Ionic hydrogen bond organic framework material as well as preparation method and application thereof

An organic framework and ionic technology, which is applied in the field of ionic hydrogen bond organic framework materials and their preparation, achieves the effects of convenient operation, high yield and easy availability of synthetic raw materials

Active Publication Date: 2021-03-26
SHAANXI UNIV OF SCI & TECH
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide an ionic hydrogen-bonded organic framework material and its preparation method and application, which solves the stability problem of the existing hydrogen-bonded organic framework material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ionic hydrogen bond organic framework material as well as preparation method and application thereof
  • Ionic hydrogen bond organic framework material as well as preparation method and application thereof
  • Ionic hydrogen bond organic framework material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The invention also discloses a preparation method of the hydrogen-bonded organic framework material, which includes the following steps:

[0030] 1) Add TPE-SO 3 H and DBD are dissolved in a mixed solution of water and DMF according to a molar ratio of 1:1-2 to obtain a reaction liquid; wherein, the molar ratio of water and DMF is 1:1-2;

[0031] 2) The reaction solution obtained in step 2) was left to stand at room temperature to obtain yellow blocky crystals, which were dried naturally to obtain an ionic hydrogen-bonded organic framework material.

Embodiment 1

[0034] The invention discloses a preparation method of an ionic hydrogen bond organic framework material, which comprises the following steps:

[0035] 1) Add 1,1,2,2-tetraphenylethylene into concentrated sulfuric acid, react at 115°C for four hours, then quench with cold water, then add ethyl acetate, stir and filter, wash, filter and dry , get TPE-SO 3 H ligand powder;

[0036] 2) dissolving the powder obtained in step 1) and DBD in a mixed solution of water and DMF at a molar ratio of 1:1 to obtain a reaction solution; wherein the molar ratio of water to DMF is 1:1;

[0037] 3) The reaction solution obtained in step 2) was left to stand at room temperature to obtain yellow blocky crystals, which were naturally dried to obtain an ionic hydrogen-bonded organic framework material.

[0038] The yield of the hydrogen-bonded organic framework material obtained in this example was 65%.

Embodiment 2

[0040] The invention discloses a preparation method of an ionic hydrogen bond organic framework material, which comprises the following steps:

[0041]1) Add 1,1,2,2-tetraphenylethylene into concentrated sulfuric acid, react at 115°C for four hours, then quench with cold water, then add ethyl acetate, stir and filter, wash, filter and dry , get TPE-SO 3 H ligand powder;

[0042] 2) dissolving the powder obtained in step 1) and DBD in a mixed solution of water and DMF according to a molar ratio of 1:2 to obtain a reaction solution; wherein the molar ratio of water to DMF is 1:1;

[0043] 3) The reaction solution obtained in step 2) was left to stand at room temperature to obtain yellow blocky crystals, which were naturally dried to obtain an ionic hydrogen-bonded organic framework material.

[0044] The yield of the ionic hydrogen-bonded organic framework material obtained in this example was 80%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of preparation of ionic hydrogen bond organic framework materials, and particularly discloses an ionic hydrogen bond organic framework material with proton conduction performance, the chemical formula of the ionic hydrogen bond organic framework material is {TPE-SO3H. 2 (DBD). 2 (DMF). 4 (H2O)} n, n is a positive integer, TPE-SO3H is 1, 1, 2, 2-tetrasulfonic acidphenyl ethylene, DBD is (C5NH4NH2) 22+, and DMF is N, N '-dimethylformamide. The structural unit belongs to a triclinic system, the space group is P-1, the molecular formula is C52H62N10O18S4, the cell parameters are as follows: alpha = 102.789 degrees, beta = 99.968 degrees and gamma = 112.169 degrees, each repetitive unit comprises four water molecules and two DMF molecules, two DBD molecules and one TPE-SO3H molecule, and amino groups on the DBD molecules and sulfonate groups on the TPE-SO3H molecule form a one-dimensional hydrogen bond network with water molecules. The material has good thermal stability, and has good performance for proton transportation. The invention discloses the preparation method of the material, the synthetic raw materials are easy to obtain, and the preparation process is simple. The ionic hydrogen bond organic framework material disclosed by the invention can be used as a proton conducting material and has a very good application prospect.

Description

technical field [0001] The invention belongs to the field of preparation of hydrogen-bonded organic framework materials, and in particular relates to an ionic hydrogen-bonded organic framework material and its preparation method and application. Background technique [0002] Since entering the 21st century, with the rapid development of the world and further urbanization, our demand for energy is increasing, and it is imminent to find renewable clean energy. Among many new energy sources, proton exchange membrane fuel cells are less polluting to the environment and can directly convert fuel into electricity without burning, which can effectively promote the sustainable development of energy and avoid the limitations of fossil fuels. Proton exchange membrane fuel cells have the advantages of high efficiency and energy saving, fast start-up, wide variety of fuels, and long service life. Proton exchange membranes are mainly Nafion series perfluorosulfonic acid membranes produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G83/00H01M8/1032
CPCC08G83/008H01M8/1032Y02E60/50
Inventor 曹丽慧杨妍徐小倩白向田赵芳
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com