Automobile paint surface crystal plating coating and preparation method thereof

A technology of automotive paint and crystal plating, applied in the direction of antifouling/underwater coatings, coatings, paints containing biocide, etc., can solve the problems of poor water resistance and low corrosion resistance, and achieve improved grades, high viscosity strength, The effect of high permeability

Active Publication Date: 2021-01-05
广东优贝精细化工有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the disadvantages of poor water resistance and low corrosion resistance of existing automotive paint surface coatings, the purpose of the present invention is to provide a car paint surface coating with high penetration, high impermeability, high viscosity strength, heat and cold resistance, and oxidation resistance. Crystal coating and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automobile paint surface crystal plating coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] See attached figure 1 Shown, a kind of automobile lacquer crystal coating, comprises following mass parts: organosilicon water repellent 10%, cationic emulsified silicone oil 1%, glycerin 1%, isothiazolinone fungicide 0.01%, silicone oil emulsion 6%, tasteless Kerosene 15%, wax 4%, deionized water 62.99%.

[0017] The present embodiment also includes the preparation method of the crystal-plated paint on the automobile paint surface, comprising the following steps:

[0018] S1. Weigh silicone water repellent, cationic emulsified silicone oil, glycerin, isothiazolinone bactericide, silicone oil emulsion, odorless kerosene, wax, deionized water in parts by mass.

[0019] S2. Heat and melt the weighed wax, then add odorless kerosene and mix and stir until the wax is completely dissolved, then add cationic emulsified silicone oil and mix and stir until the stirring is transparent and uniform, and cool to room temperature to form the first solution, wherein The heating temp...

Embodiment 2

[0024] See attached figure 1 Shown, a kind of automobile lacquer crystal coating, comprises the following parts by mass: organic silicon water repellent 10%, cationic emulsified silicone oil 8%, glycerin 8%, isothiazolinone fungicide 0.5%, silicone oil emulsion 25%, tasteless Kerosene 25%, wax 15%, deionized water 8.5%.

[0025] The present embodiment also includes the preparation method of the crystal-plated paint on the automobile paint surface, comprising the following steps:

[0026] S1. Weigh silicone water repellent, cationic emulsified silicone oil, glycerin, isothiazolinone bactericide, silicone oil emulsion, odorless kerosene, wax, deionized water in parts by mass.

[0027] S2. Heat and melt the weighed wax, then add odorless kerosene and mix and stir until the wax is completely dissolved, then add cationic emulsified silicone oil and mix and stir until the stirring is transparent and uniform, and cool to room temperature to form the first solution, wherein The heat...

Embodiment 3

[0032] This embodiment is the best embodiment, see attached figure 1 Shown, a kind of crystal-plated coating on car paint surface, a kind of crystal-plated paint on car paint surface, comprise following mass parts: organosilicon water repellent 22%, cationic emulsified silicone oil 4%, glycerin 4%, isothiazolinone fungicide 0.25%, silicone oil emulsion 15%, odorless kerosene 20%, wax 10%, deionized water 24.75%.

[0033] The present embodiment also includes the preparation method of the crystal-plated paint on the automobile paint surface, comprising the following steps:

[0034] S1. Weigh silicone water repellent, cationic emulsified silicone oil, glycerin, isothiazolinone bactericide, silicone oil emulsion, odorless kerosene, wax, deionized water in parts by mass.

[0035] S2. Heat and melt the weighed wax, then add odorless kerosene and mix and stir until the wax is completely dissolved, then add cationic emulsified silicone oil and mix and stir until the stirring is trans...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an automobile paint surface crystal plating coating and a preparation method thereof. According to the invention, an organosilicon waterproofing agent is used as a main raw material, so that the crystal plating coating has high permeability, high impermeability and high viscosity strength. Meanwhile, after the coating is sprayed on the surface, a colorless, transparent, anti-ultraviolet, waterproof, anti-corrosion and anti-static breathable film can be formed to effectively protect an automobile paint surface. Meanwhile, by adding cationic emulsified silicone oil, an isothiazolinone bactericide and silicone oil emulsion, the cleaning effect of the coating is further improved, and the automobile surface can be sterilized, so that the coating disclosed by the invention is low-foam or non-foam.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a crystal coating for automobile paint surface and a preparation method thereof. Background technique [0002] Automobile paint is a kind of protective film sprayed on the car. It is a kind of paint, which makes the car body not easy to be corroded. However, the car paint is directly exposed to the atmosphere. After a period of use, the car paint will leave a lot of dust and rust. If it is not removed in time, it will directly corrode the car shell, but after cleaning the car paint surface, it will inevitably make the car paint surface impossible to restore to its original state. Therefore, it is necessary to develop a car paint surface with corrosion resistance, scratch resistance and waterproof Crystal coating. Contents of the invention [0003] Aiming at the disadvantages of poor water resistance and low corrosion resistance of existing automotive paint surface co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/14C09D7/63C09D7/65
CPCC09D183/04C09D5/14C09D7/63C09D7/65C08L2201/08C08L2201/04C08L2205/025C08L2205/03C08L2205/02C08L2201/10C08L83/04C08L91/06C08L91/00C08K5/053C08K5/47
Inventor 骆国清余月贵胡彩南王莉莉
Owner 广东优贝精细化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More