Threaded hole protection glue and preparation method and application thereof

A technology of protective glue and threaded holes, which is applied in the direction of adhesives, non-polymer adhesive additives, adhesive additives, etc., and can solve problems such as difficult peeling and odor

Active Publication Date: 2021-05-07
上海仁速新材料有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Both of the above two light-curing protective adhesives use acrylate reactive diluents and polyurethane-modified acrylate resins, which have an odor and cross-link after light curing, making it difficult to peel off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Threaded hole protection glue and preparation method and application thereof
  • Threaded hole protection glue and preparation method and application thereof
  • Threaded hole protection glue and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] This embodiment provides a threaded hole protective glue and a preparation method thereof. The threaded hole protective glue includes the following components in mass percentage:

[0071]

[0072] The particle size of the aminopropyltriethoxysilane modified transparent powder is 1000 mesh.

[0073] The preparation method of the above threaded hole protective glue is as follows:

[0074] (1) Stir 2-acrylamide-2-methylpropanesulfonic acid, trehalose, and water at 25°C until uniform and transparent, then add carboxy-modified guar gum and continue stirring until evenly mixed to obtain mixture A ;

[0075] (2) Stir the mixture A obtained in step (1), fumed silica and aminopropyltriethoxysilane modified transparent powder at 35°C for 25 minutes to obtain mixture B;

[0076] (3) Stir the mixture B, acrylamide and sodium acrylate obtained in step (2) for 45 min at 25°C to obtain mixture C;

[0077] (4) Stir the mixture C obtained in step (3) with bis(2,4,6-trimethylbenzoy...

Embodiment 2

[0079] This embodiment provides a threaded hole protective glue and a preparation method thereof. The threaded hole protective glue includes the following components in mass percentage:

[0080]

[0081] The particle size of the aminopropyltriethoxysilane modified transparent powder is 1000 mesh.

[0082] The preparation method of the above threaded hole protective glue is as follows:

[0083] (1) Stir 2-acrylamide-2-methylpropanesulfonic acid, trehalose and water at 20°C until uniform and transparent, then add quaternary ammonium salt-modified guar gum, and continue stirring until the mixture is uniform. Mixture A is obtained;

[0084] (2) Stir the mixture A obtained in step (1), fumed silica and aminopropyltriethoxysilane modified transparent powder at 50°C for 15 minutes to obtain mixture B;

[0085] (3) Stir the mixture B, methacrylamide and potassium acrylate obtained in step (2) for 20 min at 40° C. to obtain mixture C;

[0086] (4) Under the condition of 40°C, sti...

Embodiment 3

[0088] This embodiment provides a threaded hole protective glue and a preparation method thereof. The threaded hole protective glue includes the following components in mass percentage:

[0089]

[0090] The initiator is composed of 2-hydroxy-4'-(2-hydroxyethoxy)-2-methyl propiophenone and two (2,4,6-trimethylbenzoyl) phenylphosphine oxide in mass ratio 1:1 composition, the particle size of the aminopropyltriethoxysilane modified transparent powder is 1200 mesh.

[0091] The preparation method of the above threaded hole protective glue is as follows:

[0092] (1) Under the condition of 30°C, stir 2-acrylamide-2-methylpropanesulfonic acid, trehalose and water until uniform and transparent, then add quaternary ammonium salt modified squash gum and continue stirring until uniformly mixed to obtain mixture A;

[0093] (2) Stir the mixture A obtained in step (1), fumed silica and aminopropyltriethoxysilane modified transparent powder at 40°C for 20 minutes to obtain mixture B;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
specific surface areaaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides threaded hole protection glue and a preparation method and application thereof. The threaded hole protection glue is prepared from the following components in percentage by mass: 15 to 20 percent of 2-acrylamide-2-methylpropanesulfonic acid, 16 to 23 percent of amide monomer, 15 to 20 percent of acrylate, 5 to 8 percent of trehalose, 10 to 20 percent of transparent powder, 0.5 to 2 percent of fumed silica and 2 to 3 percent of initiator. The preparation method comprises the following steps: mixing 2-acrylamide-2-methylpropanesulfonic acid, trehalose and water to obtain a mixture A; mixing the mixture A, fumed silica and transparent powder to obtain a mixture B; then mixing the mixture B, an amide monomer and acrylate to obtain a mixture C; and mixing the mixture C with an initiator to obtain the threaded hole protection glue. The threaded hole protection glue provided by the invention is resistant to high temperature, odorless, non-toxic, environment-friendly and safe, and can meet the processing requirements of surface treatment of structural parts of precise electronic products.

Description

technical field [0001] The invention belongs to the technical field of adhesives, and in particular relates to a threaded hole protective adhesive and its preparation method and application. Background technique [0002] With the development of society, many industries need to temporarily bond or protect materials under the limitation of technological conditions. For example, when a process needs to position the material or damage the material, UV glue can be used to bond or protect the material. After the process is completed, the UV glue is taken out and the next process is carried out. Due to the different processes, there are also various needs for temporary bonding or protective colloids. [0003] For example, the structural components of electronic products such as laptops, charging treasures, and mobile hard drives are often made of hard aluminum alloys. The screw holes on such structural components have the characteristics of small openings, low aperture ratio, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/04C09J11/06C09J11/08
CPCC09J4/06C09J11/04C09J11/06C09J11/08
Inventor 贾录阳刘翘楚何峰
Owner 上海仁速新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com