1000°C. When the water volatilizes, the paint will inst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J1/02C09J11/04C04B37/00
CPCC09J1/02C09J11/04C04B37/003
Inventor 林先华崔伟
Owner SHENZHEN STAIR AUTOMOBILE SALES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com