Preparation method of antibacterial inorganic high-performance mineral artificial stone plate

An artificial stone slab, high-performance technology, applied in the field of artificial stone, can solve the problems of low density of modified diatomite, affecting the fluidity of mortar, easy to bulge deformation and cracking, etc., and achieve low water absorption, good self-cleaning performance and durability good performance

Pending Publication Date: 2020-08-11
黄贺明
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polymer artificial stone mainly has the disadvantages of large heat deformation, easy deformation and cracking, aging deformation, discoloration, strength reduction due to ultraviolet radiation and temperature, unpleasant gas when burning, and non-degradable.
The Chinese patent with application number 201710760996.X discloses an antibacterial and environmentally friendly mortar prepared from cement, modified oyster shell powder, quartz sand, cellulose ether, calcium carbonate, gypsum, modified diatomite and water. The compressive strength Reaching 3.1-5.0 MPa, poor mechanical properties, modified diatomite has strong water adsorption, which affects the fluidity of mortar, and the modified diatomite has a low density and is not easy to disperse evenly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of antibacterial inorganic high-performance mineral artificial stone plate
  • Preparation method of antibacterial inorganic high-performance mineral artificial stone plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] An antibacterial inorganic high-performance mineral artificial stone slab, comprising the following raw materials in parts by weight:

[0054] 60 parts of cement whose strength is not less than 32.5MPa;

[0055] 50 parts of admixtures with an average particle size of 5-30 μm;

[0056] 80 parts of fine aggregate with an average particle size of 0.15-4.75 mm;

[0057] 0.2 parts of loaded antibacterial agent with an average particle diameter of 20-100 nm;

[0058] 0.5 parts of water repellent;

[0059] 3 parts of pigment;

[0060] 3 parts of high-performance admixture;

[0061] The ratio of water to glue is 0.16.

[0062]The loaded antibacterial agent is composed of a carrier and an antibacterial agent in a mass ratio of 1:0.5 to 1.2, the carrier is porous nano calcium carbonate with an average particle diameter of 20 to 100nm, and the antibacterial agent is nano silver oxide, silver chloride, silver nitrate, One or more combinations of copper phthalocyanine; the fin...

Embodiment 2

[0073] Except that the formula of antibacterial inorganic high-performance mineral artificial stone board is different, other conditions are the same as embodiment 1.

[0074] The antibacterial inorganic high-performance mineral artificial stone board includes the following raw materials in parts by weight:

[0075] 100 parts of cement whose strength is not less than 32.5MPa;

[0076] 80 parts of admixtures with an average particle size of 5-30 μm;

[0077] 130 parts of fine aggregate with an average particle size of 0.15-4.75mm;

[0078] 0.8 parts of loaded antibacterial agent with an average particle diameter of 20-100nm;

[0079] 2 parts of water repellent;

[0080] 10 parts of pigment;

[0081] 5 parts of high-performance admixture;

[0082] The ratio of water to glue is 0.2.

Embodiment 3

[0084] Except that the formula of antibacterial inorganic high-performance mineral artificial stone board is different, other conditions are the same as embodiment 1.

[0085] The antibacterial inorganic high-performance mineral artificial stone board includes the following raw materials in parts by weight:

[0086] 70 parts of cement whose strength is not less than 32.5MPa;

[0087] 60 parts of admixtures with an average particle size of 5-30 μm;

[0088] 95 parts of fine aggregate with an average particle size of 0.15-4.75 mm;

[0089] 0.35 parts of loaded antibacterial agent with an average particle diameter of 20-100 nm;

[0090] 0.9 parts of water repellent;

[0091] 5 parts of pigment;

[0092] 3.5 parts of high-performance admixture;

[0093] The ratio of water to glue is 0.17.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an antibacterial inorganic high-performance mineral artificial stone plate. The antibacterial inorganic high-performance mineral artificial stone platecomprises the following raw materials in parts by weight: 60-100 parts of cement with the strength not lower than 32.5 MPa; 50-80 parts of an admixture with an average particle size of 5-30 [mu] m; 80to 130 parts of fine aggregate with an average particle size of 0.15 to 4.75 mm; 0.2-0.8 part of a supported antibacterial agent with an average particle size of 20-100 nm; 0.5-2 parts of a water repellent; 3 to 10 parts of pigment; 3-5 parts of a high-performance additive, wherein the water-binder ratio is 0.16 to 0.2. The artificial stone plate is good in volume stability, good in antibacterialperformance, low in shrinkage, free of buckling deformation in use, extremely low in water absorption rate, good in durability, free of aging and other problems, good in surface stain resistance, lowin overall comprehensive cost and suitable for application and popularization.

Description

technical field [0001] The invention relates to the technical field of artificial stone, in particular to a method for preparing an antibacterial inorganic high-performance mineral artificial stone slab. Background technique [0002] With the upgrading of material manufacturing technology and equipment, people's aesthetics and quality requirements, artificial stone panels have high strength, high flame resistance, high weather resistance, high acid and alkali resistance, wide color options, realistic imitation stone effects, and good decorative effects. , Suitable for factory production, convenient construction and other advantages, making it a material for interior and exterior wall decoration, countertops, and desktops of various high-end buildings today. [0003] Microorganisms attach to the surface of artificial stone slabs through dust, sewage or carrier coughs and sneezes and other channels. Since the surface of artificial stone does not have antibacterial properties, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B22/06C04B22/12C04B22/08C04B24/12C04B103/67C04B14/28C04B111/20C04B111/27
CPCC04B28/00C04B40/0039C04B2103/67C04B2111/2092C04B2111/27C04B2201/50C04B2201/52C04B14/06C04B14/068C04B2103/54C04B24/42C04B14/28C04B20/008C04B22/06C04B22/12C04B22/085C04B24/40
Inventor 刘福财肖敏郑增勇黎浩黄贺明霍荣斌
Owner 黄贺明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap