Water-based acrylic acid energy-storage luminescent coating and preparation method thereof

A water-based acrylic, energy storage and luminous technology, applied in the field of coatings, can solve the problems of poor construction performance and high consistency, and achieve the effects of low VOC content, high luminous brightness and high luminous intensity

Active Publication Date: 2020-06-05
深圳安盾海洋新材料有限公司
View PDF19 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the technical problem to be solved by the present invention is to overcome the long-lasting luminescent europium-activated alkaline earth aluminate luminescent powder in the prior art that causes the prepared coating to have too high a consistency after being stored for a period of time due to hydrolysis. , poor construction performance, providing a water-based acrylic energy-storage luminous coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based acrylic acid energy-storage luminescent coating and preparation method thereof
  • Water-based acrylic acid energy-storage luminescent coating and preparation method thereof
  • Water-based acrylic acid energy-storage luminescent coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0077] The preparation method of water-based acrylic acid energy storage luminous paint, comprises the following steps:

[0078] Mix water, dispersant, wetting agent and luminescent powder pretreatment agent, stir evenly, add rare earth doped aluminate type long-lasting luminous powder and disperse at high speed, grind to obtain color paste; then add thickener to the color paste agent, stirred evenly and then filtered to obtain the finished product.

[0079] Wherein, grinding is carried out using a grinder.

[0080] The construction technology and detection method of the water-based luminous paint involved in the present invention are as follows:

[0081] The luminous paint can be applied by brushing or spraying, stir well before use, and adjust the viscosity with water. Only when the paint film thickness reaches more than 100μm and the film thickness is relatively uniform can a paint film with higher brightness be formed, for this reason, it generally needs to be sprayed 2-...

Embodiment 1-5

[0085] Examples 1-5 relate to a water-based acrylic energy-storing luminous paint, and the specific formula of the paint is shown in Table 1.

[0086] Table 1. The formulations of the luminous coatings of each embodiment

[0087]

[0088] Among them, the specific formulations of the luminescent powder pretreatment agents E1-E3 in Table 1 are shown in Table 2, and the specific formulations of the acrylic emulsion E4-E6 are shown in Table 3.

[0089] Table 2. Formulas of luminescent powder pretreatment agents in each embodiment

[0090]

[0091] Table 3. Acrylic emulsion formula of each embodiment

[0092]

[0093] Waterborne acrylic paints are formulated as follows:

[0094] S1. Preparation of luminescent powder pretreatment: ①Add propylene glycol methyl ether and dipropylene glycol methyl ether into a reaction vessel equipped with a stirrer, thermometer, condenser, and dropping tank, start stirring, add epoxy resin, and heat to 80- 90°C, keep stirring until the epo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of coatings, in particular to a water-based acrylic acid energy-storage luminescent coating and a preparation method thereof. The water-based acrylic energy-storageluminescent coating comprises the following components, by weight, 20 to 30 parts of water, 0.1 to 0.3 part of dispersing agent, 0.1 to 0.3 part of a wetting agent, 0.01 to 0.1 part of an antifoamingagent, 10 to 30 parts of rare earth doped aluminate type long-acting luminescent powder, 5 to 10 parts of a luminescent powder pretreatment agent, 30 to 50 parts of an acrylic emulsion, 0 to 20 partsof a filling material, 0.2 to 0.5 part of a thickening agent A and 0.2 to 0.5 part of a thickening agent B. According to the invention, the water-based acrylic acid energy-storage luminescent coatingis prepared by limiting the compatibility of the water-based acrylic energy-storage luminescent coating, so that the hydrolysis stability of luminescent powder is improved, and the obtained water-based acrylic energy-storage luminescent coating is low in VOC content, non-flammable, safe and convenient to construct, high in paint film adhesion, good in weather resistance and high in luminescent intensity, and the afterglow time reaches 12 h or longer.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a water-based acrylic energy storage luminous coating and a preparation method thereof. Background technique [0002] Traditional luminescent coatings are mostly formulated with ZnS:Cu luminescent powder as the luminescent material. The afterglow of this luminescent material can only reach 1-2h, and it is easy to deteriorate and lose effect after being irradiated by ultraviolet rays or contacting oxygen. Existing paints sometimes have deuterium and Pm added to extend the afterglow 147 And other radioactive elements, but radioactive elements are harmful to the human body, so this kind of luminescent paint has been gradually eliminated by the market. [0003] In recent years, rare earth metal doped alkaline earth metal aluminates (such as SrMgAl 2 o 4 Eu +2 Dy 3+ ) type luminescent material, the afterglow time can reach more than 12h, and it has good heat resistance and anti-oxidation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/08C09D5/22
CPCC09D5/22C09D133/08C08K9/10C08K3/24
Inventor 杨春晖陈庆侯佩民
Owner 深圳安盾海洋新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com