A kind of preparation method of anisotropic samarium cobalt magnetic powder

An anisotropic, samarium cobalt technology, used in the manufacture of inductors/transformers/magnets, magnetic objects, magnetic materials, etc., can solve the problems of low hydrogen absorption characteristics of samarium cobalt, difficulty in hydrogen absorption, and samarium cobalt particles cracking without breaking. , to achieve the effect of easy large-scale preparation, easy acquisition, and reduced requirements

Active Publication Date: 2022-05-17
杭州智宇磁业科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Publication No. 105304249A, Publication No. 105489331A, and Publication No. 106531383A use the hydrogen breaking process to prepare sintered samarium cobalt magnets, but the hydrogen absorption characteristics of samarium cobalt are much lower than that of neodymium iron boron
Only some characteristic components of samarium cobalt are easily damaged by hydrogen absorption, such as formulas with high iron content and high rare earth content, but it is still very difficult for samarium cobalt materials with general formulas (lower iron content and less rare earth content) to absorb hydrogen
In addition, even if the ingot or slab of samarium cobalt is conducive to hydrogen absorption and fragmentation due to the existence of 1:5 phase, 2:7 phase and 1:3 phase which are easy to absorb hydrogen, if samarium cobalt is sintered, solid solution and After aging, the 1:5 phase, 2:7 phase and 1:3 phase that are easy to absorb hydrogen almost completely disappear. At this time, it is more difficult to absorb hydrogen. Insufficient hydrogen absorption will cause the samarium cobalt particles to crack but not broken. At this time, it is necessary to use Other external forces to help break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of anisotropic samarium cobalt magnetic powder
  • A kind of preparation method of anisotropic samarium cobalt magnetic powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] The preparation method of anisotropic samarium cobalt magnetic powder in this embodiment is as follows:

[0059] (1) Melting and casting: The samarium-cobalt cast sheet is made by the quick-setting process, and the molecular formula of the samarium-cobalt alloy is Sm(Co bal Fe 0.25 Cu 0.06 Zr 0.02 Si 0.01 Ti 0.01 ) 7.8 , the quick-setting process adopts a copper roller cooling process, the linear speed of the copper roller is 0.5m / s, and the thickness of the samarium cobalt cast sheet is 0.8mm;

[0060] (2) Aging treatment: Place the samarium-cobalt cast piece in an inert gas environment, keep it at 830°C for 20h, then cool slowly to 400°C at a rate of 0.7°C / min and hold it for 5h, and finally at a rate of 50°C / min Cool to room temperature;

[0061] (3) Powder making: first place the samarium cobalt cast piece in a hydrogen absorbing device with a capacity of 300kg, put small steel balls with a weight of 100g / piece in the hydrogen absorbing device, the total weig...

Embodiment 2

[0063] The preparation method of anisotropic samarium cobalt magnetic powder in this embodiment is as follows:

[0064] (1) Melting and casting: The samarium-cobalt cast sheet is made by the quick-setting process, and the molecular formula of the samarium-cobalt alloy is Sm(Co bal Fe 0.20 mn 0.05 Cu 0.06 Zr 0.02 Ga 0.01 f 0.01 ) 7.4 , the quick-setting process adopts a copper roller cooling process, the linear speed of the copper roller is 0.5m / s, and the thickness of the samarium cobalt cast sheet is 0.8mm;

[0065] (2) Aging treatment: Place the samarium cobalt cast piece in an inert gas environment, keep it at 830°C for 25h, then slowly cool it to 400°C at a rate of 0.5°C / min and hold it for 5h, and finally at a rate of 50°C / min Cool to room temperature;

[0066] (3) Powder making: first place the samarium cobalt cast piece in a hydrogen absorbing device with a capacity of 300kg, put small steel balls with a weight of 100g / piece in the hydrogen absorbing device, the...

Embodiment 3

[0068] The preparation method of anisotropic samarium cobalt magnetic powder in this embodiment is as follows:

[0069] (1) Melting and casting: the samarium-cobalt cast sheet is made by the quick-setting process, and the molecular formula of the samarium-cobalt alloy is (Sm 0.8 Ce 0.2 )(Co bal Fe 0.22 Cu 0.06 Zr 0.02 V 0.01 f 0.01 ) 7.5 , the quick-setting process adopts a copper roller cooling process, the linear speed of the copper roller is 0.5m / s, and the thickness of the samarium cobalt cast sheet is 0.8mm;

[0070] (2) Aging treatment: place the samarium-cobalt cast piece in an inert gas environment, keep it at 830°C for 20h, then cool slowly to 400°C at a rate of 0.5°C / min and hold it for 5h, and finally at a rate of 50°C / min Cool to room temperature;

[0071] (3) Powder making: first place the samarium cobalt cast piece in a hydrogen absorbing device with a capacity of 300kg, put small steel balls with a weight of 200g / piece in the hydrogen absorbing device, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of anisotropic samarium-cobalt magnetic powder, which belongs to the technical field of bonded magnet materials. The preparation method of the anisotropic samarium-cobalt magnetic powder of the present invention comprises the following steps: (1) Melting and casting: passing samarium-cobalt alloy through rapid solidification process to make samarium-cobalt cast sheets, the samarium-cobalt alloy is a 2:17 type samarium-cobalt alloy, the composition of the samarium-cobalt alloy contains T2 element, and the T2 element is Si, Hf, Ti, V, Ga One or more; (2) aging treatment: aging treatment of samarium-cobalt castings; (3) powder making: making magnetic powder from the aging-treated samarium-cobalt castings; the preparation method of the present invention has simple preparation process, powder Uniform, easy to prepare on a large scale.

Description

technical field [0001] The invention relates to a preparation method of anisotropic samarium cobalt magnetic powder, belonging to the technical field of bonded magnet materials. Background technique [0002] Bonded rare-earth permanent magnet material is a new type of composite functional material, which refers to a magnet made of rare-earth permanent magnet powder and a certain proportion of binder according to a certain processing technology. The preparation process generally includes three processes of magnetic powder preparation, powder granulation and molding. Powder granulation refers to the process of mixing magnetic powder and binder with each other in a certain proportion to obtain mixed powder. The final size and shape of the bonded magnet is obtained at a certain temperature under a magnetic field or without a magnetic field. According to the final shape of bonded magnets, it can be divided into rigid rare earth bonded magnets and flexible rare earth bonded magne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F41/02H01F1/055
CPCH01F41/0253H01F41/0273H01F41/0266H01F1/0553
Inventor 卜海飞楼思浩
Owner 杭州智宇磁业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com