Black single-component polymer inorganic mineral waterproof coating for concrete base surface

A technology of inorganic mineral and waterproof coating, applied in the direction of coating, etc., can solve the problems of high cost, cumbersome and complicated construction operations, etc., and achieve the effects of maintaining stability, shortening construction time, and high adhesion

Inactive Publication Date: 2021-02-02
清远市楼固环保建材有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the waterproof coatings currently used in the market are two-component waterproofing composed of cement-containing powder and emulsion. Although they have good waterproof performance, the construction operations are cumbersome and complicated, and the cost is generally high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black single-component polymer inorganic mineral waterproof coating for concrete base surface
  • Black single-component polymer inorganic mineral waterproof coating for concrete base surface
  • Black single-component polymer inorganic mineral waterproof coating for concrete base surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of black one-component polymer inorganic mineral waterproof coating for concrete base surface, comprises the raw material of following percentage:

[0028]

Embodiment 2

[0030] A kind of black one-component polymer inorganic mineral waterproof coating for concrete base surface, comprises the raw material of following percentage:

[0031]

Embodiment 3

[0033] A kind of black one-component polymer inorganic mineral waterproof coating for concrete base surface, comprises the raw material of following percentage:

[0034]

[0035] The single-component polymer waterproof coating prepared by the present invention was inspected in the production workshop on November 7, 2018, and tested from November 14, 2018 to November 26, 2018, and finally on November 28, 2018. The data are given on a daily basis, and the specific information is shown in the table below:

[0036]

[0037] The technical effects of the present invention are mainly reflected in the following aspects: the waterproof coating is styrene-acrylic emulsion, pure acrylic emulsion, quartz ore, pigment, polyacrylic acid anionic thickener, bactericide and preservative, and the present invention processes the polymer emulsion in the coating Improvement, the waterproof emulsion is modified by adding pigments with quartz ore, polyacrylic acid anionic thickener, bactericid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a black single-component polymer inorganic mineral waterproof coating for a concrete base surface. The waterproof coating comprises a styrene-acrylic emulsion, a pure acrylic emulsion, quartz ore sand, a pigment, a polyacrylic acid anionic thickener, a bactericide and a preservative. A polymer emulsion in the coating is improved, the quartz ore sand is matched with the pigment, the polyacrylic acid anionic thickener, the bactericide and the preservative to modify the waterproof emulsion, so that the waterproof coating is modified, shows excellent tensile physical and chemical properties and shortened construction time, has the properties of water resistance, tensile resistance, high adhesion, quick construction and the like, can keep good stability, and is not likely to deteriorate.

Description

technical field [0001] The invention specifically relates to a black single-component polymer inorganic mineral waterproof coating for concrete base surfaces. Background technique [0002] Most of the waterproof coatings currently used in the market use cement-containing powder and emulsion to form two-component waterproofing. Although they have good waterproofing properties, the construction operations are cumbersome and complicated, and the cost is generally high. [0003] Aiming at the needs of the prior art, the invention discloses a novel waterproof coating, which has good mechanical detection performance and excellent construction simplicity, and is environmentally friendly, non-toxic and low in cost. Contents of the invention [0004] In view of this, the purpose of the present invention is to provide a black single-component polymer inorganic mineral waterproofing for concrete base surface that not only has the properties of water resistance, tensile strength, high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D7/61C09D7/43
CPCC08K2003/2241C08K2003/2296C08K2003/265C08L2205/02C08L2205/03C09D133/04C09D7/43C09D7/61C08L25/14C08L33/02C08K13/02C08K3/36C08K3/22C08K3/26C08K3/34C08K5/47
Inventor 刘松芝
Owner 清远市楼固环保建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap