A kind of ceramic tile with copper metal texture and preparation method thereof

A technology of ceramic tiles and copper metal, applied in the field of ceramic tiles, can solve the problems of weak decoration, dull color, single metal texture, etc.

Active Publication Date: 2021-03-19
GUANGDONG OVERLAND CERAMICS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Metal texture ceramic tiles are usually coated with a layer of metal glaze or metal dry particles on the surface of the brick. After high temperature sintering, the ceramic surface produces a metallic luster. However, the metal texture ceramic tiles produced by the prior art have a single metal texture and are not decorative. Realistic, the color of ordinary metal glaze is not bright enough, especially the imitation copper ceramic tile, the color is dull, and it cannot produce the texture of simple copper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic tile with copper metal texture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Ceramic tiles with copper metal texture, including:

[0034] Take 60 g of iron phosphate, 240 g of the hybrid, 0.0g of quartz 70g, sodium stallus, 20g of burna, 40g of alumina, borite 40g, high boron, 100 g of high boron

[0035] The above materials were mixed with ball mills to obtain a glaze, and the glaze was mashed to form a topping on the body;

[0036] The glazed glaze is applied to the top of the top, and the ceramic tile with copper metal texture is obtained.

[0037] The preparation method of aluminum phosphate aluminum phosphate includes:

[0038] Toint cyanuric acid 120g, melamine 120g, aluminum phosphate 120g, montmorillonite 240 g, silane 60g, ethanol 2000g;

[0039] Add melamine, aluminum, montmorillonite, and ethanol, mixed at 50 to 70 ° C for 10 min, and stir for 6 h;

[0040] Cyanuric acid was added at 60 ° C, and the reaction was 8h;

[0041] At 60 ° C, it was extruded into a silane reaction for 1 h;

[0042] Cooling, filtration, drying, pulverizing, and s...

Embodiment 2

[0049] Ceramic tiles with copper metal texture, including:

[0050] Take 60 g of phosphate, 250g of phosphate, quartz 70g, sodium, sodium, 20g of burna, 40g of alumina, 40g of flavous talones, zinc oxide, 100 g of high boron

[0051] The above materials were mixed with ball mills to obtain a glaze, and the glaze was mashed to form a topping on the body;

[0052] The glazed glaze is applied to the top of the top, and the ceramic tile with copper metal texture is obtained. The phosphate is commercially available in commercial phosphate, Hubei Hongjing Chemical Co., Ltd. CAS: 7784-22-7.

Embodiment 3

[0054] Ceramic tiles with copper metal texture, including:

[0055] Take 60 g of iron phosphate, 240 g of the hybrid, 0.0g of quartz 70g, sodium stallus, 20g of burna, 40g of alumina, borite 40g, high boron, 100 g of high boron

[0056] The above materials were mixed with ball mills to obtain a glaze, and the glaze was mashed to form a topping on the body;

[0057] The glazed glaze is applied to the top of the top, and the ceramic tile with copper metal texture is obtained.

[0058] The preparation method of aluminum phosphate aluminum phosphate includes:

[0059] Toint cyanuric acid 120g, melamine 120g, aluminum phosphate 120g, montmorillonite 240 g, silane 60g, ethanol 2000g;

[0060] Add melamine, aluminum, montmorillonite, and ethanol, mixed at 50 to 70 ° C for 10 min, and stir for 6 h;

[0061] Cyanuric acid was added at 60 ° C, and the reaction was 8h;

[0062] At 60 ° C, it was extruded into a silane reaction for 1 h;

[0063] Cooling, filtration, drying, pulverizing, and sph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of ceramic brick production, and provides a ceramic brick with a copper metal texture and a preparation method thereof, which are used to provide a ceramic brick with a copper-like texture. The ceramic brick with copper metal texture provided by the invention comprises: 5-8 parts by mass of iron phosphate, 20-25 parts by mass of hybrid aluminum hypophosphite, 6-8 parts by mass of quartz, 40-60 parts by mass of albite, 1 to 3 parts by mass of burnt kaolin, 3 to 7 parts by mass of alumina, 2 to 5 parts by mass of burnt talc, 3 to 5 parts by mass of zinc oxide, and 8 to 12 parts by mass of high-boron frit; the above materials are mixed and ball milled to obtain The glaze is applied to the green body to form a bottom glaze; the transparent glaze is applied to the bottom glaze, and fired for 20-24 hours to obtain a ceramic tile with a copper metal texture. It can improve the metal texture, especially make the ceramic tile have a copper-like texture and color.

Description

Technical field [0001] The present invention relates to the field of ceramic tile production involves ceramic tiles with copper metal texture. Background technique [0002] Metal texture ceramic tiles typically show a metal glaze or metal dry particles in the brick, which produces metal gloss with high temperature sintering, ceramic surface, but the metal textured ceramic brick metal texture produced by the prior art is single, not decorative, not enough Realistic, ordinary metal glaze color is not bright enough, especially the copper ceramic tiles, the color is dim, and the texture of copper is not produced. Inventive content [0003] The technical problem solved by the present invention is to provide a ceramic tile having a copper texture, providing a ceramic tile having a copper metal texture. [0004] In order to solve the above technical problems, the technical solutions provided by the present invention are: [0005] Ceramic tiles with copper metal texture, including: [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C04B41/89C03C8/00C01B25/165C03C1/00
CPCC01B25/165C03C1/00C03C8/00C03C8/14C03C2204/04C04B41/52C04B41/89C04B41/5022
Inventor 麦文英汪加武叶建明王礼石献忠卢佩玉
Owner GUANGDONG OVERLAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com