A kind of dty silk containing anti-ultraviolet agent and its production process

An anti-ultraviolet agent and production process technology, applied in the manufacture of rayon, conjugated synthetic polymer rayon, melt spinning, etc. Effective anti-ultraviolet ability, high mechanical properties and stability, durable effect

Active Publication Date: 2022-08-09
浙江裕源纺织有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the combination of chemical bonds between the added UV-shielding agent and the woven fabric cannot occur, and the washing fastness is poor. Therefore, after washing the fabric several times, the UV-shielding agent will be washed off, so that the fabric loses its anti-ultraviolet properties. ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of dty silk containing anti-ultraviolet agent and its production process

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0055] Mix 1.5g ashwain, 2.2g grape seed proanthocyanidin extract, 0.6g artemisia annua extract and 3.7g chitosan cinnamaldehyde Schiff base at a temperature of 45°C, and then dry at a temperature of 75°C. get anti-ultraviolet agent;

[0056] Wherein, the chitosan cinnamaldehyde Schiff base is prepared by the following method:

[0057] Disperse 3g chitosan in 50g methanol, swell at 20°C for 12h, then add 14g cinnamaldehyde and 30g absolute ethanol, ultrasonically disperse at 40°C for 10h, filter, wash, and extract for 12h , dried under vacuum at 50°C to obtain chitosan cinnamaldehyde Schiff base.

preparation example 2

[0059] After mixing 2.5g ashwain, 1.8g grape seed proanthocyanidin extract, 0.8g artemisia annua extract and 3.5g chitosan cinnamaldehyde Schiff base at a temperature of 45°C, it was dried at a temperature of 75°C. get anti-ultraviolet agent;

[0060] Wherein, the chitosan cinnamaldehyde Schiff base is prepared by the following method:

[0061] Disperse 3g chitosan in 50g methanol, swell at 20°C for 12h, then add 14g cinnamaldehyde and 30g absolute ethanol, ultrasonically disperse at 40°C for 10h, filter, wash, and extract for 12h , dried under vacuum at 50°C to obtain chitosan cinnamaldehyde Schiff base.

preparation example 3

[0063] After mixing 2g ashwain, 2g grape seed proanthocyanidin extract, 0.7g artemisia annua extract and 3.6g chitosan cinnamaldehyde Schiff base at a temperature of 47.5 °C, it was dried at a temperature of 80 °C to obtain the antibacterial agent. UV agent;

[0064] Wherein, the chitosan cinnamaldehyde Schiff base is prepared by the following method:

[0065] Disperse 3.1g chitosan in 51g methanol, swell at 22°C for 12.5h, then add 15g cinnamaldehyde and 31g absolute ethanol, disperse by ultrasonic for 10.25h at 45°C, filter, wash, Then extract for 12.5 h, and vacuum dry at 51 °C to obtain chitosan cinnamaldehyde Schiff base.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a DTY yarn containing an anti-ultraviolet agent and a production process thereof, belonging to the technical field of textiles. The production process of the DTY yarn comprises the following steps: S1: melt-blending and extruding the mixed fibers at a temperature of 260-290° C. out, to obtain the mixed pellets; S2: pre-crystallize the compound pellets at a temperature of 160-164 °C for 10-20 min, and then dry at a temperature of 160-170 °C to obtain dry mixed pellets; S3: dry the pellets The mixed pellets and the dried anti-ultraviolet agent are put into the screw extruder, melt-blended and extruded, and then put into the spinning machine, and the spinning process is carried out to obtain POY yarn; S4: POY yarn is passed through the first Roller, hot box deformation, false twister twisting, second roller, network nozzle, hot box setting, third roller, oiling, winding, to obtain DTY yarn with anti-ultraviolet agent, the DTY yarn prepared by the present invention has The effect of long-lasting UV resistance.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a DTY yarn containing an anti-ultraviolet agent and a production process thereof. Background technique [0002] DTY yarn, also known as stretch textured yarn, usually uses POY yarn as raw yarn, which is continuously or simultaneously stretched on a texturing machine, and then a finished yarn after being deformed by a twister. Textile, processed into fabrics. [0003] In recent years, with the destruction of the natural environment, the ozone layer has gradually become thinner. For every 1% decrease in the ozone layer, the radiation intensity of ultraviolet rays will increase by 2%. Excessive ultraviolet rays are irradiated on the human body, which is prone to accelerated wrinkles and skin aging. , and even burns, skin cancer and other lesions. Therefore, the research on anti-ultraviolet fabrics has gradually developed. [0004] The existing anti-ultraviolet fabrics are usuall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/14D01F8/06D01F1/10D01D5/08D02G1/00D02G1/20C08B37/08
CPCD01F8/14D01F8/06D01F1/106D01D5/08D02G1/20D02G1/205D02G1/004C08B37/003
Inventor 李威孙国林孙建锋李金战项伟明
Owner 浙江裕源纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com