A kind of lightweight ultra-high-strength concrete and its preparation method

An ultra-high-strength concrete and lightweight technology, applied in the field of concrete, can solve the problems of low strength of pottery sand and floating beads, reduction of cement stone thickness, and overall strength reduction, so as to ensure volume stability and strength development, reduce bulk density, The effect of improving the overall strength

Active Publication Date: 2021-08-24
CHINA STATE CONSTR READY MIXED CONCRETE CO LTD +1
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the wide application of lightweight high-strength concrete, lightweight ultra-high-strength concrete has gradually received attention and research. Patent CN107935505B proposes that lightweight ultra-high-strength concrete is prepared by using fly ash floating beads and pottery sand, and its bulk density is greater than 1980kg / m 3 , the compressive strength is between 105-111MPa, because the strength of pottery sand and floating beads is generally not high, and pottery sand is still a brittle material, when it is necessary to prepare ultra-high-strength concrete with lower bulk density and higher strength, the two are mixed The amount will increase, the thickness of the cement stone around the floating beads and pottery sand will decrease, and the overall strength will decrease, so it is difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The invention provides a lightweight ultra-high-strength concrete and a preparation method thereof.

[0043] A lightweight ultra-high-strength concrete, in parts by weight, including the following raw materials:

[0044] General portland cement, 630 parts;

[0045] Superfine fly ash, 280 parts;

[0046] Silica fume, 180 parts;

[0047] Emery powder, 110 parts;

[0048] Floating beads, 200 copies;

[0049] Peek plastic pellets, 150 servings;

[0050] Organic polymer water-absorbing resin, 18 parts;

[0051] High-performance polycarboxylate superplasticizer, 20 parts;

[0052] Water-binder ratio, 0.15.

[0053] in:

[0054] Portland cement is ordinary Portland cement with a strength of 52.5MPa.

[0055] Ultrafine fly ash with an average particle size of 2.8 μm.

[0056] The specific surface area of ​​silica fume is 22000m 2 / kg, SiO 2The content is 86%.

[0057] The fineness of emery powder is 1000 mesh, and the apparent density is 3.8g / cm 3 .

[0058] Floa...

Embodiment 2

[0068] The invention provides a lightweight ultra-high-strength concrete and a preparation method thereof.

[0069] A lightweight ultra-high-strength concrete, in parts by weight, including the following raw materials:

[0070] General portland cement, 640 parts;

[0071] Superfine fly ash, 280 parts;

[0072] Silica fume, 180 parts;

[0073] Emery powder, 120 parts;

[0074] Floating beads, 150 parts;

[0075] Peek plastic pellets, 150 servings;

[0076] Organic polymer water-absorbing resin, 20 parts;

[0077] High-performance polycarboxylate superplasticizer, 25 parts;

[0078] Water-binder ratio, 0.13.

[0079] in:

[0080] Portland cement is ordinary Portland cement with a strength of 52.5 MPa.

[0081] Ultrafine fly ash with an average particle size of 2.8 μm.

[0082] The specific surface area of ​​silica fume is 23000m 2 / kg, SiO 2 The content is 90%.

[0083] The fineness of emery powder is 1500 mesh, and the apparent density is 3.8g / cm 3 .

[0084] Flo...

Embodiment 3

[0094] The invention provides a lightweight ultra-high-strength concrete and a preparation method thereof.

[0095] A lightweight ultra-high-strength concrete, in parts by weight, including the following raw materials:

[0096] General portland cement, 650 parts;

[0097] Superfine fly ash, 300 parts;

[0098] Silica fume, 200 parts;

[0099] Emery powder, 120 parts;

[0100] Floating beads, 100 parts;

[0101] Peek plastic pellets, 150 servings;

[0102] Organic polymer water-absorbing resin, 22 parts;

[0103] High-performance polycarboxylate superplasticizer, 28 parts;

[0104] Water-binder ratio, 0.13.

[0105] in:

[0106] Portland cement is ordinary Portland cement with a strength of 52.5MPa.

[0107] Ultrafine fly ash with an average particle size of 2.8 μm.

[0108] The specific surface area of ​​silica fume is 23500m 2 / kg, SiO 2 The content is 92%.

[0109] The fineness of emery powder is 2000 mesh, and the apparent density is 3.8g / cm 3 .

[0110] Floa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lightweight super-high-strength concrete and a preparation method thereof. The lightweight super-high-strength concrete comprises the following components in parts by weight: 630-650 parts of cement, 280-300 parts of ultrafine fly ash, 180-300 parts of 200 parts of silica fume, 100-120 parts of emery powder, 100-200 parts of floating beads, 150-200 parts of Peek plastic particles, 18-23 parts of organic polymer water-absorbing resin, 20-30 parts of polycarboxylate superplasticizer, 0.13- The water-to-binder ratio is 0.15, and the floating beads are divided into two particle size grades: 40‑100 mesh and 20‑40 mesh. The obtained lightweight ultra-high-strength concrete fully optimizes and improves the internal structure by the powder and aggregates mixed therein, greatly reduces the bulk density, improves the overall strength, has excellent performance, is simple to prepare, and is suitable for popularization.

Description

technical field [0001] The invention belongs to the field of concrete, and in particular relates to a lightweight super-high-strength concrete and a preparation method thereof. Background technique [0002] Ordinary concrete is widely used due to its abundant raw materials, high compressive strength, economy and durability. of the generation. Lightweight high-strength concrete has light weight and good seismic performance, and is widely used in high-rise buildings. [0003] With the wide application of lightweight high-strength concrete, lightweight ultra-high-strength concrete has gradually received attention and research. Patent CN107935505B proposes that lightweight ultra-high-strength concrete is prepared by using fly ash floating beads and pottery sand, and its bulk density is greater than 1980kg / m 3 , the compressive strength is between 105-111MPa, because the strength of pottery sand and floating beads is generally not high, and pottery sand is still a brittle mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/40
CPCC04B28/04C04B2111/40C04B2201/20C04B2201/52C04B18/08C04B18/146C04B14/324C04B18/082C04B2103/0051C04B2103/302C04B16/04
Inventor 黄暑年王军赵日煦张恒春黄汉洋刘凯谯理格
Owner CHINA STATE CONSTR READY MIXED CONCRETE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com