Anti-fogging polyurethane acrylate resin and preparation method thereof

A technology of urethane acrylate and hydroxyl-terminated acrylate, which is applied in the field of anti-fogging urethane acrylate resin and its preparation, can solve problems such as practical application obstacles, time-consuming and labor-intensive, and achieve good anti-fogging performance and simple operation process. , Improve the effect of light curing efficiency

Inactive Publication Date: 2021-02-02
南京山维新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, many fabrication processes involve complex multi-step operations that are time-consuming and labor-intensive, which hinders practical applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-fogging polyurethane acrylate resin and preparation method thereof
  • Anti-fogging polyurethane acrylate resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Add 1.0mol of isophorone diisocyanate (IPDI), 0.2wt% 2,6-p-di-tert-butyl-p-cresol, 1.0mol of hydroxyethyl acrylate (HEA) and an appropriate amount of N,N-dimethyl Add methyl formamide in the dry reaction bottle, stir and react at room temperature for 30 minutes;

[0026] (2) At room temperature, add 1.0 mol of choline chloride into the reaction flask, heat up to 60°C, and stir for 30 minutes;

[0027] (3) Add an appropriate amount of dibutyltin dilaurate into the reaction flask, heat up to 80° C., stir and react until the measured -NCO value is 0.19%, to obtain quaternary ammonium chloride urethane acrylate resin.

Embodiment 2

[0029] (1) Add more than 1.0mol hexamethylene diisocyanate (HDI), 0.2wt% 2,6-p-di-tert-butyl-p-cresol, 1.0mol hydroxyethyl acrylate (HEA) and appropriate amount of N,N-dimethyl Add methyl formamide in the dry reaction bottle, stir and react at room temperature for 30 minutes;

[0030] (2) At room temperature, add 1.0 mol of choline chloride into the reaction flask, heat up to 60°C, and stir for 30 minutes;

[0031] (3) Then add an appropriate amount of dibutyltin dilaurate into the reaction flask, and raise the temperature to 80° C., stir the reaction until the measured -NCO value is 0.15%, and obtain the quaternary ammonium chloride urethane acrylate resin.

Embodiment 3

[0033] (1) Add 0.6mol hexamethylene diisocyanate (HDI), 0.2wt% 2,6-p-di-tert-butyl-p-cresol, 0.6mol polycaprolactone acrylate (CA) and appropriate amount of N,N- Dimethylacetamide was added into a dry reaction flask, and stirred and reacted at room temperature for 30 minutes;

[0034] (2) At room temperature, add 0.6mol choline chloride into the reaction flask, and heat up to 60°C, and stir for 30 minutes;

[0035] (3) Add an appropriate amount of dibutyltin dilaurate into the reaction flask, heat up to 80° C., stir and react until the measured -NCO value is 0.18%, to obtain quaternary ammonium chloride urethane acrylate resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anti-fogging polyurethane acrylate resin and a preparation method thereof. The preparation method comprises the following steps of: reacting polyisocyanate with hydroxyl-terminated acrylate, and then reacting with hydroxyl-terminated quaternary ammonium salt to obtain the anti-fogging polyurethane acrylate resin. The raw materials are cheap and easy to obtain, and the manufacturing process is simple. The polyurethane acrylate resin has the characteristics of good anti-fog performance and rapid photocuring.

Description

technical field [0001] The invention belongs to the technical field of polymer material synthesis, and in particular relates to an anti-fogging polyurethane acrylate resin and a preparation method thereof. Background technique [0002] Fogging occurs frequently on optical materials used in everyday life such as bathroom mirrors, eyeglasses, goggles, swimming goggles, windshields, camera lenses, skis, and analytical and medical instruments. To overcome this dilemma, various materials and processes have been proposed for durable anti-fog coatings. Maechler et al. disclose the preparation of multilayer transparent anti-fog coatings based on polycarbonate. Cebeci et al. disclosed that a stable superhydrophilic nanofilm was prepared by layer-by-layer assembly of silica nanoparticles and polycations. Yuan et al. disclosed the preparation of an anti-fog coating of UV-curable hydrophilic acrylate polymer, which contains a certain amount of sulfonic acid groups and has good anti-fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/75C08G18/73C08G18/78C08G18/67C08G18/28C08G18/68
CPCC08G18/755C08G18/73C08G18/7831C08G18/672C08G18/285C08G18/68
Inventor 杜鹏王贵富余立挺张弢
Owner 南京山维新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com