Hot-melt pressure-sensitive adhesive for normal-temperature waterproof roll butt-joint adhesive tape, and preparation method thereof

A technology of hot-melt pressure-sensitive adhesives and waterproof membranes, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of insufficient adhesion of non-polar materials and achieve improved thermal stability and compatibility, reduced impact, and improved pressure-sensitivity effects

Inactive Publication Date: 2020-08-28
SHANGHAI JIAHAO ADHESIVE PROD CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Pressure-sensitive adhesives and their products have developed rapidly in the past two decades, and their applications have spread throughout various fields of the national economy and have entered thousands of households. However, in the application of basic research and technology development of pressure-sensitive adhesive products, There is still a big gap between China and developed countries. Some high-performance pressure-sensitive adhesive products still rely on imports from developed countries. Pressure-sensitive adhesives that can be used in the waterproof industry are only 0.2mm to 0.4mm thick in products, so the adhesive is required It must have a strong cohesion to achieve the required bonding strength. The hot melt pressure-sensitive adhesives currently prepared have problems such as insufficient adhesion to non-polar materials and other specific applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-melt pressure-sensitive adhesive for normal-temperature waterproof roll butt-joint adhesive tape, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A hot-melt pressure-sensitive adhesive used for waterproof roll-to-fold tapes at room temperature, comprising the following components in parts by weight: 55 parts of SIS thermoplastic elastomer, 25 parts of polyisobutylene, 7 parts of hydrogenated monomer resin, tackifying resin complex 12 parts of compound, 1.5 parts of antioxidant and 1 part of ultraviolet absorber, wherein, in the SIS thermoplastic elastomer, the content of polystyrene is 15 wt%, and the content of polystyrene-polyisoprene diblock is 0 wt%. ~33wt%; the weight average molecular weight of the polyisobutylene is less than 2000, and the pour point is 3°C to -30°C; the tackifying resin compound is a compound of hydrogenated C9 petroleum resin and hydrogenated C5 petroleum resin, The mass ratio of the two is 1:1; the antioxidant is antioxidant 1010; and the ultraviolet absorber is UV-328.

[0022] The preparation method of the above-mentioned hot-melt pressure-sensitive adhesive is specifically as follows...

Embodiment 2

[0025] A hot-melt pressure-sensitive adhesive used for waterproof roll-to-fold tapes at room temperature, comprising the following components in parts by weight: 50 parts of SIS thermoplastic elastomer, 20 parts of polyisobutylene, 5 parts of hydrogenated monomer resin, and tackifying resin complex 10 parts of compound, 1 part of antioxidant and 0.5 part of ultraviolet absorber, wherein, in the SIS thermoplastic elastomer, the content of polystyrene is 15 wt%, and the content of polystyrene-polyisoprene diblock is 0 wt%. ~33wt%; the weight average molecular weight of the polyisobutylene is less than 2000, and the pour point is 3°C to -30°C; the tackifying resin compound is a compound of hydrogenated C9 petroleum resin and hydrogenated C5 petroleum resin, The mass ratio of the two is 2:1; the antioxidant is antioxidant 168; and the ultraviolet absorber is UV-P.

[0026] The preparation method of the above-mentioned hot-melt pressure-sensitive adhesive is specifically as follows...

Embodiment 3

[0029] A hot-melt pressure-sensitive adhesive for waterproof roll-to-fold adhesive tapes at room temperature, comprising the following components in parts by weight: 60 parts of SIS thermoplastic elastomer, 30 parts of polyisobutylene, 10 parts of hydrogenated monomer resin, tackifying resin complex 15 parts of compound, 2 parts of antioxidant and 1.5 parts of ultraviolet absorber, wherein, in the SIS thermoplastic elastomer, the content of polystyrene is 15 wt%, and the content of polystyrene-polyisoprene diblock is 0 wt%. ~33wt%; the weight average molecular weight of the polyisobutylene is less than 2000, and the pour point is 3°C to -30°C; the tackifying resin compound is a compound of hydrogenated C9 petroleum resin and hydrogenated C5 petroleum resin, The mass ratio of the two is 1.5:1; the antioxidant is antioxidant 1010 and antioxidant 168 (mass ratio 1:1); the ultraviolet absorber is UV-328 and UV-P (mass than 1:1).

[0030] The preparation method of the above-mentio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Pour pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to a hot-melt pressure-sensitive adhesive for a normal-temperature waterproof roll butt-joint adhesive tape, and a preparation method thereof. The hot-melt pressure-sensitive adhesive is prepared from, by weight, 50 to 60 parts of SIS thermoplastic elastomer, 20 to 30 parts of polyisobutene, 5 to 10 parts of hydrogenated monomer resin, 10 to 15 parts of a tackifying resin compound, 1 to 2 parts of an antioxidant and 0.5 to 1.5 parts of an ultraviolet absorbent. Compared with like products in the prior art, the hot-melt pressure-sensitive adhesive has the characteristics of high peel strength, favorable water resistance, favorable ultraviolet resistance and the like, and can well satisfy the requirements of waterproof rolls.

Description

technical field [0001] The invention belongs to the technical field of hot-melt pressure-sensitive adhesives, and relates to a hot-melt pressure-sensitive adhesive used for normal-temperature waterproof coiled adhesive tapes and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesives and their products have developed rapidly in the past two decades, and their applications have spread throughout various fields of the national economy and have entered thousands of households. However, in the application of basic research and technology development of pressure-sensitive adhesive products, There is still a big gap between China and developed countries. Some high-performance pressure-sensitive adhesive products still rely on imports from developed countries. Pressure-sensitive adhesives that can be used in the waterproof industry are only 0.2mm to 0.4mm thick in products, so the adhesive is required It must have strong cohesion to achieve the requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J153/02C09J123/20C09J11/06C09J11/08
CPCC08L2201/08C08L2205/025C08L2205/035C09J11/06C09J11/08C09J153/02C08L23/22C08L57/02C08K5/1345C08K5/3475C08K5/526
Inventor 陈宏绥史博特涂先兵
Owner SHANGHAI JIAHAO ADHESIVE PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap