A kind of amorphous melting flux and its preparation method and application

A technology of smelting flux and amorphous state, which is applied in the welding of structural steel for ships and ocean engineering, amorphous smelting flux and its preparation, can solve the problem of affecting the safe use performance of marine equipment, the decline of weld mechanical properties, and the inability to To meet service requirements and other issues, achieve the effects of reducing defects, improving mechanical properties, and improving low-temperature impact toughness

Active Publication Date: 2022-02-22
NORTHEASTERN UNIV LIAONING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, when marine steel is welded under high heat input, especially when the heat input is greater than 50kJ / cm, the mechanical properties of the weld will be seriously reduced, even lower than the mechanical properties of the base steel plate, and sometimes hydrogen embrittlement
The above problems will affect the safe use performance of marine engineering equipment, causing it to fail to meet service requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of amorphous melting flux and its preparation method and application
  • A kind of amorphous melting flux and its preparation method and application
  • A kind of amorphous melting flux and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] The amorphous smelting flux provided in this embodiment is made of the following components in terms of mass percentage: CaF 2 25%, CaO 35%, SiO 2 35% and TiO 2 5%.

[0083] The preparation method of the amorphous molten flux provided in this embodiment comprises the following steps:

[0084] (1) After crushing each raw material to a particle size of 80 mesh, weigh it according to the above mass percentage, then pour each weighed raw material into a blender, mix and stir for 30 minutes, and put it into an electric furnace for melting after stirring evenly. The temperature is 1450°C, and the temperature is kept for 20 minutes to obtain the molten material;

[0085] (2) Water quenching and granulation of the molten material obtained in step (1) to obtain a semi-finished product of gray-black amorphous flux particles; the mass ratio of the molten material to the water used for water quenching is 1:12;

[0086] (3) Put the semi-finished product of amorphous flux parti...

Embodiment 2

[0088] The amorphous smelting flux provided in this embodiment is made of the following components in terms of mass percentage: CaF 2 23%, CaO 33%, SiO 2 33% and TiO 2 11%.

[0089] The preparation method of the amorphous molten flux provided in this embodiment comprises the following steps:

[0090] (1) After crushing each raw material to a particle size of 120 mesh, weigh it according to the above mass percentage, then pour each weighed raw material into a blender, mix and stir for 20 minutes, and put it into an electric furnace for melting after stirring evenly. The temperature is 1480°C, and the temperature is kept for 20 minutes to obtain the molten material;

[0091] (2) Water-quenching and granulating the molten material obtained in step (1) to obtain a semi-finished product of gray-black amorphous flux particles; the mass ratio of the molten material to the water used for water quenching is 1:15;

[0092] (3) Put the semi-finished product of amorphous flux partic...

Embodiment 3

[0094] The amorphous smelting flux provided in this embodiment is made of the following components in terms of mass percentage: CaF 2 20%, CaO 32.5%, SiO 2 32.5% and TiO 2 15%.

[0095] The preparation method of the amorphous molten flux provided in this embodiment comprises the following steps:

[0096] (1) After crushing each raw material to a particle size of 100 mesh, weigh it according to the above mass percentage, then pour each weighed raw material into a blender, mix and stir for 25 minutes, and put it into an electric furnace for melting after stirring evenly. The temperature is 1500°C, and the temperature is kept for 15 minutes to obtain the molten material;

[0097] (2) Water-quenching and granulating the molten material obtained in step (1) to obtain a gray-black semi-finished product of amorphous flux particles; the mass ratio of the molten material to the water used for water quenching is 1:14;

[0098] (3) Put the semi-finished product of amorphous flux pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of welding technology, in particular to an amorphous melting flux and its preparation method and application. Amorphous melting flux is made of the following components in mass percent: CaF 2 20%~25%, CaO 30%~35%, SiO 2 30%~35% and TiO 2 5%~15%. The amorphous smelting flux has the advantages of no moisture absorption, good slag detachability, and effective reduction of harmful elements such as P and S in the weld by adopting specific components and dosages thereof. At the same time, the flux is in an amorphous state, and the composition of the weld seam obtained after welding is uniform, and the mechanical properties of the weld seam are excellent, especially the low temperature toughness of the weld seam is good.

Description

technical field [0001] The present invention relates to the field of welding technology, in particular, to an amorphous smelting flux and its preparation method and application, more specifically, to an amorphous smelting flux and its preparation method, and structures for ships and marine engineering Steel welding methods. Background technique [0002] With the development of resource mining from shallow sea to deep sea and polar alpine regions, the application environment of marine engineering equipment is more complex, so the requirements for materials are getting higher and higher. Marine steel is welded with large heat input energy during use, and the large heat input submerged arc welding technology can significantly improve the efficiency of welding operations. Therefore, the large heat input submerged arc welding technology has gradually become an important means of efficient manufacturing of marine engineering steel. [0003] However, when marine steel is welded un...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/362B23K35/40B23K9/18
CPCB23K35/3602B23K35/362B23K35/0255B23K35/40B23K9/18
Inventor 王聪张燕云王占军钟明袁晓波
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com