Adjustable laser-induced graphene paper heater and application thereof

A graphene paper, laser-induced technology, applied in the application, heating method, heating element material, etc., can solve the problems of low temperature and limited use, and achieve the effect of uniform heat distribution, light weight and strong stretching ability

Active Publication Date: 2020-07-17
北京烯塔科技有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the temperature that metal nanowire heaters can reach is low (the maximum temperature is about 200°C), and their applications are limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adjustable laser-induced graphene paper heater and application thereof
  • Adjustable laser-induced graphene paper heater and application thereof
  • Adjustable laser-induced graphene paper heater and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Prepare a graphene paper heater and heat it with electricity:

[0069] (1) Polyimide paper base: Spread the cut polyimide paper evenly and fix it on the laser scanning table.

[0070] (2) Single-sided laser-induced restoration: Scan the polyimide paper on one side with a laser power of 8.75-18.125W, a scanning speed of 0.889m / s and a printing resolution of 500, and take it out from under the laser after completion , to obtain graphene paper.

[0071] (3) Electrode paste: paste copper foil tape on both ends of the graphene paper.

[0072] (4) Apply conductive silver paint: smear conductive silver paint at the seam of copper foil tape and graphene paper, and obtain graphene paper heater after drying under room temperature.

[0073] (5) Heating with electricity: First pad the two ends of the graphene paper heater to make it suspended in the air to avoid the influence of heat conduction on the experimental results. Connect the two wires of the DC power supply to the two el...

Embodiment 2

[0093] Fabrication of patterned graphene paper heaters:

[0094] (1) Polyimide paper base: Spread the cut polyimide paper evenly and fix it on the laser scanning table.

[0095] (2) Single-sided laser-induced reduction: The laser is scanned on one side of the polyimide paper with a power of 15W, a scanning speed of 0.889m / s and a printing resolution of 500. After completion, it is taken out from the laser to obtain patterned graphite. Graphite paper, patterned with the letters "BUAA" and swirls.

[0096] (3) Electrode paste: paste copper foil tape on both ends of the patterned graphene paper, wherein, for the patterned graphene paper with the letter "BUAA", specifically at the beginning and last letter of the first letter Copper foil tapes are pasted on the tail ends of the spiral lines respectively; for the patterned graphene paper with the pattern of spiral lines, copper foil tapes are respectively pasted on the head and tail ends of the spiral lines.

[0097] (4) Wire con...

Embodiment 3

[0102] Preparation of large-area graphene paper heaters:

[0103] (1) Polyimide paper base: Spread the cut polyimide paper evenly and fix it on the laser scanning table.

[0104] (2) Single-sided laser-induced reduction: Scan the polyimide paper on one side with a laser at a power of 15W, a scanning speed of 0.889m / s and a printing resolution of 500. After completion, take it out from the laser to obtain a size of 20cm *20cm square large area graphene paper.

[0105] (3) Electrode paste: paste copper foil tape on both ends of the large-area graphene paper.

[0106] (4) Apply conductive silver paint: smear conductive silver paint at the seam of copper foil tape and large-area graphene paper to obtain a large-area graphene paper heater.

[0107] (5) Heating with electricity: First pad the two ends of the graphene paper heater to make it suspended in the air to avoid the influence of heat conduction on the experimental results. Connect the positive and negative electrodes of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a laser-induced graphene paper heater and application thereof, and belongs to the technical field of heaters. The laser-induced graphene paper heater comprises a graphene paper,electrodes are pasted to the two ends of the graphene paper respectively, the joints of the electrodes and the graphene paper are coated with conductive silver paint, and the graphene paper is prepared by the laser-induced reduction of a polyimide paper. The graphene paper heater is larger in heating temperature range, high in heating efficiency and high in temperature rising speed. Furthermore,the patterned graphene paper is obtained by one-time processing through the laser digital customized design and manufacturing, so that the patterned graphene paper heater is convenient to further prepare; and the temperature region regulation and control can be realized by changing an equivalent circuit connection mode and a region area mode, so that the graphene paper heater can be applied to theaspects of wearable equipment, household heating, industrial heating equipment, thermosetting composite material low-energy-consumption curing molding and the like, and is wide in application prospect.

Description

technical field [0001] The invention relates to the technical field of heaters, in particular to an adjustable laser-induced graphene paper heater and its application. Background technique [0002] Joule heat is the heat generated when current passes through a conductor. Electrothermal materials using Joule heat have been widely used in life and production, such as: electric heating, hyperthermia, deicing, curing thermosetting composite materials, etc. Indium tin oxide heaters are widely used in commercial products due to their high conductivity and transparency, but the brittleness of indium tin oxide prevents them from being used in flexible heaters. Metal nanowires also have high conductivity, transparency, and good flexibility, so they have become an alternative to indium tin oxide. However, the temperature that metal nanowire heaters can reach is relatively low (the highest temperature is about 200°C), and their applications are limited. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/14B29C35/02F24D13/02A41D13/005A61N5/06
CPCH05B3/14B29C35/02F24D13/024A41D13/0051A61N5/0625F24D2200/08A61N2005/0645A61N2005/0659A61N2005/0664
Inventor 罗斯达陈俊宇
Owner 北京烯塔科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com