Low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material and preparation method thereof

A high flame-retardant sheath and low-temperature-resistant technology, which is applied in the direction of plastic/resin/wax insulators, organic insulators, electrical components, etc., can solve the problems of low-temperature resistance, oil resistance, torsion resistance and high flame-retardant performance of cables, and achieve Increase heat aging performance, good mechanical properties and processing properties, and improve flexibility

Pending Publication Date: 2020-09-18
FAR EAST CABLE +3
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a low-temperature-resistant, oil-resistant, torsion-resistant, high-flame-retardant sheath material to solve the problems of insufficient low-temperature resistance, oil resistance, torsion resistance, and high flame-retardant performance of existing cables

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material and preparation method thereof
  • Low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material and preparation method thereof
  • Low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Weigh each component, take by weight and control the properties of each component to meet:

[0028] 60 parts of chlorinated polyethylene, the chlorine content in chlorinated polyethylene is 35%; the Mooney viscosity is 85; chlorinated polyethylene has excellent weather resistance, ozone resistance, chemical resistance and aging resistance, and has good oil resistance , Flame retardancy and coloring performance, ensuring good oil resistance and flame retardancy of the sheath;

[0029] 40 parts of chlorosulfonated polyethylene, the relative density of chlorosulfonated polyethylene is 1.19; the Mooney viscosity is 56; the chlorine content is 35%;

[0030] Chlorosulfonated polyethylene has excellent ozone resistance, atmospheric aging resistance, chemical corrosion resistance, etc., good physical and mechanical properties, aging resistance, heat resistance and low temperature resistance, oil resistance, flame resistance, wear resistance , and resistance to electrical insul...

Embodiment 2

[0050] Weigh each component, take by weight and control the properties of each component to meet:

[0051] 80 parts of chlorinated polyethylene, chlorine content in chlorinated polyethylene is 35%; Mooney viscosity is 85;

[0052] 20 parts of chlorosulfonated polyethylene. The relative density of chlorosulfonated polyethylene is 1.19; the Mooney viscosity is 56; the chlorine content is 35%;

[0053] 80 parts of talcum powder;

[0054] 30 parts of calcium carbonate;

[0055] 30 parts of magnesium hydroxide;

[0056] 5 parts of antimony trioxide, adding antimony trioxide as a flame retardant, further increasing the flame retardancy of the sheath;

[0057] 20 parts of carbon black;

[0058] 6 parts of magnesium oxide;

[0059] 5 copies of red pill;

[0060] DOS 15 copies;

[0061] 10 parts of chlorinated paraffin oil;

[0062] 1.5 parts of antioxidant;

[0063] 5 parts of TAIC cross-linking agent;

[0064] 4 parts of dicumyl peroxide.

[0065] The weighed raw material...

Embodiment 3

[0071] Weigh each component, take by weight and control the properties of each component to meet:

[0072] 70 parts of chlorinated polyethylene, chlorine content in chlorinated polyethylene is 35%; Mooney viscosity is 85;

[0073] 20 parts of chlorosulfonated polyethylene, the relative density of chlorosulfonated polyethylene is 1.19; the Mooney viscosity is 56; the chlorine content is 35%;

[0074] 10 parts of ethylene-vinyl acetate copolymer, vinyl acetate content 28%, melt index (190°C, 2.16kg) 6g / 10min, Mooney viscosity 27; ethylene-vinyl acetate copolymer can effectively reduce high crystallinity, Improve flexibility, impact resistance, filler compatibility and heat sealing performance, ensuring good mechanical properties and processing properties of the sheath;

[0075] 80 parts of talcum powder;

[0076] 40 parts of calcium carbonate;

[0077] 20 parts of magnesium hydroxide;

[0078] 5 parts of antimony trioxide;

[0079] 20 parts of carbon black;

[0080] 6 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material and a preparation method thereof. The low-temperature-resistant, oil-resistant, torsion-resistant and high-flame-retardant sheath material comprises the following components in parts by mass: 60 to 80 parts of chlorinated polyethylene, 20 to 40 parts of chlorosulfonated polyethylene, 0-10 parts of an ethylene-vinyl acetate copolymer, 60-100 parts of talcum powder, 20-40 parts of calcium carbonate, 20-40 parts of magnesium hydroxide, 0-10 parts of a flame retardant, 20parts of carbon black, 6 parts of magnesium oxide, 5 parts of red lead, 10-25 parts of a plasticizer, 10 parts of chlorinated paraffin oil, 1.5 parts of an antioxidant, 5 parts of a cross-linking agent and 4 parts of dicumyl peroxide. By adding the components and proportioning the components according to a specific ratio, the sheath material is ensured to have favorable mechanical properties and processability while prolonged in service life and enhanced in low-temperature resistance, oil resistance, torsion resistance and flame retardancy.

Description

technical field [0001] The invention relates to the technical field of cable sheaths, in particular to a low-temperature-resistant, oil-resistant, torsion-resistant, high-flame-retardant sheath material and a preparation method thereof. Background technique [0002] Existing cables, in order to adapt to different use environments, often need to meet multiple performance requirements at the same time. In addition to the high requirements for the cable's tensile, torsion resistance, fire resistance, oil resistance, low temperature resistance and other properties, it is also necessary to pay attention to fire prevention , improve flame retardant properties. The tension resistance, torsion resistance, fire resistance, oil resistance and low temperature resistance of the existing cables are not very satisfactory, and the insulating layer sheath is easy to crack; at the same time, the problem of flame retardancy has not been well solved. [0003] Therefore, there is a need for a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L23/34C08L91/06C08K13/02C08K3/34C08K3/26C08K3/22C08K5/11C08K5/3492C08L23/08C08L31/04H01B3/44C08J9/06
CPCC08L23/286H01B3/441C08J9/06C08J9/0061C08J9/0095C08J9/0066C08J9/0023C08J9/0028C08K2003/265C08K2003/2224C08L2201/02C08L2201/08C08L2203/202C08L2205/03C08L2205/035C08L2205/02C08J2203/12C08J2323/28C08J2423/34C08J2491/06C08J2423/08C08J2431/04C08J2207/06C08L23/34C08L91/06C08K13/02C08K3/34C08K3/26C08K3/22C08K5/11C08K5/34924C08K3/2279C08L23/0853C08L31/04
Inventor 邹鹏飞徐静姚玲王亮吴疆
Owner FAR EAST CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com