A preparation method of 7xxx series aluminum alloy rods based on mechanical ultrasonic vibration aging

An ultrasonic vibration, aluminum alloy technology, applied in the field of aluminum alloy processing, to achieve the effect of plasticity improvement, small roughness, and strength improvement

Active Publication Date: 2021-12-21
江苏江南创佳型材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above heat treatment process has a certain effect on improving the performance of 7XXX series alloys, there is still a lot of room for improvement in shortening the production cycle of this type of alloy and improving its corresponding fatigue resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of 7xxx series aluminum alloy rods based on mechanical ultrasonic vibration aging
  • A preparation method of 7xxx series aluminum alloy rods based on mechanical ultrasonic vibration aging

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The 7050 aluminum alloy ingot was homogenized at 470°C for 20 hours, then air-cooled; the air-cooled ingot was hot-extruded at 480°C, the extrusion ratio was 35, the extrusion speed was 1m / min, and water-cooled after extrusion , the diameter of the rod 1 obtained is 3cm; the hot extruded rod 1 is rotated through the mechanical ultrasonic vibration device 2 at a fixed position, the diameter of the cylindrical ultrasonic indenter 3 is 0.5cm, and the work of the ultrasonic indenter 3 The frequency is 20kHz, the maximum contact stress is 80N, the rotation speed of bar 1 is 3.18 rpm, and the forward speed of bar 1 is 6.37cm / min. After processing, a 7XXX series aluminum alloy bar based on mechanical ultrasonic vibration aging is obtained.

Embodiment 2

[0034] The 7050 aluminum alloy ingot was homogenized at 460°C for 6 hours, then air-cooled; the air-cooled ingot was hot-extruded at 470°C, the extrusion ratio was 15, the extrusion speed was 0.6m / min, and water-cooled after extrusion Processing, the diameter that obtains rod 1 is 20cm; The rod 1 after hot extrusion is rotated through the mechanical ultrasonic vibrating device 2 that is positioned at fixed position, and the diameter of cylindrical ultrasonic indenter 3 is 3cm, and the work of ultrasonic indenter 3 The frequency is 20kHz, the maximum contact stress is 100N, the rotation rate of bar 1 is 2.86 rpm, and the forward speed of bar 1 is 34.38cm / min. After processing, a 7XXX series aluminum alloy bar based on mechanical ultrasonic vibration aging is obtained.

Embodiment 3

[0036]The 7050 aluminum alloy ingot was homogenized at 480°C for 24 hours, then air-cooled; the air-cooled ingot was hot-extruded at 460°C, the extrusion ratio was 25, the extrusion speed was 1.2m / min, and water-cooled after extrusion Processing, the diameter that obtains rod 1 is 5cm; The rod 1 after hot extrusion is rotated through the mechanical ultrasonic vibrating device 2 that is positioned at fixed position, and the diameter of cylindrical ultrasonic indenter 3 is 0.5cm, and the diameter of ultrasonic indenter 3 The working frequency is 20kHz, the maximum contact stress is 60N, the rotation speed of bar 1 is 1.91 rpm, and the forward speed of bar 1 is 3.82cm / min. After the processing is completed, a 7XXX series aluminum alloy bar based on mechanical ultrasonic vibration aging is obtained. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a 7XXX series aluminum alloy rod based on mechanical ultrasonic vibration aging. The steps of the preparation method are as follows: A. Homogenize the 7XXX series aluminum alloy ingot; B. Homogenize the The ingot is hot-extruded into a bar; C. The hot-extruded bar is rotated through a mechanical ultrasonic vibration device at a fixed position to obtain a 7XXX series aluminum alloy bar based on mechanical ultrasonic vibration aging. The preparation method of the present invention uses a mechanical ultrasonic vibration aging device with four symmetrically distributed indenters to process hot extruded rods to promote the uniform precipitation of nanoscale precipitated phases in the alloy and the nanometerization and crystal grain size of the surface layer. The size gradient distribution, with good surface quality and uniformity, significantly improves the strength, toughness and fatigue resistance of 7XXX series aluminum alloys, realizing the combination of ultra-high strength and good plasticity.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy processing, in particular to a method for preparing 7XXX series aluminum alloy rods based on mechanical ultrasonic vibration aging. Background technique [0002] Because 7XXX series aluminum alloy has a series of advantages such as high strength, low density, good processing performance and resistance to stress corrosion cracking, it is often processed into various types of materials and widely used in rail transportation, aerospace, national defense and military fields. The 7XXX series aluminum alloys (mainly Al-Zn-Mg and Al-Zn-Mg-Cu two main alloy series) are typical precipitation-strengthened aluminum alloys, which are precipitated at the nanometer or submicron level in the alloy by controlling the effective aging process. Metastable precipitates such as Mg-Zn or Al-Mg-Zn can significantly increase the strength of the alloy and obtain ultra-high-strength aluminum alloys. [0003] The co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22F1/053C21D9/00C22F3/00B21C31/00
CPCC22F1/053C21D9/0075C22F3/00B21C31/00
Inventor 梅泽锋周宝华董春泉黄晓中
Owner 江苏江南创佳型材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com