Concrete surface anti-carbonization curing agent, preparation method and application thereof

A technology for concrete surface and curing agent, applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc. Economic benefits and market value, high production efficiency, simple production process

Active Publication Date: 2022-01-28
SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Ordinary concrete surface curing agents have single ingredients, mainly for moisturizing and curing the concrete surface, and have disadvantages such as single curing effect, low curing agent curing efficiency, and poor surface anti-carbonation effect. Therefore, it is urgent to develop a curing and anti-carbonation performance Concrete surface curing agent, this new type of concrete surface anti-carbonation curing agent can improve the durability and performance of building materials, and provide favorable conditions for the building materials industry to increase market competitiveness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete surface anti-carbonization curing agent, preparation method and application thereof
  • Concrete surface anti-carbonization curing agent, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The present embodiment provides a kind of concrete maintenance agent, and its raw material comprises: α-methacrylic acid 150kg, sodium thiocyanate 190kg, acrylic acid emulsion 90kg, dodecyl alcohol ester 4kg, nano silicon dioxide 170kg, nano montmorillonite powder 45kg, Hydroxypropyl methylcellulose 3kg, industrial ethanol 1kg, water 195kg.

[0033] Wherein, the particle diameter of the nano silicon dioxide is 10nm, and the particle diameter of the nano montmorillonite powder is 10nm.

Embodiment 2

[0035]The present embodiment provides a kind of concrete maintenance agent, and its raw material comprises: α-methacrylic acid 230kg, sodium thiocyanate 240kg, acrylic acid emulsion 70kg, dodecyl alcohol ester 2kg, nano silicon dioxide 170kg, nano montmorillonite powder 35kg, Hydroxypropyl methylcellulose 1kg, industrial ethanol 1kg, water 206kg.

[0036] Wherein, the particle diameter of the nano silicon dioxide is 30nm, and the particle diameter of the nano montmorillonite powder is 30nm.

Embodiment 3

[0038] The present embodiment provides a kind of concrete maintenance agent, and its raw material comprises: α-methacrylic acid 200kg, sodium thiocyanate 220kg, acrylic acid latex 80kg, dodecyl alcohol ester 3kg, nano silicon dioxide 190kg, nano montmorillonite powder 35kg, Hydroxypropyl methylcellulose 1kg, industrial ethanol 3kg, water 195kg.

[0039] Wherein, the particle diameter of the nano-silica is 20nm, and the particle diameter of the nano-montmorillonite powder is 20nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a concrete surface anti-carbonization curing agent, a preparation method and application thereof. The concrete surface anti-carbonization curing agent comprises the following raw materials in parts by weight: 150 to 230 parts of alpha-methacrylic acid, 190 to 240 parts of sodium thiocyanate, 70 to 90 parts of acrylic emulsion, 2 to 4 parts of 2, 2, 4-trimethyl-1, 3-pentanediol monoisobutyrate, 170 to 190 parts of nano silicon dioxide, 35 to 45 parts of nano montmorillonite powder, 1 to 3 parts of hydroxypropyl methyl cellulose, 1 to 3 parts of industrial ethanol and 195 to 206 parts of water. According to the invention, after the curing agent is sprayed on the surface of concrete, a thin compact nano-film can be quickly formed on the surface, so that the evaporation speed of water on the surface of the concrete can be remarkably reduced in a dry and windy severe environment; and the curing agent contains the anti-carbonization component and the permeation component, so that under the synergistic effect of the anti-carbonization component and the permeation component, the curing agent can effectively act on the concrete surface, and the carbonization depth of the concrete surface is obviously reduced.

Description

technical field [0001] The invention relates to the technical field of maintenance of building materials, in particular to a concrete surface anti-carbonization maintenance agent and its preparation method and application. Background technique [0002] After the concrete is poured, if the climate is hot and the air is dry, if the maintenance is not carried out in time, the moisture in the concrete will evaporate too quickly, forming a dehydration phenomenon, which will make the cement particles that have formed a gel body unable to fully hydrate and cannot be transformed into stable crystals. Lack of sufficient cohesion, resulting in flaking or powdering off the concrete surface. In addition, when the concrete does not have sufficient strength, the premature evaporation of water will also cause large shrinkage deformation and dry shrinkage cracks. Therefore, the maintenance of the initial stage after concrete pouring is very important. The concrete should be cured immediate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/65
CPCC04B41/5037C04B41/65C04B41/009C04B28/00C04B41/4543C04B41/5035C04B41/46C04B41/463C04B41/4857C04B41/4803Y02W30/91
Inventor 肖波李先勇桂根生敬尧刘登贤彭文彬吴鑫江晓君关素敏张荣华魏天酬任春蓉崔贺龙路珏
Owner SICHUAN HUASHI GREEN HOMELAND BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap