FFC glaze with high stain resistance, FFC sanitary ceramic and preparation method of FFC sanitary ceramic

A technology of sanitary ceramics and ability, applied in the field of sanitary ceramics, can solve the problems of increasing cleaning difficulty, affecting human health, and easy breeding of bacteria, etc., to improve the bonding of blank glaze, increase the range of firing temperature, and reduce the possibility of defects Effect

Active Publication Date: 2020-06-09
江门市东鹏智能家居有限公司
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the pollutants are organic matter, and the pollutants accumulate behind the tiny cracks of sanitary ware, which is easy to breed bacteria, which not only affects the appearance, but also increases the difficulty of cleaning
Moreover, the detergent used in cleaning may cause environmental pollution, and the ingredients in the detergent may affect human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • FFC glaze with high stain resistance, FFC sanitary ceramic and preparation method of FFC sanitary ceramic
  • FFC glaze with high stain resistance, FFC sanitary ceramic and preparation method of FFC sanitary ceramic
  • FFC glaze with high stain resistance, FFC sanitary ceramic and preparation method of FFC sanitary ceramic

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The present invention also provides a method for preparing the FFC sanitary ceramics of the above-mentioned high antifouling ability FFC glaze, comprising the following steps:

[0046] Pre-milling of frit: Weigh the frit according to the ratio, and pre-mill the frit with the formula amount;

[0047] Ball milling: Weigh other raw materials except the frit according to the ratio, mix the other raw materials in the formula amount with the ball-milled frit obtained in the frit pre-milling step, and then add water to ball mill to obtain the glaze slurry. Among them, the addition of water The amount is 40-45% of the total weight of raw materials;

[0048] Sieving and removing iron: the glaze slurry obtained by the ball mill is sieved with 160-200 mesh and iron is removed;

[0049] Glazing: glaze the body of sanitary ceramics, the thickness of the glaze layer is 0.8-1.2mm;

[0050] Drying: The glazed sanitary ceramics are first dried in a drying room at 50°C, and then transf...

Embodiment 4

[0069] In Example 4, the amount of water added is 45% of the total amount of raw materials, the thickness of the glaze layer after 180-mesh sieving and de-iron glazing is 0.8mm, and the firing temperature is 1205°C.

Embodiment 5

[0070] In Example 5, the amount of water added is 42% of the total amount of raw materials, the thickness of the glaze layer after 160-mesh sieving and de-iron glazing is 1.2mm, and the firing temperature is 1220°C.

[0071]

[0072] Wherein, the frit includes the following components in parts by weight: 66%SiO 2 , 4%Al 2 o 3 , 8%CaO, 12%Na 2 O, 1.0%MgO, 7.8%B 2 o 3 . The content of potassium oxide in the potassium feldspar is 10%; the content of sodium oxide in the albite feldspar is 7%; the content of magnesium oxide in the calcined talc is 30%.

[0073] The sanitary ceramic plates were prepared by using the high anti-fouling ability FFC glazes with different raw material formulations in the above Table 1 and the above preparation method, and the sanitary ceramic plates and the sanitary ceramic samples of the prior art were subjected to the dirt absorption test and gloss test.

[0074] The test method of the stain absorption test is: apply red ink or blue ink on a 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glossaaaaaaaaaa
Login to view more

Abstract

The invention discloses an FFC glaze with high stain resistance, an FFC sanitary ceramic and a preparation method of the FFC sanitary ceramic. The FFC glaze with high stain resistance comprises the following raw materials in parts by weight: 22-29 parts of quartz, 24-28 parts of potassium feldspar, 6-10 parts of wollastonite, 7-8 parts of zirconium silicate, 5-10 parts of kaolin, 0-5 parts of calcite, 5-7 parts of zinc oxide, 5-7 parts of aluminum oxide, 2-3 parts of frit, 4-8 parts of dolomite, 5-8 parts of calcined talc, 1-4 parts of barium carbonate and 0.2-0.5 part of sodium carboxymethylcellulose. According to the FFC glaze with high stain resistance, multi-alkali effect is utilized, barium carbonate is introduced, the use amount of calcined talc is increased, and the use amount of albite is reduced, so venting of a green body is more smooth, the porosity of a glaze surface is reduced, and microcracks of the glaze surface are reduced. Besides, the FFC glaze with high stain resistance also utilizes the principle of like dissolves like to increase the consumption of aluminum oxide and quartz, improve the bonding property of the blank and a glaze, and further reduce the microcracks on the glaze surface of the sanitary ceramic correspondingly.

Description

technical field [0001] The invention relates to the technical field of sanitary ceramics, in particular to an FFC glaze with high antifouling ability, FFC sanitary ceramics and a preparation method thereof. Background technique [0002] In the prior art, in order to improve the overall regularity of sanitary ceramics, ensure the original intention of the designer to the greatest extent, and improve the firing pass rate, FFC mud is generally used to make the body of sanitary ceramics. FFC is the abbreviation of Fine Fire Clay, which is a material used to prepare ceramics. FFC slurry can be used to prepare sanitary ceramic body by high-pressure grouting. The sanitary ceramic body prepared by FFC slurry is easy to dry and crack during drying, or easy to deform during firing, and most of the existing ceramic glazes contain such as high Sodium stone powder, potassium sodium feldspar and other low-temperature materials have low high-temperature resistance, which makes the body pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/02C03C8/20C04B41/86
CPCC03C8/02C03C8/20C04B41/5022C04B41/86
Inventor 王赞白静静薛福勤钟保民潘欢欢陈勇伍军玲罗宁
Owner 江门市东鹏智能家居有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap