Preparation method of environment-friendly high-performance digital ink-jet red ink

A digital inkjet, high-performance technology, applied in the direction of ink, household utensils, applications, etc., can solve the problems of narrow application range, acid and alkali resistance and scratch resistance not meeting industry requirements, poor environmental protection, etc., and achieve bright colors stable effect

Active Publication Date: 2021-08-10
闻涛
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are very few types of glass inkjet printing inks on the market, for example, red ink, which cannot meet the needs of the market; the existing glass inkjet printing inks are not environmentally friendly, and contain heavy metals, such as lead, cadmium and other chemical elements. As a result, its scope of application is narrow; and the acid and alkali resistance and scratch resistance of the existing glass inkjet printing inks cannot meet the industry requirements, and technology updates are pending

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method of an environmentally friendly high-performance digital inkjet red ink, the preparation method comprises the following steps: (1) selecting 44 parts by weight of silica, 3 parts of alumina, 30 parts of bismuth trioxide and 2 parts of boron oxide parts, 1.1 parts of sodium oxide, 0.8 part of potassium oxide, 0.3 part of strontium oxide, 1 part of calcium oxide and 1 part of lithium oxide as raw materials, weigh the raw materials and put them into a mixer to stir evenly to obtain the first mixture; (2) The first mixture obtained in step (1) is added to a high-alumina crucible, and then the high-alumina crucible is heated and melted together in a high-temperature furnace, and the heating temperature is 1250° C. to obtain a second mixture; (3) Step (2) The second mixture obtained in the process is added to the purified water at room temperature, and the second mixture in the high temperature state is quenched in the purified water to be broken to obtain ...

Embodiment 2

[0030]A preparation method of an environmentally friendly high-performance digital inkjet red ink, the preparation method comprises the following steps: (1) selecting 46 parts by weight of silica, 4 parts of alumina, 32 parts of bismuth trioxide and 4 parts of boron oxide parts, 1.3 parts of sodium oxide, 0.9 parts of potassium oxide, 0.4 parts of strontium oxide, 3 parts of calcium oxide and 2 parts of lithium oxide as raw materials, after weighing the raw materials, put them into a mixer and stir evenly to obtain the first mixture; (2) The first mixture obtained in step (1) is added to the high-alumina crucible, and then the high-alumina crucible is heated and melted together in a high-temperature furnace, and the heating temperature is 1260° C. to obtain the second mixture; (3) Step (2) The second mixture obtained in the process is added to the purified water at normal temperature, and the second mixture in the high temperature state is quenched in the purified water to be b...

Embodiment 3

[0037] A preparation method of environment-friendly high-performance digital inkjet red ink, the preparation method comprises the following steps: (1) selecting 48 parts by weight of silica, 5 parts of alumina, 35 parts of bismuth trioxide and 5 parts of boron oxide parts, 1.5 parts of sodium oxide, 1 part of potassium oxide, 0.5 part of strontium oxide, 2 parts of calcium oxide and 2 parts of lithium oxide as raw materials, after weighing the raw materials, put them into a mixer and stir evenly to obtain a first mixture; (2) The first mixture obtained in step (1) is added to the high-alumina crucible, and then the high-alumina crucible is heated and melted together in a high-temperature furnace, and the heating temperature is 1275 ° C to obtain the second mixture; (3) Step (2) The second mixture obtained in the process is added to the purified water at normal temperature, and the second mixture in the high temperature state is quenched in the purified water to be broken to obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of environment-friendly high-performance digital ink-jet red ink, and relates to the technical field of glass painting, the preparation method comprises the following steps: (1) preparing basic color glaze powder; (2) preparing red wrapping powder; (3) preparing a primary finished product of the digital ink-jet red ink; and (4) carrying out negative pressure filtration to obtain a digital ink-jet red ink finished product, and then packaging. The ink does not contain heavy metals, and meets environmental protection requirements; the red ink is subjected to ink-jet printing on the surface of glass, then is sintered and tempered at the high temperature of 650-750 DEG C, is completely dissolved in the glass and is integrated with the glass, and the color is bright and stable; the acid resistance and the alkali resistance of the red ink completely reach the industrial standard, and the scratch resistance reaches the sixth level of the industrial standard.

Description

technical field [0001] The invention relates to the technical field of glass inkjet printing, in particular to a preparation method of an environment-friendly high-performance digital inkjet red ink. Background technique [0002] Tempered glass is a prestressed glass. The impact strength and bending strength of tempered glass with the same thickness are 3 to 5 times that of ordinary glass. Although the performance of tempered glass has advantages compared with ordinary glass, its decorative effect is poor. Digital inkjet printing is a technology of non-contact printing of digital patterns in a computer on a glass surface through a nozzle. Digital inkjet printing equipment can print ink on the surface of glass, and then sinter and temper the printed glass at a high temperature of 650-750 °C, so that the ink is fused with the surface of the glass and fixed on the surface of the glass. At present, there are very few types of glass inkjet printing inks on the market, such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/40C09D11/322
CPCC09D11/40C09D11/322
Inventor 闻涛
Owner 闻涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap