Anti-oxidation lubricating oil and preparation method thereof

A lubricating oil and anti-oxidation technology, which is applied in the field of lubricating oil, can solve problems such as lubricating oil oxidation, achieve the effects of improving anti-oxidation stability, reducing the difficulty of oil film formation, and improving anti-oxidation stability

Pending Publication Date: 2020-11-24
力能石油科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that lubricating oil is easily oxidized due to mechanical friction and heating in the prior art, an anti-oxidation lubricating oil and its preparation method are proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-oxidation lubricating oil and preparation method thereof
  • Anti-oxidation lubricating oil and preparation method thereof
  • Anti-oxidation lubricating oil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A method for preparing an anti-oxidation lubricating oil, comprising the above-mentioned anti-oxidation lubricating oil, is characterized in that it also includes the following steps:

[0036] S101 configuration 4-butyl diphenylamine;

[0037] S102 configures surface-modified nano-silicon carbide particles;

[0038] S103 Mix 4-butyldiphenylamine, surface-modified nano-silicon carbide particles, molybdenum-containing compounds and base oil in parts by weight to prepare a composition, raise the temperature of the composition to 155-165°C, and stir at constant temperature under nitrogen filling conditions 2 to 4 hours to prepare anti-oxidation lubricating oil.

[0039] Further, the configuration of 4-butyldiphenylamine comprises the following steps:

[0040] S201 Weigh palladium carbene, tert-butyl potassium, aniline and p-butylbromobenzene in predetermined weight parts, and simultaneously send them to the reaction vessel for mixing to prepare a mixture;

[0041] S202 S...

specific Embodiment 1

[0050] S401 prepares 4-butyldiphenylamine, weighs 2 parts of palladium carbene, 100 parts of tert-butyl potassium, 70 parts of aniline and 150 parts of p-butylbromobenzene in predetermined weight parts and sends them to a reaction vessel for mixing to prepare a mixture;

[0051] S402 Stir the mixture in the reaction vessel for 45min under a nitrogen-filled environment;

[0052] S403 After the stirring is completed, 5 parts of 1,4-dioxane are added to the mixture, and the temperature is raised to 110° C. After stirring for 30 minutes, the reaction vessel is bathed in oil for 3 hours;

[0053] S404 After the oil bath is completed, let the reaction vessel cool to room temperature, add ethyl acetate to dissolve the reaction product in the reaction vessel, and filter with a separation column to obtain a reaction solution;

[0054] S405 Control the reaction solution at 25° C. for rotary evaporation to prepare 4-butyldiphenylamine.

[0055] S501 Prepare nano-silicon carbide particle...

specific Embodiment 2

[0060] S601 prepares 4-butyldiphenylamine, weighs 3 parts of palladium carbene, 120 parts of tert-butyl potassium, 80 parts of aniline and 160 parts of p-butylbromobenzene in predetermined weight parts and sends them to a reaction vessel for mixing to prepare a mixture;

[0061] S602 Stir the mixture in the reaction vessel for 45min under a nitrogen-filled environment;

[0062] S603 After the stirring is completed, add 10 parts of 1,4-dioxane to the mixture, and raise the temperature to 110°C, stir for 30 minutes, and put the reaction vessel in an oil bath for 3 hours;

[0063] S604 After the oil bath is completed, allow the reaction vessel to cool to room temperature, add ethyl acetate to dissolve the reaction product in the reaction vessel, and filter through a separation column to obtain a reaction solution;

[0064] S605 Control the reaction solution at 25° C. for rotary evaporation to prepare 4-butyldiphenylamine.

[0065] S701 Prepare nano-silicon carbide particles, mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses anti-oxidation lubricating oil. The anti-oxidation lubricating oil comprises the following components in parts by weight: 80-90 parts of base oil, 2-6 parts of 4-butyldiphenylamine, 0.2-1 part of surface modified nano silicon carbide particles and 2-6 parts of molybdenum-containing compound, and further discloses a preparation method of the anti-oxidation lubricating oil. The anti-oxidation lubricating oil is included. The preparation method of the antioxidant lubricating oil comprises the following steps: preparing 4-butyldiphenylamine; preparing surface modified nanosilicon carbide particles; enabling the 4-butyldiphenylamine, surface-modified nano silicon carbide particles, the molybdenum-containing compound and base oil to be matched in parts by weight to prepare a composition, wherein the composition reacts under preset conditions to prepare the antioxidant lubricating oil; and on the basis of the prior art, the surface-modified nano silicon carbide particles and the 4-butyldiphenylamine are additionally arranged in the base oil, so that the antioxidant stability of the lubricating oil is improved effectively; and the molybdenum-containing compound isadditionally arranged and is matched with the surface-modified nano silicon carbide particles, so that the antioxidant stability of the lubricating oil is improved.

Description

technical field [0001] The invention belongs to the technical field of lubricating oil, and in particular relates to an anti-oxidation lubricating oil and a preparation method thereof. Background technique [0002] Friction and wear widely exist in daily life and in nature, thus causing problems such as energy consumption and mechanical loss to become increasingly prominent. The use of lubricating oil is considered to be an important method to effectively reduce or even eliminate the problem of friction and wear. The use of lubricating oil can effectively reduce friction and wear. However, due to the heat generated by mechanical friction, lubricating oil is easily oxidized, resulting in reduced lubricating performance of lubricating oil. Contents of the invention [0003] In order to solve the problem in the prior art that lubricating oil is easily oxidized due to mechanical friction and heating, an anti-oxidation lubricating oil and a preparation method thereof are propos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M141/06C10M169/04C07C209/10C07C211/55C01B32/956B82Y40/00C10N30/10C10N30/06C10N30/02
CPCC10M141/06C10M169/045C07C209/10C01B32/956B82Y40/00C10M2215/064C10M2201/10C10M2201/14C10M2201/066C10M2203/1006C07C211/55
Inventor 颜梦曦
Owner 力能石油科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com