A kind of hips composite material and its preparation method and application

A composite material and raw material technology, applied in the field of modified plastics, can solve the problems of general heat resistance, poor barrier performance, non-antistatic, etc., and achieve the effect of good barrier grease, excellent barrier properties, and reduced surface resistance.

Active Publication Date: 2022-08-09
TIANJIN KINGFA NEW MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solve the common problems of non-antistatic, general heat resistance, and poor barrier properties in the use of ordinary PS materials for extruded blister packaging products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hips composite material and its preparation method and application
  • A kind of hips composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0043] A PS composite material with high strength, high heat resistance, antistatic properties and excellent barrier properties, its raw material formula is shown in Table 1, and its preparation method includes the following steps:

[0044] The above raw materials are uniformly mixed, and then fed from the main feeding port of the extruder. The raw materials are melted, extruded, and pelletized in the extruder to obtain PS with high strength, high heat resistance, antistatic, and excellent barrier properties. composite material; the pellets were injected into corresponding samples for testing, and the test results are shown in Table 2.

Embodiment 4

[0053] Compared with Comparative Example 3, Example 4 added copper acetate to reduce the resistance of the composite material.

Embodiment 1

[0054] Compared with Comparative Example 1, Example 1 added a toughening agent prepared from oil-extended SBS elastomer to improve the impact toughness of the composite material, and at the same time, the material could maintain better fluidity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides a HIPS composite material and a preparation method and application thereof, comprising the following components by mass percentage: HIPS resin: HIPS resin: 35-75 parts; PA resin: 15-40 parts; antistatic agent: 8-20 parts part; copper acetate: 0.1-0.5 part; toughening agent: 4-10 part; processing aid: 0.5-1.5 part. The HIPS composite material of the invention has the characteristics of high strength, high heat resistance, antistatic and excellent barrier properties.

Description

technical field [0001] The invention belongs to the field of modified plastics, and in particular relates to a HIPS composite material and a preparation method and application thereof. Background technique [0002] Styrene (PS) material is a common polymer, widely used in home appliances, electronic appliances, OA office equipment and other fields. Polystyrene material has the advantages of easy molding, good rigidity, and easy dyeing. However, the strength and heat resistance of PS materials are general, and the barrier properties are poor, which limits its application range. [0003] Due to the low polarity of conventional PS materials, the compatibility of materials modified by adding permanent antistatic agents with high polarity is not very good, especially when extruded products are easily delaminated. At the same time, the heat resistance of PS materials is general, and it cannot meet the requirements of some products with high temperature requirements, such as extr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L51/04C08L77/02C08L77/00C08L53/02C08K5/098
CPCC08L51/04C08L77/02C08L2201/08C08L2201/04C08L2205/035C08L2205/02C08L77/00C08L53/02C08K5/098
Inventor 宋晓辉肖华明孙超正郝垠龙付锦峰杨霄云陶四平王中林
Owner TIANJIN KINGFA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap