High-explosion-capacity synergistic energetic micro-projectile

A high-explosive capacity type, projectile technology, applied in the direction of non-explosive/non-thermal agent components, offensive equipment, explosives, etc., can solve the problems of damage power and insufficiency, and achieve improved explosive capacity value, low cost, and easy mass production Effect

Inactive Publication Date: 2021-10-29
BEIJING INSTITUTE OF TECHNOLOGYGY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the dosage is reduced, it will also bring about the problem of insufficient damage power

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing high-explosion-volume synergistic energetic micro-projectiles, the specific steps are as follows:

[0018] (1) Modified coating

[0019] Surface modification: Add the silane coupling agent to ethyl acetate, stir for 0.5h, and under the protection of an inert atmosphere, disperse the active metal powder into the solution, soak for 6h, filter and dry to obtain the modified metal powder;

[0020] Coating: adding the binder into ethyl acetate, stirring until completely dissolved, and dispersing the above-mentioned modified metal powder into the solution, stirring for 2 hours, to obtain a dispersion of the binder-coated metal powder.

[0021] (2) Molding preparation

[0022] Powder mixing: Add high molecular fluoropolymer and high explosive capacity synergist potassium chlorate to the dispersion obtained from the polyurethane elastomer coated metal powder, and stir for 4 hours to obtain a slurry;

[0023] Granulation: Extrude and granulate the slurry...

Embodiment 2

[0026] A method for preparing high-explosion-volume synergistic energetic micro-projectiles, the specific steps are as follows:

[0027] (1) Modified coating

[0028] Surface modification: Add the silane coupling agent to ethyl acetate, stir for 0.5h, and under the protection of an inert atmosphere, disperse the active metal powder into the solution, soak for 6h, filter and dry to obtain the modified metal powder;

[0029] Coating: adding the binder into ethyl acetate, stirring until completely dissolved, and dispersing the above-mentioned modified metal powder into the solution, stirring for 2 hours, to obtain a dispersion of the binder-coated metal powder.

[0030] (2) Molding preparation

[0031] Powder mixing: adding high molecular weight fluoropolymer and high explosive capacity synergist potassium perchlorate to the above-mentioned dispersion obtained by coating metal powder with polyurethane elastomer, and stirring for 4 hours to obtain a slurry;

[0032] Granulation:...

Embodiment 3

[0035] A method for preparing high-explosion-volume synergistic energetic micro-projectiles, the specific steps are as follows:

[0036] (1) Modified coating

[0037] Surface modification: Add the silane coupling agent to ethyl acetate, stir for 0.5h, and under the protection of an inert atmosphere, disperse the active metal powder into the solution, soak for 6h, filter and dry to obtain the modified metal powder;

[0038] Coating: adding the binder into ethyl acetate, stirring until completely dissolved, and dispersing the above-mentioned modified metal powder into the solution, stirring for 2 hours, to obtain a dispersion of the binder-coated metal powder.

[0039] (2) Molding preparation

[0040] Powder mixing: Add high molecular fluoropolymer and high explosive capacity synergist potassium permanganate to the dispersion obtained from the polyurethane elastomer coated metal powder, and stir for 4 hours to obtain a slurry;

[0041] Granulation: Extrude and granulate the sl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-explosion-capacity synergistic energetic micro-projectile, and belongs to the field of special damage. The energetic micro-projectile is composed of a fluoropolymer-based energetic micro-projectile basic formula and a high-explosion-capacity synergist. The obtained product has the prominent characteristics that the damage effect of explosion heat can be increased to 110%-170% of the damage effect of the original formula, and the product has the advantages of no sulfur, no nitrogen, slight smoke, high explosion capacity, high safety and the like, and can be widely applied to the fields of air anti-conduction, armor breaking damage and the like.

Description

technical field [0001] The invention relates to a high-explosion-volume synergistic energetic micro-projectile, which belongs to the technical field of special damage. Background technique [0002] Energetic micro-projectiles are a newly developed class of new concept damage energetic materials. The principle is to design polymer oxidants and metal reductants through the core-shell structure, and then produce them under high-energy conditions such as high-speed impact, high-temperature ignition or laser ignition. Under triggering, a rapid and violent oxidation-reduction reaction occurs, thereby releasing high temperature to the outside, using the gaseous effect of metal fluoride under high temperature conditions to achieve volume expansion of thousands of times, thereby further generating overpressure, and forming a compound such as high temperature and overpressure on the target. The damage effect has broad application prospects in the fields of air defense and anti-missile...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C06B33/06C06B27/00C06B23/00
CPCC06B33/06C06B27/00C06B23/00
Inventor 束庆海赵帅石艳松王东旭吕席卷蒋教平束红年
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com