A kind of anti-biofouling triboelectric power generation coating material and its preparation method and application

A technology for triboelectric power generation and coating materials, which is used in antifouling/underwater coatings, coatings, and paints containing biocides to improve triboelectric performance and antifouling performance, reduce biological adhesion, and inhibit biological attached effect

Active Publication Date: 2021-04-27
LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, none of the above methods integrate the collection of friction energy and antifouling properties into one coating, so that energy harvesting and antifouling properties can work at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The present invention provides a method for preparing an anti-biofouling triboelectric power generation coating material described in the above technical solution, comprising the following steps:

[0038] The acrylic resin, modified nanoparticles, polytetrafluoroethylene, fluorinated filler, diluent and film-forming aid are first mixed to obtain a mixed material;

[0039] The mixed material is mixed with the curing agent for the second time to obtain the anti-biofouling triboelectric power generation coating material.

[0040] In the invention, the acrylic resin, modified nanoparticles, polytetrafluoroethylene, fluorinated filler, diluent and film-forming auxiliary agent are first mixed to obtain a mixed material. In the present invention, the first mixing is preferably carried out under stirring conditions. During the first mixing process, the stirring rate is preferably 50-1000 rpm, more preferably 100-800 rpm, further preferably 200-500 rpm, and the stirring time is ...

Embodiment 1

[0045] Stir 10g of nano-silica and 100mL perfluorodecyltriethoxysilane solution (the solvent is n-hexane, the concentration of the solution is 0.5%) for 12h (300rpm), and the resulting mixture is filtered and dried (80°C) , to obtain perfluorodecyltriethoxysilane modified nano-silica.

[0046] With 40 parts of acrylic resin, 18 parts of toluene, 6 parts of perfluorodecyltriethoxysilane modified nano-silica (100nm), 7 parts of polytetrafluoroethylene, 18 parts of fluorinated graphite and 1 part of film-forming assistant The agent BYKA501 was added into the disperser for the first mixing, the stirring speed was 300rpm, and the stirring time was 24h to obtain the mixed material. Add 16 parts of curing agent N3300 to the mixed material, perform the second mixing, the stirring speed is 300 rpm, and the stirring time is 10 min, to obtain the anti-biofouling triboelectric power generation coating material.

[0047] The anti-biofouling triboelectric power generation coating material ...

Embodiment 2

[0050] 20g of nano-titanium dioxide and 100mL perfluorooctyltriethoxysilane solution (solvent is cyclohexane, the concentration of the solution is 2%) were stirred for 48h (200rpm), and the resulting mixture was filtered and dried (100°C) in sequence, Nano titanium dioxide modified by perfluorooctyltriethoxysilane was obtained.

[0051] 34 parts of acrylic resin, 18 parts of xylene, 6 parts of nano-titanium dioxide (100nm) modified by perfluorooctyltriethoxysilane, 9 parts of polytetrafluoroethylene, 10 parts of fluorinated paraffin and 2 parts of BYKA555 film-forming assistant Add the agent into the disperser, perform the first mixing, the stirring rate is 500rpm, and the stirring time is 12h to obtain the mixed material. Add 21 parts of HT100 curing agent to the mixed material for the second mixing, the stirring speed is 500rpm, and the stirring time is 30min, to obtain the anti-biofouling triboelectric power generation coating material.

[0052] The anti-biofouling triboel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides an anti-biofouling triboelectric coating material and its preparation method and application, and relates to the technical field of triboelectric coatings. The coating prepared by using the anti-biofouling triboelectric power generation coating material of the present invention not only has good triboelectric performance, but also can effectively collect friction energy in the environment, and the current generated during the test friction process is 0.1-30μA, The voltage is 1-200V; it also has good anti-biofouling property and has a protective effect on the base material, and the area covered by the bio-fouling is 3-10%. The coating material of the present invention has both triboelectric power generation and antifouling properties, can convert mechanical energy into electrical energy, thereby inhibiting the adhesion of organisms on the surface of the coating, and can improve the antifouling effect, and the obtained coating can be cured at room temperature, and has a good environment Adaptability and constructability, it can be coated on the surface of various materials, which greatly expands the application range of triboelectric coatings.

Description

technical field [0001] The invention relates to the technical field of triboelectric power generation coatings, in particular to an anti-biofouling triboelectric power generation coating material and its preparation method and application. Background technique [0002] Harvesting energy from the living environment is widely regarded as an effective way to achieve green energy and sustainable energy development, and is expected to play an important role in anti-fouling and anti-corrosion protection of materials, wireless transmission systems, and implanted medical devices. There are many forms of frictional energy in the natural environment, such as the friction between sea water and the hull, the friction between automobile tires and the ground, the friction between gear mechanisms, etc. If these abundant friction energy can be collected and utilized, not only can the energy pressure be greatly relieved, but also huge economic benefits can be generated. Based on the princip...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/16C09D133/00C09D127/18
CPCC08K2003/2241C08K2003/2244C08K2003/2296C08K2201/011C08L2205/03C09D5/1618C09D5/1637C09D133/00C08L27/18C08K13/06C08K9/06C08K3/36C08K3/04C08L91/06C08K3/22
Inventor 王道爱刘玉鹏周峰
Owner LANZHOU INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap