A kind of energy storage type environment-friendly luminescent paint and preparation method thereof

A luminescent paint and energy storage technology, applied in the field of paint, can solve problems such as limitations, unstable chemical properties, and short luminescent time, and achieve the effects of low cost, cheap raw materials, and easy operation

Active Publication Date: 2022-02-15
ELECTRIC POWER RES INST OF GUANGDONG POWER GRID
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Early energy-storage luminescent paints used zinc sulfide luminescent materials as luminescent pigments, but their chemical properties were unstable, easy to decompose in the environment, and the luminescence time was short, so their applications were greatly limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of energy storage type environment-friendly luminescent paint and preparation method thereof
  • A kind of energy storage type environment-friendly luminescent paint and preparation method thereof
  • A kind of energy storage type environment-friendly luminescent paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] In this example, the preparation of energy-storage-type environment-friendly luminescent paint is carried out. The energy-storage-type environment-friendly luminescent paint is composed of strontium polyaluminate luminescent material activated by rare earth ions doped with titanium dioxide and boric acid coated with silicon dioxide, film-forming substances, fillers, and auxiliary materials. The chemical formula of the rare earth ion-activated strontium polyaluminate luminescent material in the rare earth ion-activated strontium polyaluminate luminescent material of silicon dioxide-doped titanium dioxide and boric acid is 7Al 2 o 3 4SrO:Eu 2+ 0.02 :Nd 3+ 0.03 . The film-forming material is polyester imide resin (MW, 30000), the filler is nano-titanium dioxide, the film-forming aid is Loxanol CA5308, the wetting agent is Dow DOW wetting agent X-405, and the dispersant is ammonium polyacrylate Salt (MW, 2000), defoamer is emulsified methyl silicone oil (MW, 6000), ant...

Embodiment 2

[0062] This embodiment is the same as embodiment 1, the only difference is that the film-forming substance is replaced by polyurethane resin (MW, 40000).

Embodiment 3

[0064] This example is the same as Example 1, except that the film-forming substance is replaced by silicone-modified acrylic resin (MW, 6000).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of coatings, and in particular relates to an energy storage type environment-friendly luminous coating and a preparation method thereof. The film-forming material of the present invention is selected from one or more of polyester-imide resins, polyurethane resins, silicone-modified acrylic resins, and epoxy resins, and cooperates with other components to make the energy-storage environmentally friendly luminous coatings non-caking, durable Good thermal and insulating properties, ensuring the initial luminous brightness and afterglow time of the rare earth ion-activated strontium polyaluminate luminescent material; the microemulsion method is used to treat the rare earth ion-activated strontium polyaluminate luminescent material doped with titanium dioxide and boric acid. The encapsulation and other components make the luminescent pigment particles in the energy storage type environmentally friendly luminescent paint have good dispersion, improve the initial luminous brightness of the rare earth ion-activated strontium polyaluminate luminescent material, and prolong the afterglow time; in the energy storage type The toughening agent used in the environmentally friendly luminous paint improves the aging resistance, weather resistance and scratch resistance of the energy-storage environmentally friendly luminous paint.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to an energy storage type environment-friendly luminous coating and a preparation method thereof. Background technique [0002] Long afterglow energy storage type environmental protection luminous paint is a kind of self-luminous functional luminous paint, which has been widely used in the fields of architectural decoration, transportation, fire safety, military facilities and aviation. Early energy-storage luminescent paints used zinc sulfide luminescent materials as luminescent pigments, but their chemical properties were unstable, easy to decompose in the environment, and the luminescent time was short, which greatly restricted their applications. At present, non-toxic and non-radioactive rare earth activated alkaline earth metal aluminate luminescent materials are mainly used as luminescent pigments. It has the advantages of high luminous brightness, long afterglow ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D179/08C09D175/04C09D133/04C09D163/00C09D5/22C09D5/25C09D5/08C09D7/63
CPCC09D179/08C09D175/04C09D143/04C09D163/00C09D5/22C09D5/18C09D5/08C09D5/00C09D7/63C08L2201/08C08L2205/025C08L2205/035C08K2003/387C08K2003/2241C08L33/02C08L83/04C08L33/08C08K13/06C08K9/10C08K3/22C08K3/38C08K3/24C08K5/523C08L63/00
Inventor 周永言李丽孙东伟唐念
Owner ELECTRIC POWER RES INST OF GUANGDONG POWER GRID
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com